Phase equilibria for the Fe2SiO4–Fe3O4 system under high pressure

High pressure phase relation of the system Fe₂SiO₄–Fe₃O₄ was investigated by synthesis experiments using multi-anvil high pressure apparatus. A complete solid solution with spinel structure along Fe₂SiO₄–Fe₃O₄ join occurs above 9 GPa at 1200 °C. Lattice constants of the solid solution show almost linear variation with composition. A spinelloid phase is stable for intermediate compositions in the pressure range from 3 to 9 GPa. the synthesized spinelloid phase is successfully indexed assuming nickel aluminosilicate V type structure. Received: October 16, 1995 / Revised, accepted: March 19, 1997