Mechanism of chalcopyrite formation from iron monosulphides in aqueous solutions (< 100°C, pH 2–4.5)

In low-temperature aqueous solutions (< 100°C, pH 2–4.5), chalcopyrite (CuFeS₂) does not form through direct precipitation from solution. The pathway is exclusively via precursor iron sulphides and dissolved Cu salts. The reaction of dissolved Cu (II) salts with natural hexagonal pyrrhotite (Fe_0.9S) is diffusion controlled. The initial stage has an apparent activation energy of 11.4 ± 1.8 kJ mol⁻¹ and the rate (in units of mol dm⁻³s⁻¹ cm⁻²) is independent of the solid reactant surface area. The reaction proceeds through a series of metastable Cu-Fe-sulphide intermediaries. These phases form a series of ephemeral layers penetrating into the pyrrhotite surface. The first phase formed has the stoichiometry Cu_0.1Fe_0.9S. No Fe is released into the solution during its formation and this, together with the extremely low apparent activation energy and the stoichiometry, suggest that it is formed by stuffing of electron holes in the pyrrhotite structure with Cu ions. The transformation from the hexagonal close-packed arrangement of the pyrrhotite structure to the essentially cubic packing in chalcopyrite proceeds through a series of intermediaries, approximating in composition to members of the cubanite group. The rate of formation of these phases is controlled by the coupled diffusion of Fe (II), Fe (III), Cu (I) and Cu (II) species through the surface reaction zone, although the process as a whole can be approximated by steady-state diffusion of total Cu into a semi-infinite medium. Experiments with metastable precursor iron monosulphide phases, including amorphous FeS and synthetic mackinawite indicate similar reaction pathways.

The results suggest that chalcopyrite formation in low-temperature natural systems may be significantly constrained by kinetic factors. Chalcopyrite is, at least, a diagenetic mineral since its formation requires the prior formation of iron sulphides. However, at ambient temperatures its formation is probably limited to very early diagenesis.