Electrical conductivity measurements on olivines and pyroxenes under defined thermodynamic activities as a function of temperature and pressure

Electrical conductivities of Ni₂SiO₄, Fe₂SiO₄, and MgSiO₃ were measured on synthetic powders in the temperature range 340° to 1,100° C and at pressures up to 20 kbars. For ternary compounds such as olivines and pyroxenes the control of two further variables, like the chemical activities of two components are needed, besides temperature and pressure. The activities of the corresponding binary oxides were controlled by equilibrating the samples with their neighbour-phases. Control of the oxygen partial pressure was achieved by buffer techniques. From the slopes of the lg σ vs. 1/T lines the activation energies were calculated for 10 kbar: 0.56 eV and 2.7 eV for Ni₂SiO₄ in equilibrium with SiO₂ and Ni/NiO-buffer for the temperature range 500°–800°C and 800°–1,000°C resp. 0.52 eV for Fe₂SiO₄ in equilibrium with SiO₂ and metallic iron, and 0.38 eV in equilibrium with SiO₂ and magnetite; 1.11 eV for MgSiO₃ in equilibrium with SiO₂, and 1.25 eV in equilibrium with Mg₂SiO₄.