Compressibility of P2O5-Al2O3-Na2SiO3 melts

The effect of composition and temperature on the relaxed adiabatic bulk modulus of melts in the P₂O₅-Al₂O ₃-Na₂SiO₃ system have been investigated in the temperature range of 1140 to 1450 °C using ultrasonic interferometric methods at frequencies of 3, 5 and 7 MHz. The density of these melts was determined using Pt-double-bob Archimedean densitometry techiques. P₂O₅ is known to dramatically affect the structure and the chemical and physical properties of granitic and pegmatitic melts as a function of the peralkalinity of the melt. The physical results of the structural changes occurring in Na₂O-Al₂O₃-SiO₂ melt upon the addition of P₂O₅ are observed by variations in the properties such as density and compressibility. For the present peralkaline melts, the bulk modulus and density decrease with addition of 15 mol% P₂O₅, and increase with the addition of 15 mol% Al₂O₃. The addition of P₂O₅ to the present melts results in a larger increase in melt compressibility than that observed with increasing polymerization between Na₂SiO₃ and Na₂Si₂O₅ melts. This would suggest that not only is the polymerization of the melt increasing with the addition of P₂O₅ (Mysen et al. 1981; Nelson and Tallant 1984; Gan and Hess 1992), but that the tetrahedrally co-ordinated phosphorus complexes are influencing the bond lengths and energies within the melt structure; resulting in the structure becoming more compressible than expected, although incompressible (Vaughan and Weidner 1987) tetrahedral P₂O₅ polyhedra (Mysen et al. 1981; Gan and Hess 1992; Toplis et al. 1994) are being added to the melt structure.