麦秸秆加筋盐渍土重型击实效果的影响因素分析

为解决因滨海盐渍土的盐胀和溶陷而引起土的强度降低问题,可采用麦秸秆加筋的方法处理盐渍土,以提高土的强度和抗变形能力。将盐渍土与一定长度和数量的防腐麦秸秆均匀拌和在一起,按照一定的碾压功将其碾压密实,此时土的含水率、麦秸秆的质量加筋率和加筋长度是影响加筋土重型击实效果的3个因素。试验结果揭示,（1）加筋土的最大干密度均小于盐渍土的,最优含水率变化不大。（2）与盐渍土一样,随着含水率的增加,加筋土的干密度先升后降。（3）随质量加筋率和加筋长度的增加,加筋土的最优含水率变化不明显,最大干密度持续下降,但降幅较小。（4）0.2%质量加筋率加筋土的干密度最大,0.3%质量加筋率的最小。（5）30 mm加筋长度加筋土的干密度最大,70 mm加筋长度的最小。建议按0.2%质量加筋率和30 mm加筋长度的防腐麦秸秆制备三轴压缩试样,以研究麦秸秆加筋滨海盐渍土的抗剪强度和应力-应变特性。     

加筋条件和含水率对加筋土抗压强度和应力应变的影响

由滨海盐渍土的盐胀、溶陷和吸湿软化引起的土的低强度和大变形问题,可通过麦秸秆加筋的方法予以应对。加筋土的抗压强度及应力应变特性与麦秸秆的加筋长度、加筋率和土的含水率有关。加筋土的抗压强度试验结果证实：0.25%加筋率的加筋土抗压强度最大,0.20%和0.30%的次之;50 mm加筋长度加筋土的抗压强度最大,70 mm的最小。0.25%加筋率的加筋土应力应变曲线的峰值最大;随加筋长度的增加,加筋率对应力应变的影响程度降低。随加筋长度的增加,加筋土的应力应变曲线由应变软化型渐变为应变硬化型,以70 mm加筋长度的最为明显。低于最优含水率,应力应变曲线存在峰值;高于最优含水率,加筋土逐渐转向塑性变形。总结麦秸秆加筋土的抗压强度和应力应变的变化规律,为后期的三轴抗剪强度及其偏应力应变特性研究提供借鉴。     

以抗压强度确定麦秸秆加筋盐渍土的加筋条件

滨海盐渍土具有盐胀、溶陷和吸湿软化等不良工程地质问题,未经固化处理不能满足工程建设的强度和变形要求。借鉴合成纤维加筋土和草根土的研究成果,初步确定包括加筋长度、质量加筋率、加筋形状和石灰掺加量等因素的麦秸秆加筋盐渍土的加筋条件。通过抗压强度试验和Taguchi正交试验设计优化方法,确定最优加筋条件为：加筋长度为10 mm、加筋率为0.25 %、形状为1/4圆弧状和石灰掺加量为8 %。以麦秸秆作加筋与石灰共同加筋固化滨海盐渍土,其抗压强度试验结果表明,石灰+麦秸秆加筋盐渍土的抗压强度、抗变形能力和水稳性均优于石灰土和盐渍土。初步的研究成果对今后系统研究麦秸秆加筋滨海盐渍土的抗压强度、抗剪强度和变形特性等具有指导意义。     

含盐量与布筋方式对纤维加筋土抗压性能的影响

纤维与石灰粉煤灰加筋固化土的抗压性能受到含盐量与纤维布筋方式的影响。选择9个含盐量(0.5%、1.5%、2.5%、3.5%、4.5%、5.5%、7%、8.5%和10%)和6种布筋方式(试样整体、上1/3、上1/2、中1/3、下1/2和下1/3),开展固化土与加筋固化土的无侧限抗压试验。试验结果表明,随含盐量的增加,固化土及纤维加筋固化土的抗压强度与破坏应变先减小后增大,临界含盐量为7%左右;纤维位于试样的中1/3处时抗压强度最大,试样整体、下1/2、上1/2、下1/3与上1/3处布筋时抗压强度依次减小;固化土与纤维加筋固化土的应力–应变关系均为应变软化型;试样整体布筋时,土的抗变形性能最优。纤维加筋作用可抵消高含盐量引起的盐胀与吸湿软化对固化土抗压性能的破坏。选择试样整体布筋或中部布筋时,加筋效果更为显著。     

降低上海软粘土变形效应的加筋试验研究

为改良上海粘土的强度和变形特性,分别采用棕榈和麦秸秆加筋,以提高土的强度和抗变形性能。试验以质量加筋率和加筋长度作为影响因素,分析比较两种加筋土的无侧限抗压强度。试验结果为：(1)棕榈加筋土的无侧限抗压强度高于麦秸秆加筋土,两种加筋土均高于素土。(2)棕榈的适宜加筋条件为：质量加筋率1.0%,加筋长度的平均值15mm;四分之一圆管状麦秸秆的适宜加筋条件为：质量加筋率0.3%~0.4%,加筋长度15mm。(3)棕榈加筋土的应力应变曲线表现为应变强化型,麦秸秆加筋土的应力应变曲线表现为应变软化型。初步试验结果表明,棕榈与麦秸秆均适宜作上海地区粘土的加筋材料,加筋效果棕榈优于麦秸秆。     

干密度和含水率对稻草加筋土强度与变形的影响

以防腐处理后的稻草加筋滨海盐渍土,完成了三种干密度和三种含水率的稻草加筋土的抗压实验和三轴UU压缩实验。结果表明:干密度较大时,加筋土的抗压强度和抗剪强度较高,达到峰值强度的应变较大,即抗变形能力较强;随含水率的增加,加筋土的强度降低,抗变形能力减弱;加筋稻草增强了土的抗变形能力,提高了土的粘聚力,但对内摩擦角的影响很小;在最优含水率和最大干密度下,加筋效果最优。      

麦秸秆的力学性能及加筋滨海盐渍土的抗压强度研究

为开展天然草本纤维材料防腐前后的力学性能及加筋滨海盐渍土的抗压强度增长规律研究,本文探讨了麦秸秆的微结构特征及防腐方法、测试并对比了防腐前后的麦秸秆的质量增加率、吸水率、极限拉力和极限延伸率,证实用SH胶浸泡麦秸秆不仅能起到防腐作用,还可提高麦秸秆的力学性能。完成了不同加筋长度、不同加筋率及浸胶后呈不同状态麦秸秆的加筋滨海盐渍土无侧限抗压强度试验,结果证实:掺加长10mm麦秸秆优于掺加长20 mm麦秸秆;适宜加筋率为0.3%~0.4%;掺加浸泡SH胶后呈潮湿状态的麦秸秆优于掺加浸泡SH胶后呈干燥状态的;麦秸秆加筋盐渍土的抗压强度高于素盐渍土。初步的研究结果表明,麦秸秆适宜作加筋材料使用。     

聚丙烯纤维加筋对高岭土固结压缩特性影响试验研究

工程中为了改良压实黏土的强度和抗干裂性能,将分散的聚丙烯纤维均匀掺入土体中制成纤维加筋土。利用聚丙烯纤维与高岭土在室内人工拌和并压制成纤维加筋土样,基于一维固结试验研究了控制干密度条件下纤维加筋掺量与长度对加筋高岭土固结、压缩特性的影响规律。研究结果表明,在控制干密度和纤维长度条件下,随着纤维掺量的增加,加筋土的固结系数和压缩模量均先增大后减小;掺量为0.2%时固结系数最大,掺量为0.1%～0.15%时压缩模量最大;在控制干密度和纤维掺量条件下,随着纤维长度的增加,加筋土的固结系数先减小后增大,纤维长度为10 mm时固结系数最小;当固结压力较高（≥400 kPa）时,加筋土的压缩模量随纤维长度增大而减小。此外,加筋土的压缩指数总体上随纤维掺量和纤维长度的增大而增大,但纤维掺量为0.15%～0.20%以及纤维长度为10 mm时压缩指数有一极小值。     

环境温度对石油污染滨海盐渍土强度及变形特性的影响

环境温度影响石油黏滞性,改变石油污染土的力学特性。借助无侧限抗压强度试验,研究不同温度条件下石油污染滨海盐渍土的强度及变形特性。结果证实:温度对石油污染盐渍土力学性质影响显著,温度越高,污染土抗压强度越低,20℃时,含油率15%污染土的抗压强度较未污染土下降近70%;石油污染滨海盐渍土的抗压强度随含油率的增加先增大后减小,环境温度与污染土强度峰值点处的含油率反相关,10℃、20℃、30℃条件下,强度峰值点处的含油率分别为15%、10%和5%;石油污染盐渍土表现为应变软化型破坏,含油率及环境温度影响石油污染盐渍土的抗变形能力,土样的破坏面积和裂缝宽度随含油率增加及温度升高而增大。     

EPS颗粒混合轻量土无侧限抗压强度特性试验研究

为研究EPS颗粒混合轻量土的密度、强度和变形特性,对不同水泥掺量、EPS颗粒掺量、含水率和龄期的轻量土进行密度无侧限抗压强度试验。试验配置轻量土无侧限抗压强度范围为103.2~1359.0 kPa,且随水泥掺量的增大呈指数关系增大的趋势,随EPS颗粒体积比的增大而呈线性关系减小的趋势。在大于最优含水率情况下,含水率越高,无侧限抗压强度越低,两者为指数关系,而龄期的增长能够使得轻量土的无侧限抗压强度呈双曲线增大的趋势。EPS颗粒混合轻量土的应力-应变关系曲线主要表现为应变软化型,含水率和EPS颗粒体积比的增大会使得轻量土的应力-应变关系曲线逐渐向硬化型转化。水泥掺量和龄期的增大能够增强轻量土的脆性特征,增大刚度。而含水率和EPS颗粒体积比的增大则使得轻量土的延性特征增强,刚度减小。研究成果对实际工程应用具有参考价值。     

冻土单轴抗压强度影响因素的试验研究

新疆地区是我国典型的咸寒区, 渠基土在冬季的冻结引起了输水渠道衬砌的破坏. 为了解冻结状态下渠基土的物理力学特性, 在常应变率条件下对新疆北疆季节性冻土区的含硫酸钠渠基土进行了多种条件下的单轴抗压强度试验. 结果表明: 单轴抗压强度随温度的降低线性增加; 单轴抗压强度随干密度的增加而增大, 二者之间具有较好的幂函数关系. 与氯化钠盐渍土不同, 硫酸盐渍土的单轴抗压强度随着硫酸钠含量的升高而增大, 并且呈现近似线性增加的特性.     

Geo-engineering properties of expansive soil treated with xanthan gum biopolymer

ABSTRACT

This paper presents the effectiveness of xanthan gum (XG) biopolymer in stabilising the expansive soil. The XG biopolymer is mixed with expansive soil in different proportions such as 0%, 0.2%, 0.5%, 0.8% and 1.0% by weight of the dry soil mass. The plasticity, compaction, swelling, compressibility, hydraulic conductivity, strength and durability characteristics of the treated and un-treated expansive soil are examined. Results show that the plasticity index of the treated soil mass initially increases but beyond 0.5% biopolymer addition it decreases sharply. The optimum moisture content and maximum dry density of treated soil, found out from light and heavy compaction tests, do not follow any definite trend. It is also found that increasing XG content increases compressibility slightly but, it reduces swelling pressure, differential free swelling value and hydraulic conductivity remarkably. On the other hand, time-dependent compressive strength and resistance to mass loss increases with increasing XG content. Microscopic examination confirms the formation of gel-like linkage, which brings about the modifications in the treated expansive soil.     

非饱和含盐土壤水扩散系数试验研究

在室内用水平土柱吸渗法对不同含盐量、不同溶液浓度和不同土类的土壤水扩散系数进行了试验研究.试验结果表明:土壤水(或盐水)扩散系数与土壤的体积含水量之间具有指数函数的关系,且随着含水量的降低而减小.当同一类土在干容重和含水量相同时,土壤水扩散系数是随土中含盐量的增多而增大,以粗粒土最为明显.不同浓度的盐水在土壤中运行时,其盐水的扩散系数是随盐水浓度的增大而减小.     

高分子固化剂/纤维改良砂土的抗拉强度试验研究

本文采用高分子固化剂和聚丙烯纤维对砂土进行复合加固,通过对不同聚丙烯纤维含量、固化剂含量和干密度的重塑试样进行抗拉试验,测量试样破坏时的最大拉应力,对比不同试样抗拉强度的变化规律,并结合扫描电镜对复合加固机理进行较为深入的分析。试验结果表明,高分子固化剂和聚丙烯纤维的复合加固能够显著提高砂土的抗拉强度,纤维含量、固化剂含量和干密度对改良砂土的抗拉强度均具有较大的影响。当干密度和高分子固化剂含量一定时,砂土抗拉强度随纤维含量的增加逐渐增加,当固化剂含量为4%,干密度为1.5 g·cm-3时,纤维含量从0.2%到0.8%,抗拉强度从79.06 kPa增加到194.51 kPa;当干密度和纤维含量一定时,砂土抗拉强度随着高分子固化剂含量的增加而增加,当纤维含量为0.8%,干密度为1.5g·cm-3时,固化剂含量从1%到4%,抗拉强度从63.16 kPa增加到194.51 kPa;当高分子固化剂含量和纤维含量一定时,抗拉强度随着干密度的增加先增加后减小,在干密度为1.55 g·cm-3左右达到峰值。复合加固结合物理和化学加固的优点,通过纤维在颗粒间的相互作用力和固化剂在颗粒间的联结力,从而提高改良砂土的抗拉性能。本研究结果为进一步研究砂土复合加固及其工程应用提供一定的参考依据。     

Study on Strength Influence Mechanism of Fiber-Reinforced Expansive Soil Using Jute

This study was undertaken to research the effects of jute fiber content, fiber length, water content and dry density of reinforced and unreinforced soil on the strength influence mechanism by implementing a series of laboratory tests and analysis. The most efficient fiber reinforcement effects was achieved by means of adding jute fiber with content of 0.6 % and length of 6 mm into expansive soil specimen prepared at maximum dry density and optimum moisture content. The cohesion of reinforced specimens increased first with increasing fiber content and fiber length and then decreased with further increase in fiber content and fiber length. The internal friction angle of reinforced specimens were not affected significantly by fiber content and fiber length. Higher water content reduces the fiber reinforcement effects by means of acting as lubricant in the interface of fiber and soil particles. Fiber reinforcement effects is more prominent for specimens prepared at higher dry density by increasing the effective contact area of fiber/soil. The application prospect of soil reinforcement using natural fiber is impeded by the hydrophilic nature and biodegradability of natural fiber, thus, studies on using chemical additive to do surface treatment for natural fiber are needed to improve the interfacial interaction of fiber/soil so as to widen the application of natural fiber.     

超氯盐渍土的工程特性指标研究

以探讨超氯盐渍土的含盐量与工程特性指标间关系为目的 ,采用室内土工试验与数学分析相结合的方法 ,深入研究了含盐量对塑性指标、抗剪强度的影响以及盐渍土渗透系数与干重度、含水量之间的关系。研究发现 :超氯盐渍土洗盐前后可塑性变化幅度较大 ;抗剪强度随含盐量增加而增大 ;在干重度、含水量与渗透系数三者相互关系中存在界限含水量和界限干重度。所得结论对深入研究盐渍土的工程特性、指导盐田建设将有所裨益