土工格栅加筋碎石土大型三轴试验研究

在大型三轴仪上进行了素碎石土和加筋碎石土的三轴排水剪切试验，探讨了加筋碎石土的强度及变形特性；分析了塑料土工格栅的加筋机理，为加筋碎石土的理论计算提供了依据。     

土工格栅加筋膨胀土拉拔试验研究

土工格栅加筋技术对膨胀土地质灾害的防治具有特殊效果,但目前对土工格栅与膨胀土界面特性的研究不足。采用南水北调中线工程新乡段的膨胀性泥灰岩风化土作填料,塑料单向拉伸土工格栅作为加筋体,在叠环式剪切试验机上通过施加不同的竖向荷载对其界面特性进行了拉拔试验研究。研究结果表明,土工格栅在膨胀土中的拔出过程主要经过3个阶段,分别是界面静摩擦力阶段、渐进剪切阶段和整体运动阶段,各阶段受力特性有明显差异;随着法向应力的增大,静摩擦力在界面抗剪强度比值呈对数级增大,从50 kPa时0.20增大至400 kPa时0.57,极限值可达到0.75;对挡土墙、高边坡等加筋设计中应考虑最大静摩擦力所占比重,在格栅的不同竖向高度处所受垂直应力不同,分段设计更加合理。     

土与土工织物接触面力学特性的试验研究

在大型土与结构接触面循环加载剪切仪上添加了拉拔试验模块,进行了大尺寸的粗粒土与土工布接触面的单调和往返剪切试验以及土工布拉拔试验。剪切试验结果表明,粗粒土与土工布接触面出现了一定程度的应变软化,相对法向位移的变化受法向应力影响很大,并表现出异向性。土工布拉拔试验结果表明,由于土与土工织物接触面的剪胀造成该类接触面的抗剪强度与法向应力不再是线性关系;将接触面剪切试验和拉拔试验方法结合起来是研究土与土工织物接触面力学特性较为全面和合理的手段。     

土工格栅与土界面作用特性试验研究

土工格栅与土的界面摩擦特性指标是加筋土工程设计的关键。通过分析土工格栅与土的界面摩擦作用和进行了直剪摩擦试验和拉拔摩擦试验,测试了两种试验条件的界面摩擦特性。在两种试验条件下,土工格栅加筋土复合体的抗剪强度均有界面摩擦角φsq和界面凝聚力csq,且土工格栅与土相对位移量的不同,其复合体的强度机理有区别。在拉拔摩擦试验中,剪应力峰值强度对应的剪切变形值高于直剪摩擦试验中剪应力峰值强度的剪切变形值5～10倍以上。两种试验均有其适用性,而土与土工格栅的相对位移较小时直剪摩擦试验较能反映实际;土与土工格栅相对位移较大时土与格栅双面均发生相对位移,拉拔摩擦试验更为合适。随法向应力的增大,直剪摩擦和拉拔摩擦试验的剪应力峰值以及剪应力峰值对应的位移均提高。直剪摩擦的剪切速度小,剪应力峰值强度高,且达到峰值强度的剪切位移大;增加剪切速度,剪应力峰值强度降低,且对应的位移也减少,其原因是界面上的孔隙水压力消散和筋材的应力松弛。应根据具体工程的需要选择直剪摩擦试验和拉拔摩擦试验确定设计参数。     

三向土工格栅筋-土界面特性拉拔试验研究

现有关于格栅与土的筋-土界面特性研究多以单、双向格栅为研究对象,而对三向土工格栅筋-土界面特性开展的试验研究较少。以三向土工格栅为研究对象并考虑0°和90°两种拉拔方向的影响(记为TX_0工况和TX_90工况),开展了一系列室内拉拔试验,通过对三向土工格栅沿拉拔方向4个断面的位移进行量测,分析了格栅拉伸应变、筋-土相对位移、界面摩阻力分布及格栅变形与破坏模式,并分别从峰值剪切强度和残余剪切强度两个方面对筋-土界面强度参数和表观摩擦系数的变化规律进行了探讨。研究结果表明:由于平面外挠曲变形的影响,TX_0工况下横肋的嵌锁作用随法向应力增大而增强,从而使TX_0工况的拉拔性能逐渐优于TX_90工况;拉拔过程中,筋-土界面摩阻力的发挥是一个渐进的过程,其分布形式不断发生调整,筋-土界面呈弹塑性-软化特征;TX_0工况的筋-土界面摩擦角显著大于TX_90工况,黏聚力则刚好相反,法向应力较高时TX_0工况的筋-土界面强度更高,更有利于材料性能的发挥。     

土工织物与土的直剪摩擦试验研究

土工织物作为一种新型的建筑材料，因经济和技术及过滤、排水、隔离、加筋、防护作用的优势，国外自20世纪50年代后期，我国自70年代后期广泛应用于岩土工程的各个方面。土与织物界面相互作用的机理十分复杂，室内测试目前还处于探索和完善阶段。主要介绍土工织物与土的直剪摩擦试验方面的研究。     

土工袋加固膨胀土边坡降雨−日晒循环试验研究

为了解复杂气候条件下土工袋加固膨胀土边坡的效果与机制,开展袋装膨胀土边坡降雨−日晒循环试验,观察并分析边坡位移变形、坡面冲刷、降雨入渗等情况,并与素膨胀土边坡进行对比。试验结果表明：素膨胀土边坡在降雨−日晒循环作用下,边坡表面产生的裂隙较多,容易出现土体流失,土工袋则具有良好的反滤和抗冲刷作用,可以减少袋内和下卧层土体的流失,保持边坡的稳定性;土工袋对膨胀土有较好的约束作用,可以有效地抑制其膨胀变形,减小因变形引发边坡失稳的可能性;土工袋有良好的排水效果,雨水能通过土工袋袋间间隙快速地排出,边坡内含水率的增加幅度较小。     

土工格栅加筋土挡墙试验研究

采用在墙面板背后安装土压力盒以及在土工格栅上安装柔性位移计的方法,对某高速公路加筋土挡墙水平土压力和土工格栅拉筋位移进行了系统测试。试验研究表明,施工期间土工格栅加筋土挡墙墙背土压力随填土高度的增加而增大,增长速率逐渐减小,其数值均小于理论计算结果,沿墙高分布形式与计算结果有较大差别;土工格栅拉筋在施工期应变变形较大,工后应变非常小,挡墙下部土工格栅拉筋端部应变随填土高度变化较大,在加筋体锚固区末端存在过渡区,其工程特性逐渐向非加筋体填土过渡。根据试验结果对土工格栅加筋土挡墙施工控制及关键技术提出了相关建议。     

土工带加筋碎石土本构关系的三轴试验研究

通过碎石土和加筋碎石土的大型三轴试验,分析了土工带加筋碎石土的变形特性和土工带加筋对碎石土应力-应变关系的影响,采用双曲线函数拟合加筋土体的应力-应变试验曲线,建立了土工带加筋碎石土的非线性模型以克服经典的刚塑体模型不能反映加筋土体在达到破坏荷载前的变形形态的缺点,提出了土工带加筋土体切线模量的计算公式,该模型能正确反映土工带加筋土体的变形特性,在岩土工程方面有一定的实际应用价值.     

填充性岩溶软基加固方案的模糊综合评价与工程应用

运用模糊综合评判法与离散抽样模型,对渝-怀铁路干溪沟隧道Dk278+628至+678段隧底填充性岩溶软基处理方案进行了评价和选择,从而使所选择的处理方案达到整体最优,该评价方法可为今后类似的工程处理提供借鉴。     

纳米硅粉水泥土的强度特性及固化机理研究

将性能优异的纳米硅粉作为外掺剂应用于水泥土改性研究。通过室内试验，探讨了纳米硅粉水泥土的强度特性。试验表明，一定掺量下的纳米硅粉能够显著提高水泥土的各个龄期强度。结合试验测试和理论分析，探讨了纳米硅粉在水泥水化硬化过程中的作用以及纳米硅粉与土之间的作用，在此基础上，分析了纳米硅粉改性水泥土工程性状的机理，旨在为纳米硅粉应用于工程实践开展理论和试验研究探索。     

Block reinforcement behavior and mechanism of soil slopes

In recent years, blocks created by pressure grouting of cement into soil were used to reinforce slopes by targeting specific weak areas. A clear understanding of the block reinforcement mechanism is essential for the accurate evaluation of the stability of block-reinforced slopes and reasonable design of block layouts. A series of centrifuge model tests was conducted to investigate the bearing capacity and the full deformation and failure behavior of block-reinforced slopes, with a focus on the influence of block layouts on the reinforcement effect. A block reinforcement with a reasonable layout was confirmed to increase the stiffness and the ultimate bearing capacity of the slope. The block reinforcement significantly changed the failure mode to the complex disturbance and destruction from slippage failure in an unreinforced slope. The block reinforcement restrained the deformation localization around the blocks and thus prevented the development of the coupling effect between the deformation localization process and the failure process in an unreinforced slope during loading. Such a reinforcement mechanism could be used to explain why the block reinforcement increased the bearing capacity and changed the failure mode of the slope. The blocks exhibited significant motion along with the development of deformation localization in the slope during loading. The block reinforcement effect was significantly affected by the rotation of blocks, which was determined by the block layout.     

预应力土层锚杆与土钉墙联合支护的力学工作机理研究

主要论述一种新型基坑支护形式－－预应力土层锚杆与土钉墙联合支护技术在某工程中的设计，施工，监测等，并通过监测资料的分析，探求该种支护形式的力学工作机理。     

湖相软土流变模型识别及其工程应用分析

对苏州湖相软土进行了三轴流变试验,根据试验结果拟采用S-6、K-B、K-S 3个流变模型来描述土体的流变特征,在模型参数反演中发现,S-6模型对加载初期变形的拟合精度不够,K-B模型对加载中期变形的拟合精度不够,而K-S模型能够很好地描述苏州湖相软土的流变特征。在模型的实际应用中引入应力比的概念,发现应力比与模型参数成指数关系,以此可以根据不同的工程应力条件来选择模型参数,最后,将该模型用于实际工程的沉降计算,通过与实测数据的对比显示模型的拟合精度较高,可以用于指导该地区的工程建设。     

工程开挖活动诱发堆积层滑坡变形机理及加固效果分析

位于川西高原雅砻江两河口水电站库区的杜米村移民安置点由于切坡建房,诱发后山斜坡强烈变形,威胁移民安置点和S220省道安全。首先,基于现场调查、测绘、钻探、槽探等勘查手段,查明了滑坡发育的工程地质条件和变形特征;通过对滑体和滑带土开展室内直剪、反复剪试验,以及对滑床基岩进行抗压强度试验,结合反分析,合理确定了滑坡稳定性计算参数。然后,采用有限元程序Phase2建立滑坡数值计算模型,模拟再现了滑坡在开挖前、开挖后、降雨后的应力、变形特征和稳定性变化过程,在此基础上分析了滑坡的变形机理。研究认为：不良的地形地貌、地质结构和地下水是滑坡发生的内在因素,坡脚开挖是滑坡变形启动的诱发因素,后期持续降雨入渗是滑坡变形加剧直至失稳破坏的直接因素;开挖导致滑体前缘抗滑力降低、滑带和开挖边坡坡脚产生剪应力集中是滑坡变形启动的力学机制,而饱水和持续剪切变形导致滑带土强度不断衰减接近饱和残余状态是滑坡变形加剧的本质原因;滑坡的变形破坏模式为牵引式蠕滑-拉裂。最后,采用有限元强度折减法对加固治理后的滑坡稳定性进行了计算分析。结果表明：天然条件下滑坡变形主要出现在桩后填土,降雨条件下变形范围扩大至强变形区,地震条件下变形范围进一步扩大至整个滑坡范围;三种工况下滑坡的稳定系数均能达到设计要求,表明加固设计方案和工程结构参数是合理的。研究成果可为类似滑坡工程案例的机理研究及防治提供参考。     

低应变动测法在水泥土桩工程质量检测中的应用初探

本文对水泥土桩强度的影响因素和低应变动测与水泥土桩强度特性的关系进行了分析，结合工程实践探讨了低应变动测法在水泥土桩质量检测中的适用性。     

小净距隧道中夹岩对拉锚杆控制机制与工程应用

小净距隧道中夹岩受到两侧开挖的剧烈扰动,处于单向或双向受力的不利状态,严重影响施工安全,而预应力全长注浆对拉锚杆常用于中夹岩的主动支护。为阐明对拉锚杆的作用模式和控制机制,建立相应的力学模型和解析方法,开展实测验证,并进行参数分析和工程应用。研究表明：对拉锚杆为中夹岩提供强力水平约束,并提高岩体力学性能,发挥挤压加固作用;对拉锚杆利用剪切摩阻改善浅层围岩受力状态,同时锚固深部岩体,具有承载传力效果;对拉锚杆轴力和剪应力均由两侧向中间非线性衰减,作用范围局限于浅层中夹岩,实测结果验证了理论方法的合理性;进行了对拉锚杆的参数分析,提出了对拉锚杆临界长度、合理锚杆直径等工程建议;结合京张高铁长城站小净距隧道实践,主动增强对拉锚杆设计参数,变更后围岩压力、拱顶沉降和水平收敛的实测均值分别降低12.2%、14.1%和10.2%,保障了隧道开挖的安全。     

砂土介质注浆渗透扩散试验与加固机制研究

设计了一套可视化砂土介质恒压注浆渗透扩散与加固模拟试验装置。选用普通硅酸盐42.5水泥（OPC）、超细硅酸盐水泥（MC）、超细硫铝水泥（MSAC）及自主研发材料（EMCG）,对砂土多孔介质进行了注浆渗透扩散与加固试验。研究了细砂土体不同浆液、注浆压力工况下扩散距离、注浆量随时间变化规律,以及不同浆液、砂样级配及注浆压力对加固效果影响。采用极差分析法确定了加固效果主控因素,获得了加固体宏观破坏模式,通过SEM分析了岩-浆界面微观加固模型,揭示了不同材料加固效果差异的本质原因。研究结果表明：注浆材料与颗粒质量分数主导着细砂土体可注性,注浆压力对可注性提高程度不大,EMCG可注性最强,MC、MSAC次之,OPC最差;在完全可注情况下,砂样级配越细,加固体强度改善效果越明显;EMCG材料加固体7、28 d强度明显高于MSAC、MC、OPC加固体;EMCG的7 d加固体强度达到28 d参数70%以上;注浆材料主导着注浆加固效果,EMCG对不同级配砂土体注浆加固效果显著优于其他水泥类材料,OPC最差;注浆后EMCG浆-岩界面生成的致密C-S-H凝胶体能够有效提高胶结强度。最后从注浆材料选型、注浆过程控制、钻孔布置方面对砂土层渗透注浆设计方法提出了工程治理改进建议。     

超微粒子水泥加固软土试验研究

应用和研发各种固化材料,对软土进行固化和改性,以改善其工程特性是当今国际上研究的热点课题。通过室内试验,研究了一种新型超微粒子水泥材料（ALOFIX-MC,简称MC）加固软土的效果,分析了其加固和改性机制。试验中,MC以0 %、1 %、2 %、3 %、4 %和5 %的掺量分别掺入到水泥掺量15 %和石膏掺量2 %的软土试样中,配制了6组试样。室内无侧限抗压强度试验结果表明,在15 %掺量的普通水泥土中掺入少量MC就可以显著提高软土的强度和稳定性。扫描电镜（SEM）分析表明,MC的胶结填充作用和MC对水泥水化的促进、孔隙的填充以及其本身的表面吸水作用对加固效果有重要影响。研究成果为进一步提高水泥土的工程性质和减少常规水泥土中水泥掺量提供了一条新的途径。