Structural control of polyhedral compression in synthetic braunite, Mn2+Mn3+ 6O8SiO4

The compression of synthetic braunite, Mn²⁺Mn³⁺ ₆O₈SiO₄, was studied by high-pressure single-crystal X-ray diffraction carried out in a diamond-anvil cell. The equation of state at room temperature (third-order Birch-Murnaghan equation of state: V ₀=1661.15(8) ų, K _0,298=180.7±0.9 GPa, K′=6.5±0.3) was determined from unit-cell volume data to 9.18 GPa. Crystal structures were determined at 6 different pressures to 7.69 GPa. Compression of the structure (space group I4₁/acd) was found to be slightly anisotropic (a ₀=9.4262(4) Å, K _a =499±4 GPa, K _a ′=19.7±0.9; c ₀=18.6964(6) Å, K _c =657±6 GPa, K _c ′=15.7±1.4) which can be attributed to the fact that the Mn³⁺-O bonds, which are the most compressible bonds, are aligned closer to the (001) plane than to the c axis. The large bulk modulus is the result of the structural topology in which 2/3 and 1/2 of the edges of the Mn²⁺O₈ and Mn³⁺O₆ polyhedra share edges with other polyhedra. The Mn²⁺O₈ polyhedra were found to compress isotropically, whereas anisotropic compressional behaviour was observed for all three Mn³⁺O₆ octahedra. Although the polyhedral geometry of all three crystallographically independent Mn³⁺ sites shows the same type of uniaxially elongated distortion, the compression of the individual octahedral configurations was found to be strongly dependent upon both the geometry of the polyhedron itself and the types of, and the connectivity to, the neighbouring polyhedra. The differences in the configuration of the different oxygen atoms, and therefore the structural topology, is one of the major factors determining the type and degree of the pressure-induced distortion, while the Jahn-Teller effect plays a subordinate role.