应用于白光显示的Tm3+/Ho3+/Yb3+共掺碲酸盐玻璃上转换发光特性研究

用高温熔融法制备了Tm³⁺/Ho³⁺/Yb³⁺共掺碲酸盐玻璃(TeO₂-ZnO-La₂O₃)样品,测试了玻璃样品的吸收光谱和上转换发光光谱,分析了上转换发光机理.结果发现:在975 nm波长激光二极管(LD)激励下,制备的碲酸盐玻璃样品可以观察到强烈的红光(662 nm)、绿光(546 nm)和蓝光(480 nm)三基色上转换发光,红光对应于Tm³⁺离子     

Nd3+ :Gd3 Sc2 Al3 O12 晶场能级及拟合

Nd³⁺ :GSAG是性能优良的942 nm激光晶体.用提拉法成功生长Nd³⁺ :GSAG单晶,研究其室温透射光谱,辨认位置高达29967 cm^-1的68个Nd³⁺晶场能级.对这些能级拟合了自由离子及晶场Hamilton参量,拟合标准偏差为16.7 cm^-1,表明实验与计算能级符合很好.获得的Hamilton参量可用于计算Nd³⁺ :GSAG中Nd³⁺的     

蓝色荧光粉Sr2B5O9Cl:Eu2+发光特性的研究

采用高温固相法合成了近紫外光激发的蓝色荧光粉Sr₂B₅O₉Cl:Eu²⁺,研究了SrCl₂ ·6H₂O用量和Eu²⁺浓度对其结构和发光性能的影响.随着Eu²⁺浓度的增加,其结构无明显变化,发光强度先增强后减弱,当其浓度为8mol%时,荧光粉的发光强度最大;当用Ca取代Sr时,荧光粉的发射峰从425 nm红移到453 nm. 适当过量     

Sr2CoO4-δ薄膜中的自旋玻璃态的磁性质研究

用脉冲激光沉积方法(PLD)在铝酸镧衬底上制备了c取向的高氧空位含量的锶钴氧薄膜.X射线衍射分析表明薄膜单一取向且没有明显杂相.原位的高气压反射式高能电子衍射仪(RHEED)监测显示,薄膜为层状生长.通过对薄膜磁化强度随温度、磁场及时间的变化曲线进行测量,发现零场冷曲线上可能存在两个特征温度:T_f和T_a.T_f为对应玻璃态的冻结温度而T_a对应少量的不缺     

海洋解木糖赖氨酸芽孢杆菌JZ008对重金属Cd2+、Cr3+和Cu2+的吸附作用

利用单因素实验对海洋解木糖赖氨酸芽孢杆菌(Lysinibacillus xylanilyticus sp.JZ008)培养条件进行了优化.优化后的培养条件:温度为35℃、pH值为7.5、接种量为3%(V/V)、装液量为50cm3/250 cm3时,菌量达到2.01×108CFU/cm3,比优化之前提高了40.6%.添加海藻寡糖可以促进菌株生长,添加量为5.0 g/dm3时发酵液中活菌数是对照组的2.51倍.研究了菌株JZ008对Cd~(2+)、Cr~(3+)、Cu~(2+)3种重金属离子的吸附特性,结果表明菌株JZ008对3种重金属离子污染的水溶液吸附率效果明显,20 d吸附率分别达到95.6%、96.4%、87.0%.土壤重金属吸附实验结果表明,海藻寡糖复配菌株JZ008组对Cd~(2+)、Cr~(3+)、Cu~(2+)吸附效果明显,60 d吸附率分别达到82.5%、82.0%、86.9%.菌株JZ008对重金属的优良吸附作用为进一步开发解木糖赖氨酸芽孢杆菌在重金属修复方面的应用奠定了基础.     

钪原子的自电离里德伯能级3d4s(1 D2)nf2 D3/2,3d4s(1 D2)nf2 F5/2和3d4s(1 D2)np2 D3/2的理论研究

在多通道量子亏损理论框架下,利用相对论多通道理论,分别在冻结实近似和考虑偶极极化下计算钪原子的J^π=(3/2)^-,(5/2)^-的三个收敛于 3d4s(¹D₂)的自电离里德伯系列的能级.对3d4s(¹D₂)np²D_3/2和3d4s(¹     

Cu3 N弹性和热力学性质的第一性原理研究

利用基于密度泛函理论的第一性原理全势线性缀加平面波方法,研究了立方反ReO₃结构Cu₃N在零温(0 K)零压下的平衡晶格常数、体弹模量及其对压强的一阶导数,计算结果与其他实验及理论结果基本相符. 同时得出Cu₃N的弹性常数,Poisson比等,并分析出Cu₃N在零温零压下是稳定的. 通过准谐Debye模型计算Cu₃N的热力学性质,得到了Cu₃N的晶格常数、等压比热容、等容比热     

Cs2NaMF6(M＝Al,Ga):Cr3+ 络合分子体系局域结构和基态分裂的理论研究

采用双自旋轨道耦合系数模型并结合完全能量矩阵的方法对Cs₂NaMF₆(M=Al, Ga):Cr³⁺ 体系中Cr³⁺ 离子的基态分裂和局域结构进行了研究.通过模拟光谱和EPR谱确定了Cr³⁺ 取代 M³⁺ 形成的两种占位结构的畸变角,发现用双自旋轨道耦合系数模型与单自旋轨道耦合系数模型计算出的畸变角Δθ存在较大的差异.这表     

Fe（OH）3胶体与铜离子作用的研究

使用切向流超滤系统得到粒度较均匀的Fe(OH)3胶体,进而对Fe(OH)3胶体粒子与Cu2+的作用进行了研究,并将实验结果与南沙群岛海区表层水中铜与胶体物质结合状况的调查数据进行了比较分析,得到如下结果(1)在海水介质中,铜在Fe(OH)3胶体上结合的百分率(pH>5)随pH的升高而下降,随着Fe(OH)3胶体浓度的减小而下降.(2)在天然海水介质中,使铜在Fe(OH)3胶体上结合的百分率在50%-70%的有机物浓度为1.0mg     

Amorphous Er2O3 films for antireflection coatings

This paper reports that stoichiometric, amorphous, and uniform Er₂O₃ films are deposited on Si(001) substrates by a radio frequency magnetron sputtering technique. Ellipsometry measurements show that the refractive index of the Er₂O₃ films is very close to that of a single layer antireflection coating for a solar cell with an air surrounding medium during its working wavelength. For the 90-nm-thick film, the reflectance has a minimum lower than 3% at the wavelength of 600 nm and the weighted average reflectances (400--1000 nm) is 11.6%. The obtained characteristics indicate that Er₂O₃ films could be a promising candidate for antireflection coatings in solar cells.     

Si2O2 molecule: structure of ground state and the excited properties under different external electric fields

Geometry and vibrational frequencies of the ground state of Si₂O₂ molecule are studied using density function theory (DFT) at the level of cc-pvtz and 6-311++G^**. It is found that the optimizing value by B3lyp/cc-pvtz is closer to the experimental data. The excited properties under different external electric fields are also investigated by the time-dependent-DFT method. Transitions from the ground state of Si₂O₂ molecule to the first singlet state under different external electric fields can take place more easily. The corresponding absorption spectral line is about 360 nm in wavelength and the excitation energy is about 3.4 eV.     

锰掺杂对Ba(Zr,Ti)O3陶瓷压电与介电性能的影响

采用氧化物固相反应法制备了锰掺杂改性的Ba(Zr_0.06Ti_0.94)O₃陶瓷.研究了锰的掺杂量对Ba(Zr_0.06Ti_0.94)Mn_xO₃ (BZTM)陶瓷的结构、介电和压电性能的影响.实验发现,当锰含量x<0.5 mol%时进入晶格,使材料压电性能提高,损耗减小,表现出受主掺杂的特性;当锰含量x>0.5 mo     

Cr4+ :Ca2 GeO4激光晶体生长及结构表征

采用助熔剂法,以CaCl₂为助熔剂,生长Cr⁴⁺ :Ca₂GeO₄新型近红外可调谐激光晶体.通过X射线衍射(XRD)、激光Raman光谱、X射线光电子能谱(XPS)等方法对晶体进行结构表征.结果表明,得到的晶体为单斜晶系镁橄榄石结构的低温γ-Cr⁴⁺ :Ca₂GeO₄单晶,晶格参数为a=5.3209 (1 =0.1 nm)     

Cu2+/SnO2复合纳米光催化剂的制备及其对海洋柴油污染物的降解

采用化学沉淀法成功制备了Cu2+/SnO2复合纳米光催化剂,采用XRD、SEM等测试手段对复合纳米光催化剂的粒径、形态等进行表征。在紫外光条件下,分别改变催化剂掺杂比、催化剂煅烧温度、催化剂投加量、柴油初始含量和光照时间等单因素,探究不同条件对Cu2+/SnO2复合纳米光催化剂降解海洋柴油污染物的影响。结果表明,自制复合纳米光催化剂可以有效降解海水中的柴油污染物,在紫外光作用下,于400℃下煅烧Cu/Sn掺杂比为0. 03的Cu2+/SnO2复合纳米光催化剂、投加量为0. 2 g/dm3、柴油初始含量为0. 15 g/dm3、H2O2溶液含量为0. 2 g/dm3、溶液的p H为7、光照时间3 h时效果最好,海水中柴油的去除率最高,达到86. 98%。Cu2+/SnO2复合纳米光催化剂用聚丙烯纳米球负载后可以实际应用于海洋中,便于回收。     

琼胶/SiO2复合纤维的制备及性能研究

利用湿法纺丝技术制备了琼胶/SiO₂复合纤维,对琼胶分子在溶液中的分散性、纺丝液流变性、纤维的形貌、化学结构分别用DLS、旋转黏度计、SEM、FTIR和XRD进行了表征,并对纤维的力学性能、热性能和吸湿性能进行了测定。研究结果表明:琼胶分子在溶液中呈纳米尺度分布,纺丝液具有良好的流动性;琼胶/纳米SiO₂复合纤维具有良好的形态。随着纳米SiO₂的添加量逐渐提高,复合纤维的力学拉伸强度先增强后降低,复合纤维的吸水性降低,复合纤维的热稳定性逐渐增强。结合复合纤维综合性能,纳米SiO₂的最佳添加质量分数为0.5%。