The oxidation state of sulfur in synthetic and natural glasses determined by X-ray absorption spectroscopy

Sulfur K-edge X-ray absorption near edge structure (XANES) spectra were recorded for experimental glasses of various compositions prepared at different oxygen fugacities (fO₂) in one-atmosphere gas-mixing experiments at 1400 °C. This sample preparation method only results in measurable S concentrations under either relatively reduced (log fO₂ < −9) or oxidised (log fO₂ > −2) conditions. The XANES spectra of the reduced samples are characterised by an absorption edge crest at 2476.4 eV, typical of S²⁻. In addition, spectra of Fe-bearing compositions exhibit a pronounced absorption edge shoulder. Spectra for all the Fe-free samples are essentially identical, as are the spectra for the Fe-bearing compositions, despite significant compositional variability within each group. The presence of a sulfide phase, such as might exsolve on cooling, can be inferred from a pre-edge feature at 2470.5 eV.The XANES spectra of the oxidised samples are characterised by an intense transition at 2482.1 eV, typical of the sulfate anion SO₄²⁻. Sulfite (SO₃²⁻) has negligible solubility in silicate melts at low pressures. The previous identification of sulfite species in natural glass samples is attributed to an artefact of the analysis (photoreduction of S⁶⁺). S⁴⁺ does, however, occur unambiguously with S⁶⁺ in Fe-free and Fe-poor compositions prepared in equilibrium with CaSO₄ at 4-16 kbar, and when buffered with Re/ReO₂ at 10 kbar. Solubility of S⁴⁺ thus requires partial pressures of SO₂ considerably in excess of 1 bar. A number of experiments were undertaken in an attempt to access intermediate fO₂s more applicable to terrestrial volcanism. Although these were largely unsuccessful, S²⁻ and S⁶⁺ were found to coexist in some samples that were not in equilibrium with the imposed fO₂.The XANES spectra of natural olivine-hosted melt inclusions and submarine glasses representative of basalts at, or close to, sulfide saturation show mainly dissolved S²⁻, but with minor sulfate, and additionally a peak at 2469.5 eV, which, although presumably due to immiscible sulfide, is 1 eV lower than that typical of FeS. These sulfate and sulfide-related peaks disappear with homogenisation of the inclusions by heating to 1200 °C followed by rapid quenching, suggesting that both these features are a result of cooling under natural conditions. The presence of small amounts of sulfate in otherwise reduced basaltic magmas may be explained by the electron exchange reaction: S²⁻ + 8Fe³⁺ = S⁶⁺ + 8Fe²⁺, which is expected to proceed strongly to the right with decreasing temperature. This reaction would explain why S²⁻ and S⁶⁺ are frequently found together despite the very limited fO₂ range over which they are thermodynamically predicted to coexist. The S XANES spectra of water-rich, highly oxidised, basaltic inclusions hosted in olivine from Etna and Stromboli confirm that nearly all S is dissolved as sulfate, explaining their relatively high S contents.