Electron microscopy studies of akermanites (Ca1?xSrx)2CoSi2O7 with modulated structure

Single crystals of akermanite (Ca_1–x Sr _x )₂Co-Si₂O₇ solid solution were grown in nitrogen by the floating zone method using a lamp-image furnace. The grown crystals were 6 mm in diameter by 50 mm in length. Microprobe analyses indicate uniform strontium content x except in the initially crystallized part. Synthetic crystals with x from 0.0 to 0.3 give, at room temperature, satellite reflections and circular diffuse scatterings in the electron diffraction pattern, which are related to an incommensurate phase and microdomains, respectively. With increasing Sr content the wavelength of a modulation increases and the intensity of satellites decreases, but the intensity of circular diffuse scattering increases up to x=0.15 and then decreases until eventually the satellites and the circular diffuse scatterings disappear at x = 0.3. The circular diffuse scattering is explained by the cluster model for the transition state, proposed by De Ridder et al. (1976).