Geotechnical Properties of Low Calcium and High Calcium Fly Ash

In this paper, a comparative study has been made for physical and engineering properties of low calcium and high calcium Indian fly ash. The grain size distribution of fly ash is independent of lime content. Fly ash particles of size >75 μm are mostly irregular in shape whereas finer fractions are spherical for low calcium fly ash. For high calcium fly ash, chemical and mineralogical differences have been observed for different size fractions. Compared to low calcium fly ash, optimum moisture content is low and maximum dry density is high for high calcium fly ash. Optimum moisture content is directly proportional and maximum dry density is inversely proportional to the carbon content. The mode and duration of curing have significant effect on strength and stress–strain behavior of compacted fly ash. The gain in strength with time for high calcium fly ash is very high compared to that of low calcium fly ash due to presence of reactive minerals and glassy phase.     

水泥聚苯模壳格构式混凝土墙体抗震性能的芯孔尺寸影响试验研究

为研究芯孔尺寸对传统型水泥聚苯模壳(EPSC)格构式混凝土墙体抗震性能的影响,对2个传统型EPSC格构式混凝土墙体原型试件进行低周往复荷载试验,2个试件芯孔直径分别为160 mm和120 mm;对比分析了2个试件的破坏特征和承载力、滞回曲线、骨架曲线、刚度退化等抗震性能。结果表明:芯孔直径大的复合墙体具有更优良的抗震性能;芯孔直径增加,复合墙体的承载力、抗侧刚度和耗能能力均有不同程度的提高。     

纤维水泥土力学性能的试验研究

为了解加入纤维对水泥土力学性能的影响,对素水泥土及纤维水泥土进行了无侧限抗压和疲劳试验。研究结果表明,添加纤维可小幅度提高水泥土的抗压强度;与素水泥土相比,纤维水泥土在达到应力峰值时的应变明显增大,破坏后的残余强度也有所提高;纤维的加入提高了水泥土的延性,减少了裂缝的开展,改善了其力学性能;添加纤维后水泥土抵抗疲劳的能力明显增强;掺入纤维对水泥土抗疲劳能力的提高程度远大于其对水泥土无侧限强度的提高程度;水泥土的应力水平和疲劳寿命之间具有单对数线性关系;在循环荷载作用下水泥土表现为低应力性破裂特征。     

The diagenetic history of Oligocene-Miocene sandstones of the Austrian north Alpine foreland basin

Diagenesis is an essential tool to reconstruct the development of reservoir rocks. Diagenetic processes - precipitation and dissolution - have an influence on pore space. The present paper aims to study the diagenetic history of deep-marine sandstones of the Austrian Alpine Foreland Basin. To reach that goal, sediment petrology and diagenetic features of more than 110 sandstone samples from water- and gas-bearing sections from gas fields within the Oligocene-Miocene Puchkirchen Group and Hall Formation has been investigated. Special emphasis was put on samples in the vicinity of the gas-water contact (GWC). The sediment petrography of sandstones of Puchkirchen Group and Hall Formation is similar; hence their diagenesis proceeded the same way. In fact, primary mineralogy was controlled by paleo-geography with increasing transport distance and diverse detrital input.Sediment petrographically, investigated sandstones from the water-bearing horizon seemed quite comparable to the gas-bearing sediments. In general, they can be classified as feldspatic litharenites to litharenites and display porosities of up to 30% and permeabilities of up to 1300 mD. The carbon and oxygen isotopic composition of bulk carbonate cements from these sandstones range from−3.8 to +2.2 and from −7.5 to +0.2‰ [VPDB]. However, near the Gas-Water Contact (GWC) a horizon with low porosities (<3%) and permeabilities (<0.1 mD) is present. This zone is completely cemented with calcite, which has a blocky/homogenous morphology. A slight, but significant negative shift in δ18O isotopy (−2.5‰) is evident.During early diagenesis the first carbonate generations formed. First a fibrous calcite and afterwards a micritic calcite precipitated. Further siliciclastic minerals, such as quartz and feldspar (K-feldspar and minor plagioclase), exhibit corroded grains. Occasionally, clay minerals (illite; smectite, chlorite) formed as rims around detrital grains. Late diagenesis is indicated by the formation of a low permeable zone at the GWC.     

Granite weathering and silcrete formation on the Yilgarn Block,Western Australia

Weathering profiles developed on granitic rocks, exposed in the breakaways of the Barr‐Smith Range in the N of the Yilgarn Block of Western Australia, consist of kaolinitic saprolites merging upwards into silcrete, sandstone and grit. The sandstones and silcretes may also form columns or dykes, penetrating downwards into the saprolite. The silcretes are cemented by quartz and anatase, with zircon (QAZ‐cement), and‐the sandstones are cemented by aluminosilicates, either apparently amorphous (as siliceous allophane) or partly crystalline, as kaolinite and opaline silica. Transitional zones between silcretes and sandstones have all cement types. The profiles are characterized by low concentrations of alkalis and alkaline earths and most metals. The QAZ‐silcrete horizons may contain over 3% TiO₂ and 1000 p.p.m. Zr. The profiles evolved through at least four stages: (i) Formation of the deep saprolite‐sand weathering profile by kaolinization of feldspar and mica at depth, and the solution of kaolinite near the top of the profile, causing settling of resistant quartz grains, (ii) Precipitation of QAZ‐cement, the TiO₂ and SiO₂ being derived partly by lateral migration from upslope. (iii) Precipitation of aluminosilicates, in the sandstone and the saprolite. (iv) Erosion and exposure of the profiles by pedimentation. A similar profile occurs further S, at Gabbin, but no QAZ‐silcrete is present and the only exposures are in exploration pits. The kaolinitic saprolite‐quartz sand profiles probably formed under humid conditions, as the equivalents of ferruginous laterite developed on more basic rocks nearby and of lateritic bauxite in the Darling Range. However,’ the sand was a surface horizon and there is no evidence that there was ever a ferruginous zone at these sites. The sequential precipitation of QAZ‐ and aluminosilicate‐cements was probably, a response to increasing aridity and reduced groundwater flow. Aluminosilicate‐cemented materials tend to disaggregrate on exposure but they are probably more abundant than the more prominent QAZ‐silcretes.     

Utilization of sodium waterglass from sugar cane bagasse ash as a new alternative hardener for producing metakaolin-based geopolymer cement

Sugar cane bagasse ash from SOSUCAM company in Cameroon was used to synthesize sodium waterglass as a new alternative hardener. The new hardener was used to prepare metakaolin-based geopolymer cements. The compressive strength of the resulting geopolymer cement cured at room temperature for 28 days was 32.9 MPa. Samples soaked for 28 days in water in parallel experiments revealed a strength of 31.4 MPa. This shows that exposure of water does not lead to any weakening. The value of water absorption was 7.1% in the water-soaked cements, indicating the presence of fewer pores and voids than in the dry cements. However, in SEM micrographs, the microstructure of geopolymer cement appears rather homogeneous and compact without any change by water soaking. It can thus be concluded that sodium waterglass from sugar cane bagasse ash can be used as an alternative hardener or reactive ingredient for producing geopolymer cement with a high degree of cross-linking geopolymer framework. The use of this low-value silica-rich waste for producing sodium waterglass results in environmental benefits including a significant reduction of CO₂ emission and energy consumption compared to the production of commercial sodium waterglass.     

深层搅拌法在超软弱港口地基上的工程应用

某港口堆场地基上部5．0m系吹填而成,地表下18m范围均属软土,经真空预压初级加固后地基承载力仅在80—90kPa,局部区域上部淤泥土层土性指标较差,含水量大于50％,地基承载力不足60kPa。为了使地基达到230kPa的承载要求,设计采用深层搅拌法加固超软弱地基。通过现场成桩工艺试验和检测表明,桩身水泥土强度在90d龄期时大于1．80MPa,单桩承载力标准值大于150kN,以φ600桩径、桩长13．5m、置换率为0．308和φ500桩径、桩长13．5m、置换率为0．267两种方案布置的复合地基承载力标准值均超过了230kPa的设计要求。试验结果表明,深层搅拌法在港口超软弱地基土应用只要施工工艺适当,完全可以使地基承载力提高2—3．5倍以土,从而节省大量的工程投资。     

水泥固化锌污染土电阻率与强度特性研究

以标准砂及普通硅酸盐水泥为试验材料,制作水泥固化锌污染土样,进行了一系列电阻率和无侧限抗压强度试验。研究了交流电频率对水泥固化锌污染土电阻率的影响、不同含量锌离子对水泥缓凝作用的影响、锌离子含量和龄期分别对水泥土电阻率和强度的影响、电阻率与无侧限抗压强度的关系。结果表明：电阻率随电流频率的增加而明显降低,尤其当频率低于50 kHz时为甚;不同含量的锌离子对水泥土的缓凝作用影响明显,随着锌离子含量的增大,水泥土强度的充分发挥所需时间逐渐增长,但在锌离子含量为500 mg/kg时,缓凝作用表现异常;电阻率和强度均随龄期的增加而增长,随锌离子的含量的增加上下波动,电阻率在锌离子含量为50 mg/kg和500 mg/kg时出现极值,强度在锌离子含量为100 mg/kg和500 mg/kg时出现极值;在各个龄期下,电阻率与强度均呈现出很好的线性关系。     

水泥–粉煤灰–煤渣–吹填粉细砂混合料强度试验

针对大型堆填场基层结构工程,本着就地取材节约成本的原则,利用吹填砂作为骨料,添加粉煤灰、煤渣和水泥,采用正交试验方法,编制正交设计表,配制不同比例的混合料进行无侧限抗压强度试验。采用方差对不同龄期的混合料抗压强度进行分析,并对混合料加固机理进行研究,给出了混合料最佳质量配比,即水泥20%,粉煤灰15%,煤渣10%,此时混合料的强度最大;其水泥掺量对混合料强度起着关键作用,随着龄期的增长粉煤灰与煤渣对混合料强度影响程度逐渐增强,不过煤渣对混合料初期强度影响不及粉煤灰。     

粉细砂地层防渗帷幕综合施工方法

四川省武都水库右岸EL574 m灌浆平洞揭露出厚度2.3～9.8 m的粉细砂层,普通水泥高压灌浆无法形成可靠的防渗帷幕。采用高压旋喷、湿磨细水泥、化学灌浆的组合处理方式,取得了较好的施工效果。通过钻孔压水、大功率声波CT、单孔声波、钻孔全景数字成像等方法检测,表明达到了设计防渗要求。