The join grossularite-calcite through the system CaO—Al2O3—SiO2—CO2 at 30 kilobars: Crystallization range of silicates and carbonates on the liquidus

At 30 kbar, calcite melts congruently at 1615°C, and grossularite melts incongruently to liquid + gehlenite (tentative identification) at 1535°C. The assemblage calcite + grossularite melts at 1450°C to produce liquid + vapor, with piercing point at about 49 wt.% CaCO₃. Vapor phase is present in all hypersolidus phase fields except for those with less than about 7% CaCO₃ or 8% Ca₃Al₂Si₃O₁₂. These results, together with known liquidus data for CaO—SiO₂—CO₂ and inferred results for CaO—Al₂O₃—CO₂ and Al₂O₃—SiO₂—CO₂, permit construction of the position of the CO₂- saturated liquidus surface in the quaternary system, and estimation of the positions of liquidus field boundaries separating some of the primary crystallization fields on this surface. The field of calcite is separated from those for grossularite and quartz by a field boundary with about 50% dissolved CaCO₃. Crystallization paths of silicate liquids in the range Ca₂SiO₄—Ca₃Al₂Si₃O₁₂—SiO₂, with some dissolved CO₂, will terminate at a quaternary eutectic on this field boundary, with the precipitation of calcite together with grossularite and quartz, at a temperature below 1450°C. Addition of Al₂O₃ to CaO—SiO₂—CO₂ in amounts sufficient to stabilize garnet thus causes little change in the general liquidus pattern as far as carbonates and silicates are concerned. With addition of MgO, we anticipate that silicate liquids with dissolved CO₂ will also follow liquidus paths to fields for the precipitation of carbonates; we conclude that similar paths link kimberlite and some carnbonatite magmas.