Effect of silica fume on compressive strength of oil-polluted concrete in different marine environments
Authors:Hamid Shahrabadi  Sina Sayareh  Hamed Sarkardeh
Institution:1.Department of Civil Engineering,Chabahar Maritime University,Chabahar,Iran;2.Department of Civil Engineering,University of Sistan & Baluchestan,Zahedan,Iran;3.Department of Civil Engineering, Faculty of Engineering,Hakim Sabzevari University,Sabzevar,Iran
Abstract:In the present research, effect of silica fume as an additive and oil polluted sands as aggregates on compressive strength of concrete were investigated experimentally. The amount of oil in the designed mixtures was assumed to be constant and equal to 2% of the sand weight. Silica fume accounting for 10%, 15% and 20% of the weight is added to the designed mixture. After preparation and curing, concrete specimens were placed into the three different conditions: fresh, brackish and saltwater environments (submerged in fresh water, alternation of exposed in air & submerged in sea water and submerged in sea water). The result of compressive strength tests shows that the compressive strength of the specimens consisting of silica fume increases significantly in comparison with the control specimens in all three environments. The compressive strength of the concrete with 15% silica fume content was about 30% to 50% higher than that of control specimens in all tested environments under the condition of using polluted aggregates in the designed mixture.
Keywords:
本文献已被 CNKI SpringerLink 等数据库收录!
点击此处可从《中国海洋工程》浏览原始摘要信息
点击此处可从《中国海洋工程》下载免费的PDF全文
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号