Tantalum-bearing titanite: synthesis and crystal structure data

Synthetic titanite, CaTiOSiO₄, and the series of (Ca_1−x Na _x )(Ti_1−x Ta _x )OSiO₄ and Ca(Ti_1−2x Ta _x Al _x )OSiO₄ solid solutions have been prepared by ceramic methods, and their crystal structure determined by the Rietveld analysis. At ambient conditions, titanite can contain up to 20 mol% NaTaOSiO₄ or 60 mol% Ca(Al_0.5Ta_0.5)OSiO₄. These limits might differ in natural samples due to combination with substitutions involving fluorine and/or hydroxyl replacing oxygen together with vacancies at cationic sites. All cations located at the ^vii X- and ^vi Y-sites in the structures of tantalian titanite are disordered. Expansion of the <Si–O> bond from 1.618 to 1.621 Å in CaTi_0.8Ta_0.1Al_0.1OSiO₄ and CaTi_0.6Ta_0.2Al_0.2OSiO₄ to 1.644 Å in the CaTi_0.4Ta_0.3Al_0.3OSiO₄ titanite suggests the possible presence of some Al³⁺ in the tetrahedral site replacing Si⁴⁺ in the latter. All tantalian titanites crystallize in the space group A2/a. This implies that both single-site and complex double-site substitutional schemes induce P2₁/a → A2/a phase transition(s). The (Ca_1−x Na _x )(Ti_1−x Ta _x )OSiO₄ substitution scheme incorporates larger cations at both the ^vii X and ^vi Y sites, whereas the Ca(Ti_1−2x Ta _x Al _x )OSiO₄ scheme involves only ^vi Y-site (Al³⁺,Ta⁵⁺) cations with a slightly smaller “average” radius. Unit cell dimensions change insignificantly or increase incrementally with increase of average cationic radii in the (Ca_1−x Na _x )(Ti_1−x Ta _x )OSiO₄ series, and with an insignificant decrease in the ^viR _Y average cationic radii in the Ca(Ti_1−2x Ta _x Al _x )OSiO₄ series. Both Ta-doped titanite and CaTiOSiO₄ consist of distorted polyhedra with the XO₇, YO₆ coordination polyhedra and the SiO₄ tetrahedron in tantalian titanite being less distorted compared to those of the pure CaTiOSiO₄.