Effect of pressure on the diffusivity of network-forming cations in melts of jadeitic compositions

The diffusivities of network-forming cations (Si⁴⁺, Al³⁺, Ge⁴⁺ and Ga³⁺) in melts of the jadeitic composition NaAl(Si, Ge)₂O₆ and Na(Al, Ga)Si₂O₆ have been measured at pressures between 6 and 20 kbar at 1400°C. The rates of interdiffusion of Si⁴⁺-Ge⁴⁺ and Al³⁺-Ge³⁺ increase with increasing pressure at constant temperature. The results are consistent with the ion-dynamics computer simulations of Jadeite melt by Angellet al. (1982, 1983). The coefficient measured for the Si⁴⁺-Ge⁴⁺ interdiffusion is between 8 × 10^?10 and 2.5 × 10^?8$\text{cm}{}^2\text{sec}$ at 6 kbar, depending on the composition of the melt, whereas at 20 kbar it is between 7 × 10^?9 and 2 × 10^?7$\text{cm}{}^2\text{sec}$. The effect of pressure is greater for more Si-rich compositions (i.e., closer to NaAlSi₂O₆ composition). The coefficient measured for the Al³⁺-Ga³⁺ inter- diffusion is between 9 × 10^?10 and 3 × 10^?9 cm²/sec at 6 kbar and between 3 × 10^?9 and 1 × 10^?8$\text{cm}{}^2\text{sec}$ at 20 kbar. The rate of increase in diffusivity with pressure of Al³⁺-Ga³⁺ (a factor of 3–4) is smaller than that of Si⁴⁺-Ge⁴⁺ (a factor of 7–17).The Si⁴⁺-Ge⁴⁺ interdiffusion in melts of Na₂O · 4(Si, Ge)O₂ composition has also been measured at 8 and 15 kbar for comparison. The effect of pressure on the diffusivity in this melt is significantly smaller than that for the jadeitic melts. The increase in diffusivity of the network-forming cations in jadeitic melts with increasing pressure may be related to the decrease in viscosity of the same melt. The present results, as well as the ion-dynamics simulations, suggest that the homogenization of partial melts and mixing of magmas would be more efficient at greater depths.