Raman spectroscopy and heat capacity measurement of calcium ferrite type MgAl2O4 and CaAl2O4 |
| |
| Authors: | Kojitani H Nishimura K Kubo A Sakashita M Aoki K Akaogi M |
| |
| Institution: | (1) Department of Chemistry, Gakushuin University, Mejiro, Toshima-ku, Tokyo 171-8588, Japan;(2) Materials and Structures Laboratory, Tokyo Institute of Technology, Nagatsuta-cho, Yokohama 226-8503, Japan |
| |
| Abstract: | Raman spectroscopy of calcium ferrite type MgAl2O4 and CaAl2O4 and heat capacity measurement of CaAl2O4 calcium ferrite were performed. The heat-capacity of CaAl2O4 calcium ferrite measured by a differential scanning calorimeter (DSC) was represented as CP(T)=190.6–1.116 × 107T–2 + 1.491 × 109T–3 above 250 K (T in K). The obtained Raman spectra were applied to lattice dynamics calculation of heat capacity using the Kieffer model. The calculated heat capacity for CaAl2O4 calcium ferrite showed good agreement with that by the DSC measurement. A Kieffer model calculation for MgAl2O4 calcium ferrite similar to that for CaAl2O4 calcium ferrite was made to estimate the heat capacity of the former. The heat capacity of MgAl2O4 calcium ferrite was represented as CP(T)=223.4–1352T –0.5 – 4.181 × 106T –2 + 4.300 × 108T –3 above 250 K. The calculation also gave approximated vibrational entropies at 298 K of calcium ferrite type MgAl2O4 and CaAl2O4 as 97.6 and 114.9 J mol–1 K–1, respectively. |
| |
| Keywords: | Calcium ferrite Heat capacity Differencial scanning calorimetry Raman Kieffer model |
| 本文献已被 SpringerLink 等数据库收录！ |
|