The Blithfield meteorite and the origin of sulfide-rich,metal-poor clasts and inclusions in brecciated enstatite chondrites

Blithfield (EL6) is one of five known enstatite chondrite breccias. It consists of troilite-rich clasts (35 ± 5vol.%) embedded in an extremely metallic Fe,Ni-rich matrix (65 ± 5 vol.%) that contains metal nodules up to 17 mm in size. Clasts and matrix agglomerated independently in the solar nebula under conditions of high and lowpS₂/pO₂ ratios, respectively. The matrix accreted to an EL chondrite planetesimal and was metamorphosed to～ 1000°C, above the FeNiS eutectic; chondrule textures were obliterated. The S-rich eutectic melt was lost from the matrix. The matrix material was buried to a depth of at least 3 km; accreting troilite-rich material was incorporated into the matrix as clasts. The breccia cooled through～ 500°C at 1000–10,000°C/Myr. After cooling below～ 500°C, Blithfield was quenched, possibly by impact excavation from depth and deposition onto the surface.Clasts or inclusions that are enriched in sulfide and depleted in metallic Fe,Ni are common in brecciated enstatite chondrites. Variations in thepS₂/pO₂ ratio in the nebular regions where these materials formed may explain many of their petrologic properties. The silica-rich clasts in Adhi Kot (EH4) formed at very highpS₂/pO₂ratios(> 10²⁷); niningerite, free silica and troilite were produced from the sulfurization of enstatite and metallic Fe. The troilite-rich clasts in Blithfield and Atlanta (EL6) as well as the troilite-rich regions of the Hvittis (EL6) matrix formed at somewhat lowerpS₂/pO₂ ratios where sulfurization of metalic Fe produced troilite. The Ni content of the residual metal increased, forming some metal of martensitic composition. The dark inclusions in Abee (EH 4), which contain up to 9 wt.% oldhamite, formed at highpS₂/pO₂ ratios in the presence of an additional Ca-rich component.