Aluminous goethite: A mössbauer study

Mössbauer measurements at 300 K, 77 K and 4.2 K and X-ray data are presented for synthetic aluminous goethites (α Fe_1?x Al _x OOH) in two series containing up to 15 mole percent aluminium (hydrothermal preparation) and 19 mole percent aluminium (low-temperature preparation). The Mössbauer spectra for specimens at 300 K and 77 K display broadened and relaxed line-shapes with the relaxation rate increasing with aluminium substitution, whereas all the 4.2 K spectra can be described by a single magnetically split spectrum. At 4.2 K the magnitude of this splitting is 505 kOe for pure goethite and it decreases by 0.52 kOe per mole percent aluminium substitution. The absolute value of the recoil-free fraction f at 4.2 K has been measured for pure goethite and for aluminous goethites containing 7, 15 and 19 mole percent aluminium; it increases from f=0.69±0.02 to f=0.89±0.02 in this range. The increase is attributed to a stiffening of the goethite lattice as it contracts to accommodate the smaller aluminium ion. At 300 K f is found to decrease from f=0.65±0.05 for pure goethite to f=0.50±0.03 for goethite with 19 mole percent aluminium.