Characterisation of tobelite (NH4)Al2[AlSi3O10](OH)2 and ND4-tobelite (ND4)Al2[AlSi3O10](OD)2 using IR spectroscopy and Rietveld refinement of XRD spectra

Tobelite (NH₄) Al₂ [AlSi₃O₁₀] (OH)₂, the ammonium analogue of muscovite, and its deuterated form ND₄-tobelite (ND₄) Al₂ [AlSi₃O₁₀] (OD)₂ have been synthesised at 600?°C and 200 and 500 Mpa using a well homogenised, stoichiometric SiO₂-Al₂O₃ oxide mix with Al₂O₃ in excess of 5 mol% and a 25% NH₃ solution whose relative abundance was such that the amount of NH₄ ⁺ stoichiometrically available was in excess of 50%. Characterisation of both tobelite and ND₄-tobelite using IR-spectroscopy, Rietveld refinement of X-ray powder diffraction data, and electron microprobe analysis indicate that, similar to K⁺ in muscovite, the NH₄ ⁺ or ND₄ ⁺ molecule occupies the interlayer site. IR absorption bands caused by NH₄ ⁺ and ND₄ ⁺ can be explained, to a very good approximation, on the basis of T_d symmetry. Nevertheless, substantial line broadening and the occurrence of shoulders indicate a deviation from ideal T_d symmetry. However, even at 77?K, no discrete splitting of the degenerate states could be confirmed. The OH stretching frequencies observed for synthetic tobelite are quite similar to those for muscovite, indicating that the replacement of K⁺ by NH₄ ⁺ has no effect. The low FWHH of the OH bands indicate that the hydroxyl groups are well ordered within the structure. Rietveld refinement of tobelite and ND₄-tobelite indicates that all samples synthesised consist of the 3 different mica polytypes which are typical of muscovite – namely 1M (C2/m), 2M ₁ (C2/c) and 2M ₂ (C2/c). Tobelite and ND₄-tobelite synthesised at 500 Mpa principally contain the 1M polytype, whereas the principle polytype for ND₄-tobelite synthesised at 200 Mpa, is 2M ₂. Rietveld refinement of X-ray diffraction spectra for tobelite synthesised at 200 Mpa was problematic due to the very broad FWHH of the X-ray peaks indicating poor crystallinity. In comparision to synthetic muscovite, the cell dimensions observed for tobelite and its deuterated analogue are quite similar except for the lattice constant c. Due to the larger radius of NH₄ ⁺ or ND₄ ⁺ compared to K⁺ cation, the c-direction is expanded form 10.275 Å in muscovite to approximately 10.540 Å in tobelite and ND₄-tobelite.