Thermal alteration of nontronite and montmorillonite: Implications for the martian surface

To test the effects of meteorite impacts on martian phyllosilicate deposits, we heated two smectites (nontronite and montmorillonite) to temperatures ranging from 350 °C to 1150 °C for durations of 4-24 h in two different atmospheres, under air and a steady flow of CO₂. Samples were analyzed using X-ray diffraction (XRD) and near-infrared (NIR) and mid-infrared (MIR) reflectance spectroscopy. Interlayer water was lost after heating to temperatures of ∼400 °C. Between 400 °C and 700 °C, nontronite converted to an intermediary phase which conserved the XRD pattern of untreated nontronite with the exception of the 0 0 1 peak. Nanocrystalline high-temperature phases formed for both smectites at temperatures between 700 °C and 1000 °C. Finally, after being heated to temperatures above ∼1100 °C, the samples melted and recrystallized into secondary phases. Secondary high-temperature phases included sillimanite and cristobalite for both smectites plus hematite for nontronite. NIR and MIR reflectance spectra significantly evolved with increasing temperature. NIR spectra of smectites showed that 1.4 and 1.9 μm bands decrease in intensity and disappear above 700 °C. Similarly, the 2.2-2.3 μm metal-OH band showed a decrease in intensity as well as an overall shift towards lower wavelengths (for nontronite) due to the thermal resistance of the Al-OH bond compared to the Fe-OH bond. NIR spectra of montmorillonite showed a gradual increase in band depth up to temperatures between 500 °C and 600 °C, then decreased with increasing temperature. In the MIR spectra of samples heated to temperatures above ∼1100 °C, newly formed bands confirmed the secondary phases identified by XRD. Similarities between the NIR spectra of our heated samples and the phyllosilicates in some martian craters imply that these phyllosilicates were altered by the impact-generated heat and thus were not formed post-impact. In addition, NIR reflectance spectra provide a proxy for shock temperatures of smectites up to 700 °C while MIR is optimum for identification of high-temperature phases of smectites above 700 °C.