Use of clay as a pozzolona in high strength Portland cement and its thermal activation

In this investigation local clay from Cherat mines, Nowshera District, NWFP, Pakistan, has been tested as a pozzolanic material in high strength Portland cement. Thermal treatments were performed as a means of activation of the clay. It was found that thermal treatment of the clay can increase its pozzolanic activity. Different blended mortars, containing different amounts of clay, activated at different temperatures were studied for compressive strength, consistency, and setting times. It was concluded that the mechanical properties of the blended cements were mainly governed by the percentage of incorporation of the calcined clay. Blended cement composition has been formulated, with optimal results of 20% calcined clay at a temperature of 600℃.     

灼烧法中有机质与总有机碳换算关系的重建及其在页岩分析中的应用

有机质与总有机碳(TOC)的换算关系为wo=1.724×wTOC,难以满足当前页岩气开发的现场测定要求,需要作出修正。本文以鄂尔多斯盆地南部页岩样品为研究对象,在传统灼烧法基础上,采用X射线荧光光谱仪测定页岩组成,得出影响烧失量的因素;用热重-差热仪研究页岩灼烧情况,确定了无机盐不分解而有机质分解的最佳灼烧温度和时间。通过线性拟合灼烧法测得的有机质含量与仪器法测得的有机碳含量间的换算关系,建立了一种通过测定烧失量来换算总有机碳含量的新方法。在页岩最佳灼烧温度480℃,灼烧时间1.5 h条件下线性拟合建立了两种新的换算关系,获得TOC测定值与仪器法的标准值相对误差分别为1.691%、0.486%,检出限分别为0.41%、1.60%。综合它们的优缺点,可将测定页岩类样品的换算关系重建为wo=2.125×wTOC。重建的方法通过严格控制灼烧温度,解决了传统灼烧法中烧失量因无机盐高温分解造成有机质代表性不足的问题,可用于精确测定页岩中的有机质或有机碳含量。     

金矿石鉴定过程中的一些体会

在鉴定金矿石的光片时 ,有时见不到金矿物 ,这是由多种原因引起的。我们通过改进制片工艺及抛光前对光片进行烘烤、煅烧等方法 ,使金矿石光片中金矿物可见几率提高 ,并可使许多原矿石中的不可见金归并加大 ,变为可见金。此外 ,本文还提到一种金矿石中经常存在的富铁黄铜矿 ,它可作为某些地区中金矿石的指示矿物     

氢氧化镁煅烧工艺和原料配比对氯氧镁水泥抗压强度的影响

以电石渣和MgCl_2制备的Mg(OH)_2为原料,制备氯氧镁水泥(MOC)用活性MgO,通过正交实验的方法观察煅烧温度、保温时间、活性MgO与MgCl_2摩尔比、H_2O与MgCl_2摩尔比对MOC试件抗压强度的影响。以3d、7d、28dMOC试件的抗压强度为评价指标,综合各因素对抗压强度的影响趋势发现:随煅烧温度及活性MgO与MgCl_2摩尔比的增加,MOC试件抗压强度呈增加趋势;保温时间大于30 min时,MOC试件的抗压强度随保温时间增加而降低;随H_2O与MgCl_2摩尔比的增大,试件的抗压强度逐渐减小。且不同龄期内,H_2O与MgCl_2摩尔比对试件抗压强度影响最为显著。当煅烧温度为600℃,保温时间为30 min,MgO与MgCl_2摩尔比为8,H_2O与MgCl_2摩尔比为13时,试件的抗压强度最佳。     

Abundances of Sulfur,Selenium, Tellurium,Rhenium and Platinum‐Group Elements in Eighteen Reference Materials by Isotope Dilution Sector‐Field ICP‐MS and Negative TIMS

Geological reference materials (RMs) with variable compositions and NIST SRM 612 were analysed by isotope dilution mass spectrometry for bulk rock concentrations of chalcogen elements (sulfur, selenium and tellurium), rhenium and platinum‐group elements (PGEs: Ru, Pd, Os, Ir and Pt), including the isotope amount ratios of ¹⁸⁷Os/¹⁸⁸Os. All concentrations were obtained from the same aliquot after HCl‐HNO₃ digestion in a high pressure asher at 320 °C. Concentrations were determined after chemical separation by negative TIMS, ICP‐MS and hydride generation ICP‐MS (Se, Te). As in previous studies, concentrations of the PGEs in most RMs were found to be highly variable, which may be ascribed to sample heterogeneity at the < 1 g level. In contrast, S, Se and Te displayed good precision (RSD < 5%) in most RMs, suggesting that part of the PGE budget is controlled by different phases, compared with the chalcogen budget. The method may minimise losses of volatile chalcogens during the closed‐system digestion and indicates the different extent of heterogeneity of chalcogens, Re and PGEs in the same sample aliquot. OKUM, SCo‐1, MRG‐1, DR‐N and MAG‐1 are useful RMs for the chalcogens. NIST SRM 612 displays homogenous distribution of S, Se, Te, Pt and Pd in 30 mg aliquots, in contrast with micro‐scale heterogeneity of Se, Pd and Pt.     

府谷煤矸石的赋存状态及煅烧增白特性

据地质勘探资料并结合显微镜观察、X衍射和差热分析法,研究了陕西府谷地区煤层中的煤矸石赋存状况。结果表明:府谷地区的煤矸石赋存丰富,且大多数样品中高岭石的质量分数均在90%以上,可作为优质的高岭土矿产。对该煤矸石的煅烧增白研究表明,在相同的煅烧条件下,含碳量高的煤矸石白度提高得快。      

新疆尉犁蛭石高温膨胀试验研究

通过原料物相组成、原料粒度及煅烧温度对新疆尉犁蛭石膨胀性能的影响研究。结果表明:新疆尉犁蛭石主要物相为蛭石、金云母、蛭石-云母混层矿物和方解石;蛭石与蛭石混层矿物含量越高蛭石膨胀倍越大,并主要受蛭石混层矿物含量的影响;在一定范围内蛭石膨胀倍随粒度增大而增大,当原料粒度超过2 mm时,其膨胀倍随粒度的增加而较小;蛭石膨胀倍随煅烧温度上升而迅速增加,但煅烧温度超过700℃时,其膨胀倍不再增加。     

煅烧高岭土的开发与应用

本文主要介绍了高岭土煅烧反应机理和为煅烧过程中高岭土的结构变化以及煅烧高岭土在电缆、造纸、涂料、耐火材料及化学工业等领域的实际应用。     

五氟化溴法测定硅酸盐及氧化物矿物氧同位素组成的影响因素研究

应用五氟化溴法(BrF5)测定硅酸盐及氧化物矿物的氧同位素组成,试剂纯化、样品预处理、环境湿度、反应器洁净程度以及实验质量控制是影响该法准确度的主要因素。为确定BrF5法最佳实验条件,提高分析精度,本文以国家标准物质为参考,对硅酸盐及氧化物矿物在不同焙烧温度下的氧同位素组成进行分析,并对实验环境湿度和反应器洁净程度对分析数据质量的影响进行了系统研究。实验确定了焙烧温度设置为650～750℃,可去除硅酸盐全岩样品中的炭质成分,避免了温度因素引起的同位素分馏;将实验环境相对湿度降低至50%RH,并在0. 5min内完成样品装填,可解决由于水汽造成δ18O值明显偏低的突出问题;对于新使用的反应器,或反应器在使用中有黄色物质脱落、内壁受到污染,及时进行氟化处理和清洗,可避免因氧气产率降低所引起的氧同位素分馏;反应器交替进行样品和标准物质CO2试样的制备,可对样品同位素数据的可靠性进行监测。对国家标准GBW04409的氧同位素组成进行测试,δ18O测试结果与推荐值一致,分析精度优于0. 1‰。以上途径有效控制了氧同位素分馏,提高了BrF5氧同位素分析方法的适用性。     

水泥工艺的矿物特征研究

利用Ｘ射线衍射、扫描电子显微镜和光学显微镜等分析手段,对水泥熟料的矿物组成特征、晶体的生长程度及显微结构特征等进行了深入的研究。结果表明,该水泥熟料中含有损熟料质量的Ｃ１２Ａ７及α－Ｃ２Ｓ等物相;熟料的烧成是还原环境及过于快速的冷却条件下进行的。