Summary Five polished samples of zoned magnetites from skarn deposits showed optical anisotropy effects under the ore microscope, though X-ray powder diffraction investigations indicated cubic magnetite. Using high magnification ore microscopy (oil immersion lenses, monochromatic light), extremely fine zones with slightly different reflectivity were observed. Scanning electron microscopy (SEM) of etched samples confirmed zones with a thickness between a few m and 100 nm. EDX analyses showed differences in the composition of these zones, ranging from almost pure magnetite to contents of CaO, MgO, A1₂O₃, SiO₂ up to 4 wt.% in total. Thus, the extremely thin, parallel zones of magnetite, with slightly different compositions and different optical constants (reflectivity, absorption, refraction), obviously lead to optical anisotropy due to form birefringence.

---

Optische anisotropie zonarer Magnetite aufgrund von formdoppelbrechung

Zusammenfassung Fünf Anschliffe von zonar gebauten Magnetiten aus Skarn-Lagerstätten zeigten unter dem Erzmikroskop optische Anisotropie-Erscheinungen, obwohl Röntgen-Pulverauf-nahmen kubischen Magnetit ergaben. Mittels hochauflösender Erzmikroskopie (Öl-Immersion, monochromatisches Licht) wurden extrem feine Zonierungen mit etwas unterschiedlichem Reflexionsvermögen beobachtet. Rasterelektronenmikroskopie (SEM) von angeätzten Proben bestätigte eine Zonendicke zwischen einigen Yin und 100 nm. EDX Analysen zeigten Unterschiede in der Zusammensetzung dieser Zonen, die von fast reinem Magnetit bis zu CaO-, MgO-, A1₂O_3-, SiO₂-Gehalten von insgesamt 4 Gew.% reichen. Offensichtlich fiihren die extrem diinnen, parallelen Zonierungen mit unterschiedlicher Zusammensetzung, und folglich unterschiedlichen optischen Konstanten (Reflexion, Absorption, Lichtbrechung) zu optischer Anisotropie durch Formdoppelbrechung.