High- and low-velocity impact experiments on porous sintered glass bead targets of different compressive strengths: Outcome sensitivity and scaling

Impact experiments on porous targets consisting of sintered glass beads have been performed at different impact velocities in order to investigate the disruption impact energy threshold (also called Q^∗) of these targets, the influence of the target compressive strength on this threshold and a scaling parameter of the degree of fragmentation that takes into account material strength. A large fraction of small bodies of our Solar System are expected to be composed of highly-porous material. Depending on their location and on the period considered during the Solar System history, these bodies collide with each other at velocities which cover a wide range of values from a few m/s to several km/s. Determining the impact response of porous bodies in both high- and low-velocity regimes is thus crucial to understand their collisional evolution over the entire Solar System history, from the early stages of planetary formation through collisional accretion at low impact velocities to the current and future stages during which impact velocities are much higher and lead to their disruption. While these problems at large scale can only be addressed directly by numerical simulations, small scale impact experiments are a necessary step which allows the understanding of the physical process itself and the determination of the small scale behavior of the material used as target. Moreover, they are crucial to validate numerical codes that can then be applied to larger scales.Sintered glass beads targets of different shapes and porosity have been built and their main material properties, in particular their compressive strength and their porosity, have been measured. The outcomes of their disruptions both at low and high impact velocities have then been analyzed.We then found that the value of Q^∗ strongly depends on the target compressive strength. Measuring the particle velocities as a function of their distance to the impact point, we first found that the attenuation rate of the stress wave in our sintered glass bead targets does not depend on the impact velocity regime. Ejecta velocities as a function of the distance from the impact point can thus be well fitted by a power law with an exponent about −2 in both velocity regimes. We then looked for a scaling parameter that can apply to both regimes. We found that the scaling parameter PI, which is related to the initial peak pressure and to the stress wave attenuation can be used to represent the outcome in a general way. Future investigations will be performed to determine whether these results can be generalized to other kinds of porous materials.