Overbreak and underbreak in underground openings Part 2: causes and implications

Summary The newly developed light sectioning method has been used to investigate some of the causes and costs of overbreak and underbreak. Investigations at the Aquamilpa Hydroelectric Project in Mexico have shown decreased overbreak and increased underbreak as a result of increased rock quality and decreased explosive energy. A new measure of explosive energy, the perimeter powder factor (PPF), has been defined and shown to be useful in the context of tunnel-wall rock damage. Tentative results indicate that explosive energy (PPF) may be a more important factor in producing underbreak, whereas rock quality may be a greater factor in producing overbreak. A site-specific equation is given for predicting overbreak or underbreak as a function of rock quality and explosive energy, with an evaluation of the cost of underbreak and overbreak.     

In situ time resolved synchrotron powder diffraction study of thaumasite

Structural changes during dehydration and subsequent decomposition in thaumasite Ca₃Si(SO₄)(CO₃)(OH)₆·12 H₂O were studied by in situ synchrotron powder diffraction between 303 and 1,098 K. Evolution of the crystal structure was observed through 28 structure refinements, by full profile Rietveld analysis performed in the P6₃ space group, between 300 and 417 K, whereupon the thaumasite structure was observed to breakdown. Within this temperature range, the cell parameters of thaumasite increased as a function of temperature in a nearly linear fashion up to about 393 K, at which temperature, a slight slope change was observed. Above 400 K, the thermogravimetric analysis revealed that the dehydration process proceeded very rapidly while the refined occupancy of water molecules dropped below a critical level, leading to instability in the thaumasite structure. At a same time, a remarkable change in the unit cell parameters occurring at about 417 K indicated that the crystal structure of thaumasite collapsed on losing the crystallization water and it turned amorphous. This result indicated that the dehydration/decomposition of thaumasite was induced by the departure of the crystallization water. At about 950 K, anhydrite and cristobalite crystallized from the thaumasite glass.     

三类高强度悬式瓷绝缘子的成分和物相分析

为探讨高原牌70kN和进口120，210kN瓷绝缘子的成分和结构性能，中采用原子吸收光谱（AAS）和X射线衍射（XRD）方法，对三类产品进行了检测。结果表明，有效成分除K2O外，70kN和210kN的SiO2,Al2O3,Fe2O3含量接近，主晶相基本相同，有刚玉，莫来石、石英和长石等；结晶相总量：70kN35%，120kN40%,210kN48%，这表明机械强度愈大，结晶相含量愈高，只需调整70kN原样的部分成分，粒度和工艺，即生产出高等级（如210kN)瓷绝缘子。     

利用高铁钾长石粉合成13X沸石分子筛的实验研究

对江苏丰县的富钾页岩进行预处理，得到钾长石含量达76．4％的钾长石粉，其Fe2O3含量高达7．52％。以此钾长石粉为原料经过焙烧处理、水热合成实验，在铁含量较高情况下成功合成了13X沸石分子筛，并采用正交实验法确定了优化工艺参数。对实验产物的主要性能测试表明，合成的富铁沸石产品与13X沸石分子筛工业产品相似，吸附量达到国家化学工业产品标准，可用于对含重金属离子废水的吸附处理。     

锇粉中杂质元素分析方法研究

利用ＩＣＰ＿ＭＳ技术建立了锇粉中痕量杂质元素的分析方法。在浓ＨＮＯ３介质中，锇以ＯｓＯ４形式挥发除去，分离锇基体后，可直接测定的痕量元素达５０余种。取样量０．１ｇ，测定限为０．２～２４６ｎｇ／ｇ，可实现质量分数ｗ（Ｏｓ）为９９．９９９９％锇粉中杂质元素测定。结合ＩＣＰ＿ＡＥＳ测定Ｋ、Ｎａ、Ｃａ、Ｍｇ、Ａｌ、Ｆｅ、Ｓｉ和Ｐ，可实现锇粉原料及产品的纯度分析。     

原位磁化X射线粉末衍射法测还原铁粉的微观磁致伸缩系数

首次报导X射线粉末衍射法测量铁粉晶胞的磁致伸缩系数。还原铁粉样品原位磁化后 ,铁立方晶胞产生磁致伸缩效应 ,晶胞参数的变化引起衍射峰位置和晶面间距的变化。实验测得铁晶胞λ1 0 0 为 3 .3 3× 10 - 4,此结果表明铁晶胞的微观磁致伸缩系数比棒状、薄膜或粉末压片的系数大约 16倍。对此现象进行了合理的理论解释 ,指出大块材料中的粉末多晶之间具有较大的空隙 ,从而使得宏观磁致伸缩系数变小     

测试超细煤粉粒度的实验研究

利用激光粒度仪测试超细煤粉的粒度。对测试超细煤粉试样粒度时的试样浓度、测试温度、分散时间、分散剂的种类及浓度等方面的影响进行了实验研究，给出了激光粒度仪测试超细煤粉粒度的最佳实验条件。     

药用滑石粉酸中可溶物测定方法考察

考察药用滑石粉酸中可溶物测定方法的重复性、耐用性 ,分析主要影响因素。比较酸溶物提取液滤过介质对测定结果差异的影响 ;采用重量法随机测定酸溶物含量和室间差异。两种滤过介质处理对测定结果没有显著差异 ;室间测定结果没有显著差异 ;30批样品平行测定结果的 RSD值范围为 0 %～ 18.2 %。酸中可溶物测定法存在重复性和耐用性不佳的问题 ,应相应调整酸中可溶物含量限度     

无机盐超细粉体制备技术的回顾与展望

评述了制备无机盐超细粉体的传统方法以及一些传统方法的改进 ,对当前几种新技术做了介绍与展望     

低温低压条件下辉石粉末的热导率实验分析:对月球及火星表面热环境研究的指示

在真空条件下矿物粉末热导率的实验测量,可为我们研究月球及行星表面的热属性和热演化,解译热红外和微波探测数据,开展月球及行星探测载荷设计提供重要的数据参数。本研究主要采用改造后的Hot Disk TPS 2500S导热仪对辉石粉末的热导率进行测量。同时,分析了真空度、温度对辉石粉末热导率的影响。实验结果表明:1)热导率随着真空度的降低呈下降趋势,大气压力在1000Pa时,辉石粉末热传导机制发生明显改变。在低压条件下(1000Pa)热导率随真空度的变化趋于平缓;2)辉石粉末热导率随温度的升高而增大,但是增大的幅度在低压和常压条件下存在明显差异。根据实验结果,提出了低压条件下辉石粉末热导率随真空度和温度变化的关系式。本研究表明,在月球和火星表面热环境的研究中,温度和压力对热导率的影响程度是不同的。上述结果对未来开展地外样品的热导率测量提供了重要的参考。