The effects of sulfur intercalation on the optical properties of artificial ‘hackmanite’, Na8[Al6Si6O24]Cl1.8S0.1; ‘sulfosodalite’, Na8[Al6Si6O24]S; and natural tugtupite, Na8[Be2Al2Si8O24](Cl,S)2?δ

The minerals ??hackmanite?? and tugtupite exhibit tenebrescence (reversible photochromism) and photoluminescence. These features are generally attributed to the presence of sulfide species within their structures. But how these optical properties might be affected by intercalating additional amounts of sulfur into their structures was until now unknown. Artificial ??hackmanite??, Na₈[Al₆Si₆O₂₄]Cl_1.8S_0.1, and ??sulfosodalite??, Na₈[Al₆Si₆O₂₄]S, were heated with sulfur in evacuated quartz-glass ampoules over the temperature range 450?C1,050°C. This work has shown that sulfur intercalation into Na₈[Al₆Si₆O₂₄]Cl_1.8S_0.1 destroys the tenebrescence and induces a permanently pale blue and, at higher temperature, a pale green coloration. The effect on Na₈[Al₆Si₆O₂₄]S induced similar colorations but of a deeper hue. Annealing tugtupite, Na₈[Be₂Al₂Si₈O₂₄](Cl,S)_2??? under a sulfur atmosphere over the range 600?C700°C, destroyed the tenebrescence and resulted in a colorless tugtupite; but did not effect the photoluminescence. This suggests that the chemical species responsible for the tenebrescence in tugtupite is unlikely to be the same as that for the luminescence.     

Correlation between electron paramagnetic resonance and thermoluminescence in natural sodalite

Samples of natural sodalite, Na₈Al₆Si₆O₂₄Cl₂, submitted to gamma irradiation and to thermal treatments, have been investigated using the thermoluminescence (TL) and electron paramagnetic resonance (EPR) techniques. Both, natural and heat-treated samples at 500°C in air for 30 min, present an EPR signal around g = 2.01132 attributed to oxygen hole centers. The EPR spectra of irradiated samples show an intense line at g = 2.0008 superimposed by a hyperfine multiplet of 11 lines due to an O⁻ ion in an intermediate position with respect to two adjacent Al nuclei. In the TL measurements, the samples were annealed at 500°C for 30 min and then irradiated with γ doses varying from 0.001 to 20 kGy. All the samples have shown TL peaks at 110, 230, 270, 365, and 445°C. A correlation between the EPR g = 2.01132 line and the 365°C TL peak was observed. A TL model is proposed in which a Na⁺ ion acts as a charge compensator when an Al³⁺ ion replaces a Si⁴⁺ lattice ion. The γ ray destruction of the Al–Na complex provides an electron trapped at the Na and a hole trapped at a non-bridging oxygen ion adjacent to the Al³⁺ ion.     

Distance least squares modelling of the cubic sodalite structure and of the thermal expansion of Na8(Al6Si6O24)I2

The Distance Least Squares (DLS) structure modelling technique is used to determine the room-temperature structures of the sodalites Li₈(Al₆Si₆O₂₄)Cl₂, Na₈(Al₆Si₆O₂₄)Cl₂, K₈(Al₆Si₆O₂₄)Cl₂, Na₈(Al₆Si₆O₂₄)Br₂, and Na₈(Al₆Si₆O₂₄)I₂. The technique is also used to calculate the thermal expansion behaviour of Na₈(Al₆Si₆O₂₄)I₂ assuming that the discontinuity in its thermal expansion curve occurred either when the ideal fully-expanded state was achieved (case 1) or when the x-coordinate of the sodium atom became 0.25 (case 2). The results are given as plots of bond lengths and bond angles as a function of temperature. Case 2 was preferred and analysis of the results implied that the driving force for the untwisting of the partially-collapsed sodalite framework was in the framework bonds with the cavity ion bonds resisting the untwisting. Best estimates indicate that the expansion of the Na-O and Na-I bonds are 9% and 27.4% respectively, between room temperature and 810° C, and there is an apparent shortening of the framework bond distances of about 1.5%.     

(Na,Ca)(Ti3+,Mg)Si2O6-clinopyroxenes at high pressure: influence of cation substitution on elastic behavior and phase transition

A compressional study of (Na,Ca)(Ti³⁺,Mg)Si₂O₆-clinopyroxenes was carried out at high pressures between 10⁻⁴ and 10.2 GPa using in situ single-crystal X-ray diffraction, Raman spectroscopy and optical absorption spectroscopy. Compressional discontinuities accompanied by structural changes, in particular, the appearance of two distinct Ti³⁺–Ti³⁺ distances within the octahedral chains at 4.37 GPa, provide evidence for the occurrence of a phase transition in NaTi³⁺Si₂O₆. Equation-of-state parameters are K ₀ = 115.9(7) GPa with K′ = −0.9(3) and K ₀ = 102.7(8) GPa with K′ = 4.08(5) for the low- and high-pressure range, respectively. The transition involves a C2/c–P [`1] \overline{1} symmetry change, which can be confirmed by the occurrence of new modes in Raman spectra. Since no significant discontinuity in the evolution of the unit-cell volume with pressure has been observed, the transition appears to be second-order in character. The influence of the coupled substitution Na⁺Ti³⁺↔Ca²⁺Mg²⁺ on the static compression behavior and the structural stability has been investigated using a sample of the intermediate composition (Na_0.54Ca_0.46)(Mg_0.46Ti_0.54)Si₂O₆. No evidence for a deviation from continuous compression behavior has been found, neither in lattice parameter nor in structural data and the fit of a third-order Birch–Murnaghan equation-of-state to the pressure–volume data yields a bulk modulus of K ₀ = 109.1(5) GPa and K′ = 5.02(13). Raman and polarized absorption spectra have been compared to NaTiSi₂O₆ and reveal major similarities. The main driving force for the phase transition in NaTi³⁺Si₂O₆ is the localization of the Ti³⁺ d-electron and the accompanying distortion, which is suppressed in the (Na,Ca)(Ti³⁺,Mg)Si₂O₆-clinopyroxene.     

Chemical composition and species attribution of tourmalines from a rare-metal pegmatite vein with scapolite, Sangilen Upland, Tuva

A detailed study of the chemical composition and substitutions in calcium tourmalines from a scapolite-bearing rare-metal pegmatite vein from the Sol’bel’der River basin has shown that their species attribution is determined by occupancy of octahedral site Y. The composition of the yellow tourmaline most abundant in the central part of the pegmatite bodyis rather constant and characterized by the ideal formula Ca(Mg₂Li)Al₆(Si₆O₁₈)(BO₃)₃(OH)₃F. Variations in the chemical composition of zonal tourmaline crystals from the contact part of the pegmatite are controlled by abrupt change in the chemical medium during their formation. The yellow cores of these crystals are close in composition to tourmaline from the central part of the pegmatite vein. The Mg content abruptly decreases toward the crystal margin: Mg²⁺ → Fe²⁺, 2Mg²⁺ → Li⁺ + Al³⁺, and Mg²⁺ + OH → Al³⁺ + O²⁻. The composition of dark green marginal zones in tourmaline is characterized by the ideal formula Ca(Al_1.5Li_1.5)Al₆(Si₆O₁₈)(BO₃)₃ (OH₂O)(F). The results indicate specific formation conditions of pegmatite. The crystallochemical formulas of the studied tourmalines allow us to regard them as new mineral species in the tourmaline group.     

Boron substitution in diopside evaluated through 11B nuclear reaction analysis

 Nuclear reaction analyses on boron in flux-grown Me³⁺- and Na⁺-doped diopside crystals utilising the ¹¹B(p,2α)⁴He reaction in conjunction with EMP analyses for major elements and optical absorption spectroscopy for determination of Me-valence state distributions show that appreciable amounts of B may enter the diopside lattice in crystals produced in Na₂B₄O₇ fluxes. The results indicate that the substitution ^[6]Me^3+[4]B^3+[6]Mg²⁺ ₋₁ ^[4]Si⁴⁺ ₋₁ operates in the present diopside samples in addition to the coupled substitution ^[6]Me^3+[8]Na^+[6]Mg²⁺ ₋₁ ^[8]Ca²⁺ ₋₁. The specific NRA technique applied allows for quantitative, high resolution (ca. 5 μm) B analyses at ppm level as well as high-resolution and high-contrast imaging of B-concentration patterns in minerals. The estimated detection limit and relative error of the B analyses are 10 ppm and 5–10%, respectively. Received: 20 September 1999 / Accepted: 6 June 2000     

Environmental research of groundwater in the urban and suburban areas of Attica region,Greece

In this study, 92 groundwater samples were collected from the Attica region (Greece). Moreover, geographical information system database, geochemistry of groundwater samples and statistics were applied. These were used for studying the chemical parameters (NO₃ ⁻, Mg²⁺, Ca²⁺, Cl⁻, and Na⁺) and conductivity spatial distribution and for assessing their environmental impact. The ranges of chemical parameters of the water samples (in mg L⁻¹) are: NO₃ ⁻ 1–306, Mg²⁺ 2–293, Ca²⁺ 3–453, Cl⁻ 5–1,988, and Na⁺ 4–475. The elevated concentrations of sodium, Mg²⁺, Cl⁻ are attributed to natural contamination (seawater intrusion). On the other hand, NO₃ ⁻ elevated concentrations are attributed to anthropogenic contamination (nitrate fertilizers). The results of the GIS analysis showed that elevated values of Na⁺, Mg²⁺, Cl⁻ are related to shrubby and sparsely vegetated areas, while elevated values of NO₃ ⁻ are connected with urban and agricultural areas.     

A study of phase transformation in hedenbergite to 40 GPa at ∼1200° C

Phase transformations in a natural sample of hedenbergite ((Ca_0.93Fe_0.61Mn_0.34Mg_0.08Na_0.01Zn_0.02Al_0.003)Si₂O₆) have been studied by X-ray diffraction up to 40 GPa at ∼ 1200°C in a diamond anvil cell interfaced with a laser heating system. The starting hedenbergite phase decomposed into a garnet plus γ-spinel and stishovite at ∼ 14 GPa; then into garnet plus stishovite and wüstite at ∼ 18 GPa; and finally into perovskite plus stishovite and wüstite at pressures higher than ∼ 24 GPa. On decompression to 0.1 MPa, all the high pressure phases are retained except for the cubic perovskite, which reverts back into the ɛ-CaSiO₃ phase, in accordance with previous reports. Energy-dispersive SEM analyses show that the garnet is present as a calcium-rich ABO ₃-type phase. As no garnet phase has been previously observed either in pure CaSiO₃ or in pure CaMgSi₂O₆, it appears that the observed calcium-rich garnet phase has been stabilized by the presence of other cations such as the Na⁺, Zn²⁺, Mn²⁺, Fe²⁺, Mn³⁺, Fe³⁺ and Al³⁺.     

On the mechanisms for H and Al incorporation in stishovite

The solubility and incorporation mechanisms of hydrogen in synthetic stishovite as a function of Al₂O₃ content have been investigated. Mechanisms for H incorporation in stishovite are more complex than previously thought. Most H in stishovite is incorporated via the Smyth et al. (Am Mineral 80:454–456, 1995) model, where H docks close to one of the shared O–O edges, giving rise to an OH stretching band in infrared (IR) spectra at 3,111–3,117 cm⁻¹. However, careful examination of IR spectra from Al-stishovite reveals the presence of an additional OH band at 3,157–3,170 cm⁻¹. All H is present on one site, with interstitial H both coupled to Al³⁺ substitutional defects on adjacent octahedral (Si⁴⁺) sites, and decoupled from other defects, giving rise to two distinct absorption bands. Trends in IR data as a function of composition are consistent with a change in Al incorporation mechanism in stishovite, with Al³⁺ substitution for Si⁴⁺ charge-balanced by oxygen vacancies at low bulk Al₂O₃ contents, and coupled substitution of Al³⁺ onto octahedral (Si⁴⁺) and interstitial sites at high bulk Al₂O₃ contents. Trends in OH stretching frequencies as a function of Al₂O₃ content suggest that any such change in Al incorporation mechanism could alter the effect that Al incorporation has on the compressibility of stishovite, as noted by Ono et al. (Am Mineral 87:1486–1489, 2002).     

Kyanoxalite,a new cancrinite-group mineral species with extraframework oxalate anion from the Lovozero alkaline pluton,Kola Peninsula

Kyanoxalite, a new member of the cancrinite group, has been identified in hydrothermally altered hyperalkaline rocks and pegmatites of the Lovozero alkaline pluton, Kola Peninsula, Russia. It was found at Mount Karnasurt (holotype) in association with nepheline, aegirine, sodalite, nosean, albite, lomonosovite, murmanite, fluorapatite, loparite, and natrolite and at Mt. Alluaiv. Kyanoxalite is transparent, ranging in color from bright light blue, greenish light blue and grayish light blue to colorless. The new mineral is brittle, with a perfect cleavage parallel to (100). Mohs hardness is 5–5.5. The measured and calculated densitiesare 2.30(1) and 2.327 g/cm³, respectively. Kyanoxalite is uniaxial, negative, ω = 1.794(1), ɛ = 1.491(1). It is pleochroic from colorless along E to light blue along O. The IR spectrum indicates the presence of oxalate anions C₂O₄²⁻ and water molecules in the absence of CO₃²⁻ Oxalate ions are confirmed by anion chromatography. The chemical composition (electron microprobe; water was determined by a modified Penfield method and carbon was determined by selective sorption from annealing products) is as follows, wt %: 19.70 Na₂O, 1.92 K₂O, 0.17 CaO, 27.41 Al₂O₃, 38.68 SiO₂, 0.64 P₂O₅, 1.05 SO₃, 3.23 C₂O₃, 8.42 H₂O; the total is 101.18. The empirical formula (Z = 1) is (Na_6.45K_0.41Ca_0.03)_Σ6.89(Si_6.53Al_5.46O₂₄)[(C₂O₄)_0.455(SO₄)_0.13(PO₄)_0.09(OH)_0.01]_Σ0.68 · 4.74H₂O. The idealized formula is Na₇(Al₅₋₆Si₆₋₇O₂₄)(C₂O₄)_0.5−1 · 5H₂O. Kyanoxalite is hexagonal, the space group is P6₃, a = 12.744(8), c = 5.213(6) -ray powder diffraction pattern are as follows, [d, [A] (I, %)(hkl)]: 6.39(44) (110), 4.73 (92) (101), 3.679 (72) (300), 3.264 (100) (211, 121), 2.760 (29) (400), 2.618 (36) (002), 2.216, (29) (302, 330). According to the X-ray single crystal study (R = 0.033), two independent C₂O₄ groups statistically occupy the sites on the axis 6₃. The new mineral is the first natural silicate with an additional organic anion and is the most hydrated member of the cancrinite group. Its name reflects the color (κɛανgoΣς is light blue in Greek) and the species-forming role of oxalate anions. The holotype is deposited at the Fersman Mineralogical Museum of the Russian Academy of Sciences, Moscow, registration no. 3735/1.     

Compositional limits and analogs of monoclinic triple-chain silicates

Growing recognition of triple-chain silicates in nature has prompted experimental research into the conditions under which they can form and the extent of solid solution that is feasible for some key chemical substitutions. Experiments were done primarily in the range of 0.1–0.5 GPa and 200–850 °C for durations of 18–1,034 h. A wide range of bulk compositions were explored in this study that can be classified broadly into two groups: those that are Na free and involve various possible chemical substitutions into jimthompsonite (Mg₁₀Si₁₂O₃₂(OH)₄), and those that are Na bearing and involve chemical substitutions into the ideal end-member Na₄Mg₈Si₁₂O₃₂(OH)₄. Numerous attempts to synthesize jimthompsonite or clinojimthompsonite were unsuccessful despite the type of starting material used (reagent oxides, magnesite + SiO₂, talc + enstatite, or anthophyllite). Similarly, the chemical substitutions of F⁻ for OH⁻, Mn²⁺, Ca²⁺, or Fe²⁺ for Mg²⁺, and 2Li⁺ for Mg²⁺ and a vacancy were unsuccessful at nucleating triple-chain silicates. Conversely, nearly pure yields of monoclinic triple-chain silicate could be made at temperatures of 440–630 °C and 0.2 GPa from the composition Na₄Mg₈Si₁₂O₃₂(OH)₄, as found in previous studies, though its composition is most likely depleted in Na as evidenced by electron microprobe and FTIR analysis. Pure yields of triple-chain silicate were also obtained for the F-analog composition Na₄Mg₈Si₁₂O₃₂F₄ at 550–750 °C and 0.2–0.5 GPa if a flux consisting of Na-halide salt and water in a 2:1 ratio by weight was used. In addition, limited chemical substitution could be documented for the substitutions of 2 Na⁺ for Na⁺ + H⁺ and of Mg²⁺ + vacancy for 2Na⁺. For the former, the Na content appears to be limited to 2.5 cations giving the ideal composition of Na_2.5Mg₈Si₁₂O_30.5(OH)_5.5, while for the latter substitution the Na content may go as low as 1.1 cations giving the composition Na_1.1Mg_9.4Si₁₂O_31.9(OH)_4.1 based on a fixed number of Si cations. Further investigation involving Mg for Na cation exchange may provide a pathway for the synthesis of Na-free clinojimthompsonite. Fairly extensive solid solution was also observed for triple-chain silicates made along the compositional join Na₄Mg₈Si₁₂O₃₂(OH)₄–Ca₂Mg₈Si₁₂O₃₂(OH)₄ where the limit of Ca substitution at 450 °C and 0.2 GPa corresponds to Na_0.7Ca_1.8Mg_7.8Si₁₂O_31.9(OH)_4.1 (with the OH content adjusted to achieve charge balance). Aside from the Na content, this composition is similar to that observed as wide-chain lamellae in host actinolite. The relative ease with which Na-rich triple chains can be made experimentally suggests that these phases might exist in nature; this study provides additional insights into the range of compositions and formation conditions at which they might occur.     

Biachellaite, (Na,Ca,K)8(Si6Al6O24)(SO4)2(OH)0.5 · H2O, a new mineral species of the cancrinite group

Biachellaite, a new mineral species of the cancrinite group, has been found in a volcanic ejecta in the Biachella Valley, Sacrofano Caldera, Latium region, Italy, as colorless isometric hexagonal bipyramidal-pinacoidal crystals up to 1 cm in size overgrowing the walls of cavities in a rock sample composed of sanidine, diopside, andradite, leucite and hauyne. The mineral is brittle, with perfect cleavage parallel to {10$ \bar 1 $ \bar 1 0} and imperfect cleavage or parting (?) parallel to {0001}. The Mohs hardness is 5. D_meas = 2.51(1) g/cm³ (by equilibration with heavy liquids). The densities calculated from single-crystal X-ray data and from X-ray powder data are 2.515 g/cm³ and 2.520 g/cm³, respectively. The IR spectrum demonstrates the presence of SO₄²⁻, H₂O, and absence of CO₃²⁻. Biachellaite is uniaxial, positive, ω = 1.512(1), ɛ = 1.514(1). The weight loss on ignition (vacuum, 800°C, 1 h) is 1.6(1)%. The chemical composition determined by electron microprobe is as follows, wt %: 10.06 Na₂O, 5.85 K₂O, 12.13 CaO, 26.17 Al₂O₃, 31.46 SiO₂, 12.71 SO₃, 0.45 Cl, 1.6 H₂O (by TG data), −0.10 −O=Cl₂, total is 100.33. The empirical formula (Z = 15) is (Na_3.76Ca_2.50K_1.44)_Σ7.70(Si_6.06Al_5.94O₂₄)(SO₄)_1.84Cl_0.15(OH)_0.43 · 0.81H₂O. The simplified formula is as follows: (Na,Ca,K)₈(Si₆Al₆O₂₄)(SO₄)₂(OH)_0.5 · H₂O. Biachellaite is trigonal, space group P3, a =12.913(1), c = 79.605(5) ?; V = 11495(1) ?³. The crystal structure of biachellaite is characterized by the 30-layer stacking sequence (ABCABCACACBACBACBCACBACBACBABC)_∞. The tetrahedral framework contains three types of channels composed of cages of four varieties: cancrinite, sodalite, bystrite (losod) and liottite. The strongest lines of the X-ray powder diffraction pattern [d, ? (I, %) (hkl)] are as follows: 11.07 (19) (100, 101), 6.45 (18) (110, 111), 3.720 (100) (2.1.10, 300, 301, 2.0.16, 302), 3.576 (18) (1.0.21, 2.0.17, 306), 3.300 (47) (1.0.23, 2.1.15), 3.220 (16) (2.1.16, 222). The type material of biachellaite has been deposited at the Fersman Mineralogical Museum of the Russian Academy of Sciences, Moscow, Russia, registration number 3642/1.     

Correlative and comparative characterization of main ion concentrations in laterite groundwater in semi-arid northern Burkina Faso

About 24 samples from hand-dug wells and boreholes were used to characterize concentrations of the main inorganic ions in a laterite environment under semi-arid climatic conditions in Tikaré, northern Burkina Faso. It was found that the most represented groundwater anion in groundwater was HCO₃ ⁻ with average levels of 49.1 mg/L in the dry season and 33.5 mg/L in the rainy season. The most represented cation was Ca²⁺ with mean concentrations of 13.7 and 9.5 mg/L, respectively. The main processes, which influence the concentrations of these ions, are evaporation (dry season), local enrichment of recharge water in some elements, ion exchange and fixation by clay minerals (in case of K⁺). The best correlations were found between Ca²⁺ and Mg²⁺ (r = 0.95), Cl⁻ and Na⁺ (r = 0.95), HCO₃ ⁻ and Mg²⁺ (r = 0.89), HCO₃ ⁻ and Ca²⁺ (r = 0.89), and between HCO₃ ⁻ and Na⁺ (r = 0.80). In general, the quality of the groundwater from the different wells sampled for this study was good enough to serve as drinking water. However, there were situations where the quality of water was polluted because of anthropogenic contaminants (mainly NO₃ ⁻, K⁺, Cl⁻) from septic tanks and manure pits located in the vicinity of some sampled wells. In addition, application of fertilizers also represents a potential anthropogenic contamination source with regard to SO₄ ²⁻, Ca²⁺, K⁺, Na⁺, and Mg²⁺. Considering the high concentrations of SO₄ ²⁻, Mg²⁺, Na⁺ and Ca²⁺ found in one borehole, the deeper, fractured aquifers were also likely to be enriched in these elements. In contrast, the shallow aquifers are likely to be contaminated with Cl⁻, NO₃ ⁻ and K⁺. Cl⁻ and K⁺ seem to be locally present in recharge water as shown by their relative higher mean concentrations in the rainy season samples.     

Geochemistry characterization of groundwater in an agricultural area of Razan,Hamadan, Iran

This study was conducted to evaluate factors regulating groundwater quality in an area with agriculture as main use. Thirty groundwater samples have been collected from Razan area (Hamadan, Iran) for hydrochemical investigations to understand the sources of dissolved ions and assess the chemical quality of the groundwater. The chemical compositions of the groundwater are dominated by Na⁺, Ca²⁺, HCO₃ ⁻, Cl⁻ and SO₄ ²⁻, which have been derived largely from natural chemical weathering of carbonate, gypsum and anthropogenic activities of fertilizer’s source. The production of SO₄ ²⁻ has multiple origins, mainly from dissolution of sulphate minerals, oxidation of sulphide minerals and anthropogenic sources. The major anthropogenic components in the groundwater include Na⁺, Cl⁻, SO₄ ²⁻ and NO₃ ⁻, with Cl⁻ and NO₃ ⁻ being the main contributors to groundwater pollution in Razan area.     

A computer model for the cubic sodalite structure

A computer model for cubic sodalite structures, general formula M ₈(T ₁₂O₂₄)X ₂ where M, X and T are the cavity cation and anion and framework cation respectively, has been devised. It has been used to determine the effect of changing cavity cation and anion radii on the cell edge, tilt angle of the tetrahedra and T-O-T angle for the following sodalite frameworks: (Al₆Si₆O₂₄)^6?, (Be₆Si₆O₂₄)^12?, (Al₁₂O₂₄)^12?, and (B₁₂O₂₄)^12?. After fixing the T-O distance(s), the cavity cation-framework oxygen distance and taking a value of 1.4 Å for the radius of oxygen the model was used to calculate atomic coordinates and interatomic distances and angles for selected aluminosilicate-sodalites. The structure calculated for Na₈(Al₆Si₆O₂₄)Cl₂ agrees closely with that determined for natural sodalite (Löns and Schulz, 1967). The model is also applied to the estimation of the effective radii of the tetrahedrally-coordinated cavity anions which can be accommodated in natural and synthetic sodalites: OH^? 1.48–1.51, Cl^? 1.78, Br^? 1.93, I^? 2.14–2.17, SO ₄ ^2? 2.37–2.57, MoO ₄ ^2? 2.70 and WO ₄ ^2? 2.79 Å.     

Heat capacity and phase equilibria of hollandite polymorph of KAlSi3O8

The low-temperature heat capacity (C _p ) of KAlSi₃O₈ with a hollandite structure was measured over the range of 5–303 K with a physical properties measurement system. The standard entropy of KAlSi₃O₈ hollandite is 166.2±0.2 J mol⁻¹ K⁻¹, including an 18.7 J mol⁻¹ K⁻¹ contribution from the configurational entropy due to disorder of Al and Si in the octahedral sites. The entropy of K₂Si₄O₉ with a wadeite structure (Si-wadeite) was also estimated to facilitate calculation of phase equilibria in the system K₂O–Al₂O₃–SiO₂. The calculated phase equilibria obtained using Perple_x are in general agreement with experimental studies. Calculated phase relations in the system K₂O–Al₂O₃–SiO₂ confirm a substantial stability field for kyanite–stishovite/coesite–Si-wadeite intervening between KAlSi₃O₈ hollandite and sanidine. The upper stability of kyanite is bounded by the reaction kyanite (Al₂SiO₅) = corundum (Al₂O₃) + stishovite (SiO₂), which is located at 13–14 GPa for 1,100–1,400 K. The entropy and enthalpy of formation for K-cymrite (KAlSi₃O₈·H₂O) were modified to better fit global best-fit compilations of thermodynamic data and experimental studies. Thermodynamic calculations were undertaken on the reaction of K-cymrite to KAlSi₃O₈ hollandite + H₂O, which is located at 8.3–10.0 GPa for the temperature range 800–1,600 K, well inside the stability field of stishovite. The reaction of muscovite to KAlSi₃O₈ hollandite + corundum + H₂O is placed at 10.0–10.6 GPa for the temperature range 900–1,500 K, in reasonable agreement with some but not all experiments on this reaction.     

The threshold value of epikarst runoff in forest karst mountain area

Hydrochemical investigations were carried out in Damagh area, Hamadan, western Iran, to assess chemical composition of groundwater. Forty representative groundwater samples were collected from different wells to monitor the water chemistry of various ions. Chemical analysis of the groundwater showed that the mean concentration of the cations is in the order Na⁺ > Ca²⁺ > Mg²⁺ > K⁺, while that for anions was HCO₃⁻ > Cl⁻ > SO₄^{2 −} > NO₃⁻. All of the investigated groundwaters present two different chemical facies (Ca–HCO₃ and Na–HCO₃) which is in relation with their interaction with the geological formations of the basin, cation exchange between groundwater and clay minerals and anthropogenic activities. The principal component analysis (PCA) performed on groundwater identified three principal components controlling their variability in groundwater. Electrical conductivity, Mg²⁺, Na⁺, SO₄²⁻, and Cl⁻ content were associated in the same component (PC1) (salinity), determined principally by anthropogenic activities. The pH, CO₃^{2 −}, HCO₃⁻, and Ca²⁺ (PC2) content were related to the geogenic factor. Finally, the NO₃⁻, Cl⁻ and K⁺ (PC3) were controlled by anthropogenic activity as a consequence of inorganic fertilizers.     

Fivegite K4Ca2[AlSi7O17(O2 ? xOHx)][(H2O)2 ? xOH]Cl: A new mineral species from the Khibiny alkaline pluton of the Kola Peninsula in Russia

A new mineral fivegite has been identified in a high-potassium hyperalkaline pegmatite at Mt. Rasvumchorr in the Khibiny alkaline complex of the Kola Peninsula in Russia. This mineral is a product of the hydrothermal alteration of delhayelite (homoaxial pseudomorphs after its crystals up to 2 × 3 × 10 cm in size). Hydrodelhayelite, pectolite, and kalborsite are products of fivegite alteration. The associated minerals are aegirine, potassic feldspar, nepheline, sodalite, magnesiumastrophyllite, lamprophyllite, lomonosovite, shcherbakovite, natisite, lovozerite, tisinalite, ershovite, megacyclite, shlykovite, cryptophyllite, etc. Areas of pure unaltered fivegite are up to 2 mm in width. The mineral is transparent and colorless; its luster is vitreous to pearly. Its Cleavage is perfect (100) and distinct (010). Its Mohs hardness is 4, D(meas) = 2.42(2), and D(calc) = 2.449 g/cm³. Fivegite is optically biaxial positive: α 1.540(1), β 1.542(2), γ 1.544(2), and 2V(meas) 60(10)°. Its orientation is X = a, y = c, and Z = b. Its IR spectrum is given. Its chemical composition (wt %; electron microprobe, H₂O determined by selective sorption) is as follows: 1.44 Na₂O, 19.56 K₂O, 14.01 CaO, 0.13 SrO, 0.03 MnO, 0.14 Fe₂O₃, 6.12 Al₂O₃, 50.68 SiO₂, 0.15 SO₃, 0.14 F, 3.52 Cl, 4.59 H₂O; −O = −0.85(Cl,F)2; total 99.66. The empirical formula based on (Si + Al + Fe) = 8 is H_4.22K_3.44Na_0.39Ca_2.07Sr_0.01Fe_0.01Al_1.00Si_6.99O_21.15F_0.06Cl_0.82(SO₄)_0.02. The simplified formula is K₄Ca₂[AlSi₇O₁₇(O_{2 − x} OH _x ][(H₂O)_{2 − x} OH _x ]Cl (X = 0−2). Fivegite is orthorhombic: Pm2₁ n, a = 24.335(2), b = 7.0375(5), c = 6.5400(6) ?, V = 1120.0(2) ?³, and Z = 2. The strongest reflections of the X-ray powder pattern are as follows (d, ?, (I, %), [hkl]): 3.517(38) [020], 3.239(28) [102], 3.072(100) [121, 701], 3.040(46) [420, 800, 302], 2.943 (47) [112], 2.983(53) [121], 2.880 (24) [212, 402], 1.759(30) [040, 12.2.0]. The crystal structure was studied using a single crystal: R _hkl = 0.0585. The base of fivegite structure is delhayelite-like two-layer terahedral blocks [(Al,Si)₄Si₁₂O₃₄(O_{4 − x} OH _x )] linked by Ca octahedral chains. K⁺ and Cl⁻ are localized in zeolite-like channels within the terahedral blocks, whereas H₂O and OH occur between the blocks. The mineral is named in memory of the Russian geological and mining engineer Mikhail Pavlovich Fiveg (1899–1986), the pioneering explorer of the Khibiny apatite deposits. The type specimen is deposited at the Fersman Mineralogical Museum of the Russian Academy of Sciences in Moscow. The series of transformations is discussed: delhayelite K₄Na₂Ca₂[AlSi₇O₁₉]F₂Cl—fivegite K₄Ca₂[AlSi₇O₁₇(O_{2 − x} OH _x ]Cl—hydrodelhayelite KCa₂[AlSi₇O₁₇(OH)₂](H₂O)_{6 − x} .     

Optical spectroscopic study of synthetic NaScSi<Subscript>2</Subscript>O<Subscript>6</Subscript>–CaNiSi<Subscript>2</Subscript>O<Subscript>6</Subscript> pyroxenes at normal and high pressures

Six synthetic NaScSi₂O₆–CaNiSi₂O₆ pyroxenes were studied by optical absorption spectroscopy. Five of them of intermediate (Na_1−x , Ca _x )(Sc_1−x , Ni _x )Si₂O₆ compositions show spectra typical of Ni²⁺ in octahedral coordination, more precise Ni²⁺ at the M1 site of the pyroxene structure. The common feature of all spectra is three broad absorption bands with maxima around 8,000, 13,000 and 24,000 cm⁻¹ assigned to ³ A _2g → ³ T _2g, ³ A _2g → ³ T _1g and →³ T _1g (³ P) electronic spin-allowed transitions of ^VINi²⁺. A weak narrow peak at ∼14,400 cm⁻¹ is assigned to the spin-forbidden ³ A _2g → ¹ T _2g (¹ D) transition of Ni²⁺. Under pressure the spin-allowed bands shift to higher energies and change in intensity. The octahedral compression modulus, calculated from the shift of the ³ A _2g → ³ T _2g band in the (Na_0.7Ca_0.3)(Sc_0.7Ni_0.3)Si₂O₆ pyroxene is evaluated as 85±20 GPa. The Racah parameter B of Ni²⁺(M1) is found gradually changing from ∼919 cm⁻¹ at ambient pressure to ∼890 cm⁻¹ at 6.18 GPa. The Ni end-member pyroxene [(Ca_0.93 Ni_0.07)NiSi₂O₆] has a spectrum different from all others. In addition to the above mentioned bands of Ni²⁺(M1) it displays several new relatively intense and broad extra bands, which were attributed to electronic transitions of Ni²⁺ at the M2 site. In difference to CaO₈ polyhedron geometry of an eightfold coordination, Ni²⁺(M2)O₈ polyhedra are assumed to be relatively large distorted octahedra. Due to different distortions and different compressibilities of the M1 and M2 sites the Ni²⁺(M1)- and Ni²⁺(M2)-bands display rather different pressure-induced behaviors, becoming more resolved in the high-pressure spectra than in that measured at atmospheric pressure. The octahedral compression modulus of Ni²⁺(M1) in this end-member pyroxene is evaluated as 150 ± 25 GPa, which is noticeably larger than in Ni_0.3 pyroxene. This is due to a smaller size and, thus, a stiffer character of Ni²⁺(M1)O₆ octahedron in the (Ca_0.93Ni_0.07)NiSi₂O₆ pyroxene compared to (Na_0.7Ca_0.3)(Sc_0.7Ni_0.3)Si₂O₆.

The thermal expansion of synthetic aluminosilicate-sodalites,M 8(Al6Si6O24)X 2

Thermal expansion data, determined by powder X-ray diffraction methods are presented for 11 members of the (Li,Na,K,Rb)₈(Al₆Si₆O₂₄)Cl₂ solid solution series, 3 members of the (Na,K)₈(Al₆Si₆O₂₄)Br₂ solid solution series and Na₈(Al₆Si₆O₂₄)I₂. Only the latter showed a discontinuity in its expansion curve at 810° C wigh a mean linear expansion coefficient of 22.0×10^?6 °C^?1 below and 7.7×10^?6 °C^?1 above the discontinuity. The mean expansion coefficients from 0° to 500° C decrease gradually over the range of room temperature cell edges from 8.4 to 8.89 Å, then increase up to a cell edge of 9.01 Å above which they decrease sharply and extrapolate to a zero coefficient at 9.4 Å. These variations may be related to the expansion characteristics of the bonds between the cavity cations and cavity anions in different sodalites. The aluminosilicate-sodalites which show a discontinuity in their thermal expansion curves are those with large cavity anions, I^? or SO ₄ ^2? ; the discontinuity is believed to occur at the point when the x-coordinate of the cavity cation becomes 0.25.