CORROSION RESISTANCE OF INTERFERENCE FILM ON STAINLESS STEEL

IwrRODUcrlONStainlessstalhasbeenusedwidelyasbuildingrnateria1,especiallyasdecoratingrnate-rialinbuildings.Ordinarystainlesssteehasonlyonemonot0noussilverywhitCcolourwhichsomeimesdoesnotrnatchwithitSsurmundingenvironment.lnordert0improveitSdereratingperfonnaneeandexpanditsuse,muchresearchhasbeenconductedsincethe4O'st0trytoformabright,uniform,highcorrosi0nandwearresistantco1ourfilmonastainlesssteesurface.Duringtheeariystage,anirnmersionedhodwasused,i.e.inimrs-ingthestainlesssteelinahots0luti…     

STRESS CORROSION CRACKING OF AISI 321 STAINLESS STEEL IN ACIDIC SEAWATER

ImooUonONSCCisoneofthemosttwortantcausoffailureofstaiuleSsstalequipmentandfacilitieS.Studiesonunh0refacilitiesshowedthatanaddicchloridesolutionfilmcouldbefo~onthescheeofstalandthatstaiuleSSstalisinaCtivedissolutionstateinaedicchloridesolutionopinetal.,l99O;Gnanamoorthyetal.,l99O).ltisgenerallythoughtxthatSCCcannotoimrwhenthematerialisinaCtiveanodicdissolutionstate,soitsomcewithresultingcasualties(0ldfieldetal.,l99O)arousedattentiont0it.SomeSCCmeCanisrnsproposedpeuang,l988,Newmanctal.,…     

ELECTROCHEMICAL CORROSION BEHAVIOR OF STEEL IN THE JUNCTURE AREA OF SEA CLAY AND SAND

Corrosion behavior of steel in the juncture area of sea clay and sand was studied. The results show that galvanic corrosion occurred between steel samples buried in sea clay and sand, and that the polarity of the galvanic cell reversed after some testing later. The cause of reversing of polarity is discussed.     

CORROSION AND ADHERENCE AT SEA OIL-PLATFORM

Measurements of the adhesive corrosion and protective potentials of 3 Bohai Sea oilplatforms under different cathodic protection showed corrosion still occurred on these platforms undertheir designed protective potentials. Preliminary conclusions from indoor experiments on the relation betweenadhesive corrosion and cathodic protection showed adhering organisms caused the corrosion onthese platforms.     

EFFECT OF SULPHATE-REDUCING BACTERIA ON ELECTRO-CHEMICAL CORROSION BEHAVIOR OF 16Mn STEEL IN SEA MUD

ＩＮＴＲＯＤＵＣＴＩＯＮＩｔｗａｓｇｅｎｅｒａｌｌｙｃｏｎｓｉｄｅｒｅｄｐｒｅｖｉｏｕｓｌｙｔｈａｔｔｈｅｃｏｒｒｏｓｉｏｎｏｆｓｔｅｅｌｉｎｓｅａｍｕｄｗａｓｎｏｔｓｅｒｉｏｕｓ.Ｈｏｗｅｖｅｒ,ｉｔｗａｓｌａｔｅｒｆｏｕｎｄｔｈａｔｔｈｅｃｏｒｒｏｓｉｏｎｒａｔｅｏｆｓｔｅｅｌｉｎｓｏｍｅｓｅａｍｕｄｗａｓｈｉｇｈｅｒｔｈａｎｔｈａｔｉｎｓｅａｗａｔｅｒ(Ｋｉｎｇ,1980;Ｓｅｈｍｉｄｅ,1982;Ｇｕｏｅｔａｌ.,1997;Ｈｏｕ,1998).Ｔｈｅｒｅａｒｅｓｏｍｅｒｅｐｏｒｔｓｔｈａｔｔｈｅｃｏｒｒｏｓｉｏｎｒ…     

Full-range nonlinear analysis of fatigue behaviors of reinforced concrete structures by finite element method

Ｆｕｌｌ－ｒａｎｇｅｎｏｎｌｉｎｅａｒａｎａｌｙｓｉｓｏｆｆａｔｉｇｕｅｂｅｈａｖｉｏｒｓｏｆｒｅｉｎｆｏｒｃｅｄｃｏｎｃｒｅｔｅｓｔｒｕｃｔｕｒｅｓｂｙｆｉｎｉｔｅｅｌｅｍｅｎｔｍｅｔｈｏｄ￥ＳｏｎｇＹｕｐｕ；ＺｈａｏＳｈｕｎｂｏ；ＷａｎｇＲｕｉｍ...     

Fuzzy Fatigue Reliability Analysis of Offshore Platforms in Ice-Infested Waters

1 .IntroductionTheBohaiGulfisinfestedbyiceinthewholewinter,andoffshorestructuresthereexperiencenotonlywind ,waves ,currentsandearthquake ,butalsoiceloadswhicharecomplicatedbecauseofthedynamicinteractionbetweenicesheetsandstructures.Duanetal.( 2 0 0 0 )hadacomprehensivere viewofthelatestadvancesonice inducedvibration ,fatigueandfractureofoffshorestructures ,payingmuchattentiontothedifferencesinicebreakingmodeanddynamicsofstructuresindifferentice in festedwaters .Theypresentedcriticallythelates…     

Fatigue Behavior of Plain Concrete Under Biaxial Compression: Experiments and Theoretical Model

The effects of different lateral confinement stress on the fatigue behavior of and cumulative damage to plain concrete are investigated experimentally. Eighty 100 mm x 100 mm x 100 mm specimens of ordinary strength concrete are tested under constant- or variable-amplitude fatigue loading and lateral confinement pressure in two orthogonal directions. A fatigue equation is developed by modifying the classical Aas-Jakobsen S-N equation for taking into account the effect of the confined stress on fatigue strength of plain concrete. The results of variable-amplitude fatigue tests indicate that the linear damage theory proposed by Palmgren and Miner is unreasonable in the biaxial stress state. A nonlinear cumulative damage model that could model the effects of the magnitude and sequence of variable-amplitude fatigue loading and lateral confinement pressure is proposed on the basis of the evolution laws of the residual strains in the longitudinal direction during fatigue tests. The residual fatigue life predic     

随机载荷下的疲劳损伤计算公式

本文推导了随机载荷下的疲劳损伤计算公式。数值计算结果表明：Ｐ．Ｈ．Ｗｉｒｓｃｈｉｎｇ给出的公式在宽带情况下与实际情况不符；Ｇ．Ｃｈａｕｄｈｕｒｙ给出的公式在窄带情况下与实际不符；本文绘出的公式不仅适合于窄带，也适合于具有各种不同带宽的宽带随机载荷。     

非常规管节点疲劳寿命分析与计算

对非常规管节点的疲劳寿命进行了分析研究，用SESAM计算疲劳载荷，应用精细有限元分析计算热点应力，用规范的S—N曲线计算管节点的疲劳寿命。通过实例计算表明，这些处理对非常规管节点疲劳寿命分析与计算是很有效的。