Repeated Load Triaxial Testing of Recycled Concrete Aggregate for Pavement Base Construction

This paper presents the results and analysis of Repeated Load Triaxial Testing (RLTT) conducted on three basecourse products; two crushed concrete, or Recycled Concrete Aggregate (RCA) materials, and a local Virgin Aggregate (VA). The objective of this testing program was to study the impact of applied stress states on resilient modulus and permanent deformation of the materials using the AUSTROADS RLTT approach (Vuong and Brimble 2000). A series of RLTT was performed under drained conditions on cylindrical specimens statically compacted at different levels of initial moisture content. The RLTT specimens were tested at 60, 80 and 90 % of Optimum Moisture Content (OMC) and to a single target dry density ratio of 98 % of Maximum Dry Density from Modified Proctor compaction testing. Duplicate specimens were tested for each moisture level. On sample measurements were made of sample deformation. It was found that the resilient moduli of the two RCA products ranged between 340 and 715 MPa, while corresponding moduli from tests on VA varied from 270 to 450 MPa. Resilient modulus was found to be dependent on both moisture content and applied stress. The two specimens of VA prepared at 90 % OMC failed during the permanent strain testing stages of the AUSTROADS test protocol. Moreover the recycled materials could be used as basecourses according to interpretation of the AUSTROADS RLTT data by Vuong and Arnold (2006).