富钴结壳超细标准物质的加工制备
引用本文:郑存江,刘清辉,胡勇平,董利明,王毅民,顾铁新. 富钴结壳超细标准物质的加工制备[J]. 岩矿测试, 2010, 29(3): 301-304
作者姓名:郑存江  刘清辉  胡勇平  董利明  王毅民  顾铁新
作者单位:1. 浙江省地质矿产研究所,浙江,杭州,310007
2. 国家地质实验测试中心,北京,100037
3. 中国地质科学院地球物理地球化学勘查研究所,河北,廊坊,065000
基金项目:"国际海底资源研究开发"国家专项"十五"计划项目资助 
摘    要:用气流磨制备了2个具有超细粒度的海山富钴结壳标准物质MCPt-1和MCPt-2。原样先经球磨成74μm(-200目),再用气流磨进行超细加工。样品粒度采用激光粒度仪检测,用粒度分布图和特征粒度来表达测量结果。两个样品的平均粒度分别为1.8μm和1.5μm(约2 000目),是目前粒度最小的标准物质。文章介绍了用于超细加工的流化床式气流磨原理与方法,展示了样品加工后的粒度分析结果,对比了国内外超细标准物质的概况。最后讨论了当前关注样品加工的重要性、超细加工的问题及超细样品分析研究的意义。

关 键 词:标准物质  超细加工  气流磨  粒度分析与表征
收稿时间:2009-04-15
修稿时间:2009-07-28

Processing and Preparation of Ultra-fine Co-rich Crust Reference Materials
ZHENG Cun-jiang,LIU Qing-hui,HU Yong-ping,DONG Li-ming,WANG Yi-min and GU Tie-xin. Processing and Preparation of Ultra-fine Co-rich Crust Reference Materials[J]. Rock and Mineral Analysis, 2010, 29(3): 301-304
Authors:ZHENG Cun-jiang  LIU Qing-hui  HU Yong-ping  DONG Li-ming  WANG Yi-min  GU Tie-xin
Affiliation:Zhejiang Institute of Geology & Mineral Resources, Hangzhou 310007, China;Zhejiang Institute of Geology & Mineral Resources, Hangzhou 310007, China;Zhejiang Institute of Geology & Mineral Resources, Hangzhou 310007, China;Zhejiang Institute of Geology & Mineral Resources, Hangzhou 310007, China;National Research Center for Geoanalysis, Beijing 100037, China;Institute of Geophysical and Geochemical Exploration, Langfang 065000, China
Abstract:Two Co-rich seamount crust reference materials of MCPt-1 and MCPt-2 for platinum group elements(PGEs) with an ultra-fine particle size have been prepared by a jet mill.The raw samples of the reference materials were ground by a ball mill to 74 μm(-200 mesh) powder and then were further processed by a jet mill to ultra-fine size.After well-mixed,the particle size distribution of the samples were tested by a laser particle analyzer.The results of particle size analysis were expressed by the particle size distribution plot and specific particle size.The average particle size MCPt-1 and MCPt-2 were 1.8 μm and 1.5 μm(about 2000 mesh) respectively.The paper also introduced principle and application development of fluidized bed jet mill used in ultra-fine process in standard reference material preparation worldwide.Finally,the importance and problems in ultra-fine sample processing,the significance of ultra-fine sample analysis in scientific research were discussed.
Keywords:reference material  ultra-fine processing  jet mill  analysis and characterization of particle size