系列富硅铝矿石水热晶化法合成纳米莫来石复相粉体的研究

分别以粉煤灰、煤矸石、红柱石千枚岩、油页岩渣等富硅铝矿石为原料,经过除杂、煅烧活化后,利用水热晶化法制备出纳米莫来石复相粉体。采用X射线粉末衍射(XRD)、透射电子显微镜(TEM)、能量色散X射线荧光光谱分析(EDX)和选区电子衍射(SAED)等手段研究了复相粉体的物相组成与显微结构,并用魔角旋转核磁(MAS~NMR)分析水热晶化反应机理。结果表明:经过一定温度煅烧活化后,当NaOH溶液浓度为2~3 mol/L、搅拌温度80~90℃、恒温3 h、液固比为10 mL/g时,上述四种原料均可制得以莫来石为主晶相的纳米复相粉体,其中以煤矸石、红柱石千枚岩、油页岩渣为原料制备的晶体均为结晶良好的柱状晶,平均长度分别为50、300和150 nm,平均长径比分别为4、3.5和3.75;以粉煤灰为原料制备的晶体主要呈现棒状、针状和纤维状,其棒状晶长度约30~80 nm、直径约4.5~30 nm。

The preparation of mullite nanocomposites powders from silicon_aluminium_ bearing minerals through hydrothermal crystallization

Mullite nanocomposites powders were successfully synthesized from high-aluminium coal fly ash,coal gangue,andalusite-sericite phyllite and oil shale slag through the hydrothermal crystallization process after the removal of the residual carbon,deferrization or calcination.The phase constitution and microstructure of the synthesized mullite nanocomposites powders were investigated by X-ray diffraction(XRD),transmission electron microscopy(TEM),selected area electron diffraction(SAED) and energy-dispersive X-...