Heat capacity and phase equilibria of wadeite-type K2Si4O9

The low-temperature heat capacity (C _p) of Si-wadeite (K₂Si₄O₉) synthesized with a piston cylinder device was measured over the range of 5–303 K using the heat capacity option of a physical properties measurement system. The entropy of Si-wadeite at standard temperature and pressure calculated from the measured heat capacity data is 253.8 ± 0.6 J mol⁻¹ K⁻¹, which is considerably larger than some of the previous estimated values. The calculated phase transition boundaries in the system K₂O–Al₂O₃–SiO₂ are generally consistent with previous experimental results. Together with our calculated phase boundaries, seven multi-anvil experiments at 1,400 K and 6.0–7.7 GPa suggest that no equilibrium stability field of kalsilite + coesite intervenes between the stability field of sanidine and that of coesite + kyanite + Si-wadeite, in contrast to previous predictions. First-order approximations were undertaken to calculate the phase diagram in the system K₂Si₄O₉ at lower pressure and temperature. Large discrepancies were shown between the calculated diagram compared with previously published versions, suggesting that further experimental or/and calorimetric work is needed to better constrain the low-pressure phase relations of the K₂Si₄O₉ polymorphs. Electronic supplementary material The online version of this article (doi:) contains supplementary material, which is available to authorized users.