FRP约束混凝土柱抗震性能若干问题的探讨

基于实验研究和理论分析结果,对纤维增强复合材料(FRP)约束混凝土柱抗震性能研究中存在的若干关键问题进行了探讨,包括FRP约束混凝土构件在往复荷载作用下的受力特点、破坏特征、荷载-位移关系、弯矩-曲率关系、耗能及延性变化规律等,最后重点探讨了FRP约束混凝土柱在往复荷载作用下的刚度特性。     

部分预制型钢混凝土梁抗震性能试验研究

为探究部分预制型钢混凝土梁的抗震性能,进行了7个部分预制型钢混凝土梁试件的拟静力试验,研究了试件的裂缝开展过程、破坏形态、承载能力、延性、耗能能力和刚度退化情况,探究预制截面模式、剪跨比和后浇混凝土强度等对其抗震能力的影响。结果表明:地震作用下,该7个试件力学性能较好,剪跨比是影响试件抗震性能的首要要素,剪跨比大的试件耗能能力强,型钢约束部分混凝土可以提高试件的耗能能力,截面模式和后浇混凝土强度对抗震性能影响不大。     

不同跨高比对多层钢框架内填混凝土深梁结构抗震性能影响

为了研究不同跨高比多层钢框架内填混凝土深梁结构的抗震性能,在钢框架内填混凝土深梁滞回性能试验的基础上,利用ABAQUS对六层纯钢框架（结构一）、钢框架内填跨高比为2混凝土深梁结构（结构二）和钢框架内填跨高比为0.75混凝土深梁结构（结构三）进行弹塑性时程分析。结果表明:内填混凝土深梁使结构整体刚度明显增大;在地震波的作用下,结构二的最大顶点位移降低可达58.3%,结构三的最大顶点位移降低可达89.3%,内填混凝土深梁,结构的抗侧移性能得到了极大改善,且随着深梁跨高比的减小而大幅度提升;结构二滞回曲线饱满,呈现纺锤形,混凝土深梁充分起到了第一道防线作用。经济合理的钢框架内填混凝土深梁结构具有一定的工程应用价值。     

Homogenization‐based analysis of anisotropic damage in brittle materials with unilateral effect and interactions between microcracks

This paper is devoted to micromechanical modeling of induced anisotropic damage in brittle geomaterials. The formulation of the model is based on a proper homogenization procedure by taking into account unilateral effects and interactions between microcracks. The homogenization procedure is developed in the framework of Eshelby's inclusion solution and Ponte‐Castaneda and Willis (J. Mech. Phys. Solids 1995; 43 :1919–1951) estimate. The homogenization technique is combined with the thermodynamics framework at microscopic level for the determination of damage evolution law. A rigorous crack opening–closure transition condition is established and an energy‐release‐rate‐based damage criterion is proposed. Computational aspects on the implementation of micromechanical model are also discussed. The proposed model is evaluated by comparing numerical predictions with experimental data for various laboratory tests on concrete. Parametric studies on unilateral effects and influences of microcracks interactions are finally performed and analyzed. Copyright © 2008 John Wiley & Sons, Ltd.     

猴子岩水电站导流洞HF混凝土施工工艺研究

HF混凝土是由HF外加剂、优质粉煤灰（或其它优质掺合料如硅粉、磨细矿渣等）、符合要求的砂石骨料和水泥等组成,并按规定的要求进行设计和组织施工浇筑的混凝土。HF混凝土是水利水电工程中应用于抵抗水流冲刷泥沙磨损、高速水流空蚀破坏的高性能（综合性能优良）的水工抗冲耐磨护面材料。猴子岩导流洞底板设有30cm厚的HF混凝土面层,为保证施工质量,结合其它工程实际,进行了HF混凝土施工工艺的研究。     

大体积混凝土的施工控制要点

以邢台市七里河大桥为例,基于施工中采取的施工工艺,针对大体积混凝土出现温度裂缝的病害,提出了相应的施工控制要点。     

Research of Recycled Salt and Glauber’ Salt Precipitation Rules of Yabulai Salt Lake Brine

正1 Introduction The main production of Yabulai salt lake was original salt and recycled salt many years ago.After decade’s production,the sale lake resource is more and more deficient.Glauber's salt and magnesium salt are concentrated in brine now.It could affect the quality of the salt.In recent years,research had done much work to     

Meso‐scale particle modeling of concrete deterioration caused by alkali‐aggregate reaction

A meso‐scale particle model is presented to simulate the expansion of concrete subjected to alkali‐aggregate reaction (AAR) and to analyze the AAR‐induced degradation of the mechanical properties. It is the first attempt to evaluate the deterioration mechanism due to AAR using the discrete‐element method. A three‐phase meso‐scale model for concrete composed of aggregates, mortar and the interface is established with the combination of a pre‐processing approach and the particle flow code, PFC2D. A homogeneous aggregate expansion approach is applied to model the AAR expansion. Uniaxial compression tests are conducted for the AAR‐affected concrete to examine the effects on the mechanical properties. Two specimens with different aggregate sizes are analyzed to consider the effects of aggregate size on AAR. The results show that the meso‐scale particle model is valid to predict the expansion and the internal micro‐cracking patterns caused by AAR. The two different specimens exhibit similar behavior. The Young's modulus and compressive strength are significantly reduced with the increase of AAR expansion. The shape of the stress–strain curves obtained from the compression tests clearly reflects the influence of internal micro‐cracks: an increased nonlinearity before the peak loading and a more gradual softening for more severely affected specimens. Similar macroscopic failure patterns of the specimens under compression are observed in terms of diagonal macroscopic cracks splitting the specimen into several triangular pieces, whereas localized micro‐cracks forming in slightly affected specimens are different from branching and diffusing cracks in severely affected ones, demonstrating different failure mechanisms. Copyright © 2012 John Wiley & Sons, Ltd.     

Cohesive‐frictional model for bond and splitting action of prestressing wire

This paper presents a numerical procedure for bond between indented wires and concrete, and the coupled splitting process of the surrounding concrete. The bond model is an interface, non‐associative, plasticity model. It is coupled with a cohesive fracture model for concrete to take into account the splitting of such concrete. Bond between steel and concrete is fundamental for the transmission of stresses between both materials in precast prestressed concrete. Indented wires are used to improve the bond in these structural elements. The radial component of the prestressing force, increased by Poisson's effect, may split the surrounding concrete, decreasing the wire confinement and diminishing the bonding. The combined action of the bond and the splitting is studied with the proposed model. The results of the numerical model are compared with the results of a series of tests, such as those which showed splitting induced by the bond between wire and concrete. Tests with different steel indentation depths were performed. The numerical procedure accurately reproduces the experimental records and improves knowledge of this complex process. Copyright © 2010 John Wiley & Sons, Ltd.