Das System NaAlSi3O8-BaAl2Si2O8-H2O bei 1 Kbar

The system albite-celsian-water was investigated at isothermal sections of 670, 760, 800, 900, 1000 and 1100° C at 1 Kbar. At temperatures above about 950° C the existence of a solid solution series could be shown. In the condensed part of the 930° C/1 Kbar section the partition of barium between melt and coexisting crystals was measured using an electron probe microanalyzer. The barium content of crystals grown in equilibrium with a melt is always higher than the barium content of the starting composition, so albite-celsian shows an ascending type solid solution series at low total water pressures. In the subsolidus region two types of solvi are existent, which show different ways of phase unmixing. The relatively low barium contents of natural albites are interpreted as being due to geochemical reasons rather than crystalchemical reasons.

---

---

Meinem hochverehrten Lehrer, Herrn Prof. Dr. K. Jasmund, danke ich für sein lebhaftes Interesse während der Durchführung dieser Arbeit und für die kritische Durchsicht des Manuskripts. Mein Dank gilt ferner Herrn Dr. H. A. Seck für die Einarbeitung in die experimentellen Methoden der Hydrothermalsynthese und für kritische Anmerkungen zum Manuskript. Fräulein Dr. M. Corlett danke ich für wertvolle Informationen zur Messung mit der Elektronenstrahl-Mikrosonde.

---

Die Untersuchung wurde mit Hilfe von Personal- und Sachmitteln durchgeführt, die Herrn Professor Dr. K. Jasmund von der Deutschen Forschungsgemeinschaft zur Verfügung gestellt worden waren.