Attikaite,Ca<Subscript>3</Subscript>Cu<Subscript>2</Subscript>Al<Subscript>2</Subscript>(AsO<Subscript>4</Subscript>)<Subscript>4</Subscript>(OH)<Subscript>4</Subscript> · 2H<Subscript>2</Subscript>O,a new mineral species

Attikaite, a new mineral species, has been found together with arsenocrandalite, arsenogoyazite, conichalcite, olivenite, philipsbornite, azurite, malachite, carminite, beudantite, goethite, quartz, and allophane at the Christina Mine No. 132, Kamareza, Lavrion District, Attiki Prefecture (Attika), Greece. The mineral is named after the type locality. It forms spheroidal segregations (up to 0.3 mm in diameter) consisting of thin flexible crystals up to 3 × 20 × 80 μm in size. Its color is light blue to greenish blue, with a pale blue streak. The Mohs’ hardness is 2 to 2.5. The cleavage is eminent mica-like parallel to {001}. The density is 3.2(2) g/cm³ (measured in heavy liquids) and 3.356 g/cm³ (calculated). The wave numbers of the absorption bands in the infrared spectrum of attikaite are (cm^?1; sh is shoulder; w is a weak band): 3525sh, 3425, 3180, 1642, 1120w, 1070w, 1035w, 900sh, 874, 833, 820, 690w, 645w, 600sh, 555, 486, 458, and 397. Attikaite is optically biaxial, negative, α = 1.642(2), β = γ = 1.644(2) (X = c) 2V _means = 10(8)°, and 2V _calc = 0°. The new mineral is microscopically colorless and nonpleochroic. The chemical composition (electron microprobe, average over 4 point analyses, wt %) is: 0.17 MgO, 17.48 CaO, 0.12 FeO, 16.28 CuO, 10.61 Al₂O₃, 0.89 P₂O₅, 45.45 As₂O₅, 1.39 SO₃, and H₂O (by difference) 7.61, where the total is 100.00. The empirical formula calculated on the basis of (O,OH,H₂O)₂₂ is: Ca_2.94Cu _1.93 ²⁺ Al_1.97Mg_0.04Fe _0.02 ²⁺ [(As_3.74S_0.16P_0.12)_Σ4.02O_16.08](OH)_3.87 · 2.05H₂ O. The simplified formula is Ca₃Cu₂Al₂(AsO₄)₄(OH)₄ · 2H₂O. Attikaite is orthorhombic, space group Pban, Pbam or Pba2; the unit-cell dimensions are a = 10.01(1), b = 8.199(5), c = 22.78(1) Å, V = 1870(3) ų, and Z = 4. In the result of the ignition of attikaite for 30 to 35 min at 128–140°, the H₂O bands in the IR spectrum disappear, while the OH-group band is not modified; the weight loss is 4.3%, which approximately corresponds to two H₂O molecules per formula; and parameter c decreases from 22.78 to 18.77 Å. The strongest reflections in the X-ray powder diffraction pattern [d, Å (I, %)((hkl)] are: 22.8(100)(001), 11.36(60)(002), 5.01(90)(200), 3.38(5)(123, 205), 2.780(70)(026), 2.682(30)(126), 2.503(50)(400), 2.292(20)(404). The type material of attikaite is deposited in the Fersman Mineralogical Museum, Russian Academy of Sciences, Moscow. The registration number is 3435/1.     

Middendorfite,K<Subscript>3</Subscript>Na<Subscript>2</Subscript>Mn<Subscript>5</Subscript>Si<Subscript>12</Subscript>(O,OH)<Subscript>36</Subscript> · 2H<Subscript>2</Subscript>O,a new mineral species from the Khibiny pluton,Kola Peninsula

Middendorfite, a new mineral species, has been found in a hydrothermal assemblage in Hilairite hyperperalkaline pegmatite at the Kirovsky Mine, Mount Kukisvumchorr apatite deposit, Khibiny alkaline pluton, Kola Peninsula, Russia. Microcline, sodalite, cancrisilite, aegirine, calcite, natrolite, fluorite, narsarsukite, labuntsovite-Mn, mangan-neptunite, and donnayite are associated minerals. Middendorfite occurs as rhombshaped lamellar and tabular crystals up to 0.1 × 0.2 × 0.4 mm in size, which are combined in worm-and fanlike segregations up to 1 mm in size. The color is dark to bright orange, with a yellowish streak and vitreous luster. The mineral is transparent. The cleavage (001) is perfect, micalike; the fracture is scaly; flakes are flexible but not elastic. The Mohs hardness is 3 to 3.5. Density is 2.60 g/cm³ (meas.) and 2.65 g/cm³ (calc.). Middendorfite is biaxial (?), α = 1.534, β = 1.562, and γ = 1.563; 2V (meas.) = 10°. The mineral is pleochroic strongly from yellowish to colorless on X through brown on Y and to deep brown on Z. Optical orientation: X = c. The chemical composition (electron microprobe, H₂O determined with Penfield method) is as follows (wt %): 4.55 Na₂O, 10.16 K₂O, 0.11 CaO, 0.18 MgO, 24.88 MnO, 0.68 FeO, 0.15 ZnO, 0.20 Al₂O₃, 50.87 SiO₂, 0.17 TiO₂, 0.23 F, 7.73 H₂O; ?O=F₂?0.10, total is 99.81. The empirical formula calculated on the basis of (Si,Al)₁₂(O,OH,F)₃₆ is K_3.04(Na_2.07Ca_0.03)_Σ2.10(Mn_4.95Fe_0.13Mg_0.06Ti_0.03Zn_0.03)_Σ5.20(Si_11.94Al_0.06)_Σ12O_27.57(OH)_8.26F_0.17 · 1.92H₂O. The simplified formula is K₃Na₂Mn₅Si₁₂(O,OH)₃₆ · 2H₂O. Middenforite is monoclinic, space group: P2₁/m or P2₁. The unit cell dimensions are a = 12.55, b = 5.721, c = 26.86 Å; β = 114.04°, V = 1761 ų, Z = 2. The strongest lines in the X-ray powder pattern [d, Å, (I)(hkl)] are: 12.28(100)(002), 4.31(81)(11\(\overline 4 \)), 3.555(62)(301, 212), 3.063(52)(008, 31\(\overline 6 \)), 2.840(90)(312, 021, 30\(\overline 9 \)), 2.634(88)(21\(\overline 9 \), 1.0.\(\overline 1 \)0, 12\(\overline 4 \)), 2.366(76)(22\(\overline 6 \), 3.1.\(\overline 1 \)0, 32\(\overline 3 \)), 2.109(54)(42–33, 42–44, 51\(\overline 9 \), 414), 1.669(64)(2.2.\(\overline 1 \)3, 3.2.\(\overline 1 \)3, 62\(\overline 3 \), 6.1.\(\overline 1 \)3), 1.614(56)(5.0.\(\overline 1 \)6, 137, 333, 71\(\overline 1 \)). The infrared spectrum is given. Middendorfite is a phyllosilicate related to bannisterite, parsenttensite, and the minerals of the ganophyllite and stilpnomelane groups. The new mineral is named in memory of A.F. von Middendorff (1815–1894), an outstanding scientist, who carried out the first mineralogical investigations in the Khibiny pluton. The type material of middenforite has been deposited at the Fersman Mineralogical Museum, Russian Academy of Sciences, Moscow.     

Mangazeite,Al<Subscript>2</Subscript>(SO<Subscript>4</Subscript>)(OH)<Subscript>4</Subscript> · 3H<Subscript>2</Subscript>O,a new mineral species

Mangazeite, a new mineral species, has been found at the Mangazeya silver deposit (300 km east of the Lena River, 65°43′40″ N and 130°20′ E) in eastern Yakutia (Sakha Republic, Siberia, Russia). The new mineral was described from fractured, sericitized, and pyritized granodiorite adjacent to a quartz-arsenopyrite vein. Associated minerals are gypsum and chlorite. The new mineral occurs as radial fibrous segregations of thin lamellar crystals. The size of the fibers does not exceed 40 μm in length and 1 μm across. The mineral is white, with a white streak and a vitreous luster. Mangazeite is transparent in isolated grains. No fluorescence is observed. The Mohs hardness is 1–2. The calculated density is 2.15 g/cm³. The new mineral is biaxial; its optical character was not determined; α = 1.525(9), β was not measured, and γ = 1.545(9). The average chemical composition is as follows (wt %): Al₂O₃ 36.28, SO₃ 28.81, H₂O⁺ 34.35, total 99.44, H₂O^? 9.27. The H₂O^? content was neither included in the total nor used in formula calculation. The empirical formula is Al_1.99(SO₄)_1.01(OH)_3.94 · 3.37H₂O. The simplified formula is Al₂(SO₄)(OH)₄ · 3H₂O. The theoretical chemical composition calculated from this formula is (wt %) Al₂O₃ 37.47, SO₃ 29.42, H₂O 33.11, total 100.00. The new mineral is triclinic; the unit cell parameters refined from X-ray powder diffraction data are a = 8.286(5), b = 9.385(5), c = 11.35(1) Å, α = 96.1(1), β = 98.9(1), γ = 96.6(1)°, and Z = 4. The strongest lines in the X-ray powder diffraction pattern (d(I, %)) are 8.14(19), 7.59(49), 7.16(46), 4.258(100), 4.060(48), and 3.912(43). Mangazeite is supergene in origin and crystallized in a favorable aluminosilicate environment in the presence of sulfate ion due to pyrite oxidation.     

Nickelpicromerite,K<Subscript>2</Subscript>Ni(SO<Subscript>4</Subscript>)<Subscript>2</Subscript>•6H<Subscript>2</Subscript>O,a new picromerite-group mineral from Slyudorudnik,South Urals,Russia

A new picromerite-group mineral, nickelpicromerite, K₂Ni(SO₄)₂?·?6H₂O (IMA 2012–053), was found at the Vein #169 of the Ufaley quartz deposit, near the town of Slyudorudnik, Kyshtym District, Chelyabinsk area, South Urals, Russia. It is a supergene mineral that occurs, with gypsum and goethite, in the fractures of slightly weathered actinolite-talc schist containing partially vermiculitized biotite and partially altered sulfides: pyrrhotite, pentlandite, millerite, pyrite and marcasite. Nickelpicromerite forms equant to short prismatic or tabular crystals up to 0.07 mm in size and anhedral grains up to 0.5 mm across, their clusters or crusts up to 1 mm. Nickelpicromerite is light greenish blue. Lustre is vitreous. Mohs hardness is 2–2½. Cleavage is distinct, parallel to {10–2}. D _meas is 2.20(2), D _calc is 2.22 g cm^?3. Nickelpicromerite is optically biaxial (+), α?=?1.486(2), β?=?1.489(2), γ?=?1.494(2), 2V_meas =75(10)°, 2V_calc =76°. The chemical composition (wt.%, electron-microprobe data) is: K₂O 20.93, MgO 0.38, FeO 0.07, NiO 16.76, SO₃ 37.20, H₂O (calc.) 24.66, total 100.00. The empirical formula, calculated based on 14 O, is: K_1.93Mg_0.04Ni_0.98S_2.02O_8.05(H₂O)_5.95. Nickelpicromerite is monoclinic, P2₁/c, a?=?6.1310(7), b?=?12.1863(14), c?=?9.0076(10) Å, β?=?105.045(2)°, V?=?649.9(1) ų, Z?=?2. Eight strongest reflections of the powder XRD pattern are [d,Å-I(hkl)]: 5.386–34(110); 4.312–46(002); 4.240–33(120); 4.085–100(012, 10–2); 3.685–85(031), 3.041–45(040, 112), 2.808–31(013, 20–2, 122), 2.368–34(13–3, 21–3, 033). Nickelpicromerite (single-crystal X-ray data, R?=?0.028) is isostructural to other picromerite-group minerals and synthetic Tutton’s salts. Its crystal structure consists of [Ni(H₂O)₆]²⁺ octahedra linked to (SO₄)^2? tetrahedra via hydrogen bonds. K⁺ cations are coordinated by eight anions. Nickelpicromerite is the product of alteration of primary sulfide minerals and the reaction of the acid Ni-sulfate solutions with biotite.     

Elastic and thermoelastic properties of synthetic Ca<Subscript>2</Subscript>MgSi<Subscript>2</Subscript>O<Subscript>7</Subscript> (åkermanite) and Ca<Subscript>2</Subscript>ZnSi<Subscript>2</Subscript>O<Subscript>7</Subscript> (hardystonite)

Elastic and thermoelastic constants of large single crystals of Ca₂MgSi₂O₇ and Ca₂ZnSi₂O₇ have been derived from ultrasonic resonance frequencies of plane-parallel plates and their shift upon variation of temperature, respectively. In addition, coefficients of thermal expansion and dielectric constants were determined. Both species possess quite similar properties. As observed in other isotypic magnesium and zinc compounds, the mean elastic stiffness and the deviation from the Cauchy relations are significantly larger in the zinc compound, due to a covalent contribution of the Zn–O bond. Positive thermoelastic constants T₄₄ and T₆₆ in Ca₂MgSi₂O₇ allow temperature-independent ultrasonic generators and oscillators to be manufactured.     

Nickeltalmessite,Ca<Subscript>2</Subscript>Ni(AsO<Subscript>4</Subscript>)<Subscript>2</Subscript> · 2H<Subscript>2</Subscript>O,a new mineral species of the fairfieldite group,Bou Azzer,Morocco

Nickeltalmessite, Ca₂Ni(AsO₄)₂ · 2H₂O, a new mineral species of the fairfieldite group, has been found in association with annabergite, nickelaustinite, pecoraite, calcite, and a mineral of the chromite-manganochromite series from the dump of the Aït Ahmane Mine, Bou Azzer ore district, Morocco. The new mineral occurs as spheroidal aggregates consisting of split crystals up to 10 × 10 × 20 μm in size. Nickeltalmessite is apple green, with white streak and vitreous luster. The density measured by the volumetric method is 3.72(3) g/cm³; calculated density is 3.74 g/cm³. The new mineral is colorless under a microscope, biaxial, positive: α = 1.715(3), β = 1.720(5), γ = 1.753(3), 2V _meas = 80(10)°, 2V _calc = 60.4. Dispersion is not observed. The infrared spectrum is given. As a result of heating of the mineral in vacuum from 24° up to 500°C, weight loss was 8.03 wt %. The chemical composition (electron microprobe, wt %) is as follows: 25.92 CaO, 1.23 MgO, 1.08 CoO, 13.01 NiO, 52.09 As₂O₅; 7.8 H₂O (determined by the Penfield method); the total is 101.13. The empirical formula calculated on the basis of two AsO₄ groups is Ca_2.04(Ni_0.77Mg_0.13Co_0.06)_Σ0.96 (AsO₄)_2.00 · 1.91H₂O. The strongest reflections in the X-ray powder diffraction pattern [d, Å (I, %) (hkl)] are: 5.05 (27) (001) (100), 3.57 (43) (011), 3.358 (58) (110), 3.202 (100) (020), 3.099 (64) (0\(\bar 2\)1), 2.813 (60), (\(\bar 1\)21), 2.772 (68) (2\(\bar 1\)0), 1.714 (39) (\(\bar 3\)31). The unit-cell dimensions of the triclinic lattice (space group P1 or P) determined from the X-ray powder data are: a = 5.858(7), b = 7.082(12), c = 5.567(6) Å, α = 97.20(4), β = 109.11(5), γ = 109.78(5)°, V = 198.04 ų, Z = 1. The mineral name emphasizes its chemical composition as a Ni-dominant analogue of talmessite. The type material of nickeltalmessite is deposited at the Fersman Mineralogical Museum, Russian Academy of Sciences, Moscow, Russia, registration number 3750/1.     

Kamarizaite,Fe<Stack><Subscript>3</Subscript><Superscript>3+</Superscript></Stack>(AsO<Subscript>4</Subscript>)<Subscript>2</Subscript>(OH)<Subscript>3</Subscript> · 3H<Subscript>2</Subscript>O,a new mineral species,arsenate analogue of tinticite

Kamarizaite, a new mineral species, has been identified in the dump of the Kamariza Mine, Lavrion mining district, Attica Region, Greece, in association with goethite, scorodite, and jarosite. It was named after type locality. Kamarizaite occurs as fine-grained monomineralic aggregates (up to 3 cm across) composed of platy crystals up to 1 μm in size and submicron kidney-shaped segregations. The new mineral is yellow to beige, with light yellow streak. The Mohs hardness is about 3. No cleavage is observed. The density measured by hydrostatic weighing is 3.16(1) g/cm³, and the calculated density is 3.12 g/cm³. The wavenumbers of absorption bands in the IR spectrum of kamarizaite are (cm^?1; s is strong band, w is weak band): 3552, 3315s, 3115, 1650w, 1620w, 1089, 911s, 888s, 870, 835s, 808s, 614w, 540, 500, 478, 429. According to TG and IR data, complete dehydration and dehydroxylation in vacuum (with a weight loss of 15.3(1)%) occurs in the temperature range 110–420°C. Mössbauer data indicate that all iron in kamarizaite is octahedrally coordinated Fe³⁺. Kamarizaite is optically biaxial, positive: n _min = 1.825, n _max = 1.835, n _mean = 1.83(1) (for a fine-grained aggregate). The chemical composition of kamarizaite (electron microprobe, average of four point analyses) is as follows, wt %: 0.35 CaO, 41.78 Fe₂O₃, 39.89 As₂O₅, 1.49 SO₃, 15.3 H₂O (from TG data); the total is 98.81. The empirical formula calculated on the basis of (AsO₄,SO₄)₂ is Ca_0.03Fe _2.86 ³⁺ (AsO₄)_1.90(SO₄)_0.10(OH)_2.74 · 3.27H₂O. The idealized formula is Fe ₃ ³⁺ (AsO₄)₂(OH)₃ · 3H₂O. Kamarizaite is an arsenate analogue of orthorhombic tinticite, space group Pccm, Pcc2, Pcmm, Pcm2₁, or Pc2m; a = 21.32(1), b = 13.666(6), c =15.80(1) Å, V= 4603.29(5) ų, Z= 16. The strongest reflections of the X-ray powder diffraction pattern [\(\bar d\), Å (I, %) (hkl)] are: 6.61 (37) (112, 120), 5.85 (52) (311), 3.947 (100) (004, 032, 511), 3.396 (37) (133, 431), 3.332 (60) (314), 3.085 (58) (621, 414, 324). The type material of kamarizaite is deposited in the Mineralogical Collection of Technische Universität Bergakademie Freiberg, Germany, inventory number 82199.     

Dachiardite-K, (K<Subscript>2</Subscript>Ca)(Al<Subscript>4</Subscript>Si<Subscript>20</Subscript>O<Subscript>48</Subscript>) · 13H<Subscript>2</Subscript>O,a new zeolite from Eastern Rhodopes,Bulgaria

Dachiardite-K (IMA No. 2015-041), a new zeolite, is a K-dominant member of the dachiardite series with the idealized formula (К₂Са)(Al₄Si₂₀O₄₈) · 13H₂О. It occurs in the walls of opal–chalcedony veinlets cutting hydrothermally altered effusive rocks of the Zvezdel paleovolcanic complex near the village of Austa, Momchilgrad Municipality, Eastern Rhodopes, Bulgaria. Chalcedony, opal, dachiardite-Ca, dachiardite-Na, ferrierite-Mg, ferrierite-K, clinoptilolite-Ca, clinoptilolite-K, mordenite, smectite, celadonite, calcite, and barite are associated minerals. The mineral forms radiated aggregates up to 8 mm in diameter consisting of split acicular individuals. Dachiardite-K is white to colorless. Perfect cleavage is observed on (100). D _meas = 2.18(2), D _calc = 2.169 g/cm³. The IR spectrum is given. Dachiardite-K is biaxial (+), α = 1.477 (calc), β = 1.478(2), γ = 1.481(2), 2V _meas = 65(10)°. The chemical composition (electron microprobe, mean of six point analyses, H₂O determined by gravimetric method) is as follows, wt %: 4.51 K₂O, 3.27 CaO, 0.41 BaO, 10.36 A1₂O₃, 67.90 SiO₂, 13.2 H₂O, total is 99.65. The empirical formula is H_26.23K_1.71Ca_1.04Ba_0.05Al_3.64Si_20.24O₆₁. The strongest reflections in the powder X-ray diffraction pattern [d, Å (I, %) (hkl)] are: 9.76 (24) (001), 8.85 (58) (200), 4.870 (59) (002), 3.807 (16) (202), 3.768 (20) (112, 020), 3.457 (100) (220), 2.966 (17) (602). Dachiardite-K is monoclinic, space gr. C2/m, Cm or C2; the unit cell parameters refined from the powder X-ray diffraction data are: a = 18.670(8), b = 7.511(3), c = 10.231(4) Å, β = 107.79(3)°, V= 1366(1) ų, Z = 1. The type specimen has been deposited in the Earth and Man National Museum, Sofia, Bulgaria, with the registration number 23927.     

Avdoninite: New data,crystal structure and refined formula K<Subscript>2</Subscript>Cu<Subscript>5</Subscript>Cl<Subscript>8</Subscript>(OH)<Subscript>4</Subscript> · 2H<Subscript>2</Subscript>O

The paper reports new findings of avdoninite from deposits of active fumaroles in the Second Scoria Cone at the Northern Breach of the Great Fissure Tolbachik Eruption, Tolbachik Volcano, Kamchatka Peninsula, Russia. The crystal structure of the mineral has been determined for the first time, which has allowed reliable determination of its space group and unit cell dimensions, refinement of its formula K₂Cu₅-Cl₈(OH)₄ · 2H₂O, and correct indexing of its X-ray powder diffraction pattern. Avdoninite is monoclinic, space group P2₁/c, a = 11.592(2), b = 6.5509(11), c = 11.745(2) Å, β = 91.104(6)°, V = 891.8(3) ų, Z = 2. The crystal structure of this mineral has been determined on a single crystal R ₁ [F > 4σ (F)] = 0.063. It is based on sheets of copper–oxo-chloride complexes [Cu₅Cl₈(OH)₄]^2– parallel to (100). The K⁺ cation and H₂O molecules are interlayers.     

Crystal structure and refined formula of garyansellite Mg<Subscript>2</Subscript>Fe<Superscript>3+</Superscript>(PO<Subscript>4</Subscript>)<Subscript>2</Subscript>(OH) · 2H<Subscript>2</Subscript>O

Single-crystal study of the structure (R = 0.0268) was performed for garyansellite from Rapid Creek, Yukon, Canada. The mineral is orthorhombic, Pbna, a = 9.44738(18), b = 9.85976(19), c = 8.14154(18) Å, V = 758.38(3) ų, Z = 4. An idealized formula of garyansellite is Mg₂Fe³⁺(PO₄)₂(OH) · 2H₂O. Structurally the mineral is close to other members of the phosphoferrite–reddingite group. The structure contains layers of chains of M(2)O₄(OH)(H₂O) octahedra which share edges to form dimers and connected by common edges with isolated from each other M(1)O₄(H₂O)₂ octahedra. The neighboring chains are connected to the layer through the common vertices of M(2) octahedra and octaahedral layers are linked through PO₄ tetrahedra.     

High-pressure X-ray diffraction and Raman spectroscopy of CaFe<Subscript>2</Subscript>O<Subscript>4</Subscript>-type β-CaCr<Subscript>2</Subscript>O<Subscript>4</Subscript>

In situ high-pressure synchrotron X-ray diffraction and Raman spectroscopic studies of orthorhombic CaFe₂O₄-type β-CaCr₂O₄ chromite were carried out up to 16.2 and 32.0 GPa at room temperature using multi-anvil apparatus and diamond anvil cell, respectively. No phase transition was observed in this study. Fitting a third-order Birch–Murnaghan equation of state to the P–V data yields a zero-pressure volume of V ₀ = 286.8(1) ų, an isothermal bulk modulus of K ₀ = 183(5) GPa and the first pressure derivative of isothermal bulk modulus K ₀′ = 4.1(8). Analyses of axial compressibilities show anisotropic elasticity for β-CaCr₂O₄ since the a-axis is more compressible than the b- and c-axis. Based on the obtained and previous results, the compressibility of several CaFe₂O₄-type phases was compared. The high-pressure Raman spectra of β-CaCr₂O₄ were analyzed to determine the pressure dependences and mode Grüneisen parameters of Raman-active bands. The thermal Grüneisen parameter of β-CaCr₂O₄ is determined to be 0.93(2), which is smaller than those of CaFe₂O₄-type CaAl₂O₄ and MgAl₂O₄.     

Yegorovite,Na<Subscript>4</Subscript>[Si<Subscript>4</Subscript>O<Subscript>8</Subscript>(OH)<Subscript>4</Subscript>]·7H<Subscript>2</Subscript>O,a new mineral from the Lovozero alkaline pluton,Kola Peninsula

A new mineral, yegorovite, has been identified in the late hydrothermal, low-temperature assemblage of the Palitra hyperalkaline pegmatite at Mt. Kedykverpakhk, Lovozero alkaline pluton, Kola Peninsula, Russia. The mineral is intimately associated with revdite and megacyclite, earlier natrosilite, microcline, and villiaumite. Yegorovite occurs as coarse, usually split prismatic (up to 0.05 × 0.15 × 1 mm) or lamellar (up to 0.05 × 0.7 × 0.8 mm) crystals. Polysynthetic twins and parallel intergrowths are typical. Mineral individuals are combined in bunches or chaotic groups (up to 2 mm); radial-lamellar clusters are less frequent. Yegorovite is colorless, transparent with vitreous luster. Cleavage is perfect parallel to (010) and (001). Fracture is splintery; crystals are readily split into acicular fragments. The Mohs hardness is ～2. Density is 1.90(2) g/cm³ (meas) and 1.92 g/cm³ (calc). Yegorovite is biaxial (?), with α = 1.474(2), β = 1.479(2), and γ = 1.482(2), 2V _meas > 70°, 2V _calc = 75°. The optical orientation is X ∧ a ～ 15°, Y = c, Z = b. The IR spectrum is given. The chemical composition determined using an electron microprobe (H₂O determined from total deficiency) is (wt %): 23.28 Na₂O, 45.45 SiO₂, 31.27 H₂O_calc; the total is 100.00. The empirical formula is Na_3.98Si_4.01O_8.02(OH)_3.98 · 7.205H₂O. The idealized formula is Na₄[Si₄O₈(OH)₄] · 7H₂O. Yegorovite is monoclinic, space group P2₁/c. The unit-cell dimensions are a = 9.874, b= 12.398, c = 14.897 Å, β = 104.68°, V = 1764.3 ų, Z = 4. The strongest reflections in the X-ray powder pattern (d, Å (I, %)([hkl]) are 7.21(70)[002], 6.21(72)[012, 020], 4.696(44)[022], 4.003(49)[211], 3.734(46)[\(\bar 2\) 13], 3.116(100)[024, 040], 2.463(38)[\(\bar 4\)02, \(\bar 2\)43]. The crystal structure was studied by single-crystal method, R _hkl = 0.0745. Yegorovite is a representative of a new structural type. Its structure consists of single chains of Si tetrahedrons [Si₄O₈(OH)₄]∞ and sixfold polyhedrons of two types: [NaO(OH)₂(H₂O)₃] and [NaO(OH)(H₂O)₄] centered by Na. The mineral was named in memory of Yu. K. Yegorov-Tismenko (1938–2007), outstanding Russian crystallographer and crystallochemist. The type material of yegorovite has been deposited at the Fersman Mineralogical Museum of Russian Academy of Sciences, Moscow.     

Structural changes and valence states in the MgCr<Subscript>2</Subscript>O<Subscript>4</Subscript>–FeCr<Subscript>2</Subscript>O<Subscript>4</Subscript> solid solution series

The influence on the structure of Fe²⁺ Mg substitution was studied in synthetic single crystals belonging to the MgCr₂O₄–FeCr₂O₄ series produced by flux growth at 900–1200 °C in controlled atmosphere. Samples were analyzed by single-crystal X-ray diffraction, electron microprobe analyses, optical absorption-, infrared- and Mössbauer spectroscopy. The Mössbauer data show that iron occurs almost exclusively as ^IVFe²⁺. Only minor Fe³⁺ (<0.005 apfu) was observed in samples with very low total Fe. Optical absorption spectra show that chromium with few exceptions is present as a trivalent cation at the octahedral site. Additional absorption bands attributable to Cr²⁺ and Cr³⁺ at the tetrahedral site are evident in spectra of end-member magnesiochromite and solid-solution crystals with low ferrous contents. Structural parameters a₀, u and T–O increase with chromite content, while the M–O bond distance remains nearly constant, with an average value equal to 1.995(1) Å corresponding to the Cr³⁺ octahedral bond distance. The ideal trend between cell parameter, T–O bond length and Fe²⁺ content (apfu) is described by the following linear relations: a₀=8.3325(5) + 0.0443(8)Fe²⁺ (Å) and T–O=1.9645(6) + 0.033(1)Fe²⁺ (Å) Consequently, Fe²⁺ and Mg tetrahedral bond lengths are equal to 1.998(1) Å and 1.965(1) Å, respectively.     

Thermal expansion of hydrated six-coordinate silicon in thaumasite,Ca<Subscript>3</Subscript>Si(OH)<Subscript>6</Subscript>(CO<Subscript>3</Subscript>)(SO<Subscript>4</Subscript>)·12H<Subscript>2</Subscript>O

Thaumasite, Ca₃Si(OH)₆(CO₃)(SO₄)12H₂O, occurs as a low-temperature secondary alteration phase in mafic igneous and metamorphic rocks, and is recognized as a product and indicator of sulfate attack in Portland cement. It is also the only mineral known to contain silicon in six-coordination with hydroxyl (OH)^? that is stable at ambient P–T conditions. Thermal expansion of the various components of this unusual structure has been determined from single-crystal X-ray structure refinements of natural thaumasite at 130 and 298 K. No phase transitions were observed over this temperature range. Cell parameters at room temperature are: a= 11.0538(6) Å, c=10.4111(8) Å and V=1101.67(10) ų, and were measured at intervals of about 50 K between 130 and 298 K, resulting in mean axial and volumetric coefficients of thermal expansion (×10^?5K^?1); α _a =1.7(1), α _c =2.1(2), and α _V =5.6(2). Although the unit cell and ^VIIICaO₈ polyhedra show significant positive thermal expansion over this temperature range, the silicate octahedron, sulfate tetrahedron, and carbonate group show zero or negative thermal expansion, with α _V (^VISiO₆) = ?0.6 ± 1.1, α _V (^IVSO₄)=?5.8 ± 1.4, and α _R (C–O)= 0.0 ± 1.8 (×10^?5 K^?1). Most of the thermal expansion is accommodated by lengthening of the R(O...O) hydrogen bond distances by on average 5σ, although the hydrogen bonds involving hydroxyl sites on ^VISi expand twice as much as those on molecular water, causing the [Ca₃Si(OH)₆(H₂O)₁₂]⁴⁺ columns to expand in diameter more than they move apart over this temperature range. The average Si–OH bond length of the six-coordinated Si atom 〈R(^VISi–OH)〉 in thaumasite is 1.783(1) Å, being about 0.02 Å (?20σ) shorter than ^VISi–OH in the dense hydrous magnesium silicate, phase D, MgSi₂H₂O₆.     

Tinnunculite,C<Subscript>5</Subscript>H<Subscript>4</Subscript>N<Subscript>4</Subscript>O<Subscript>3</Subscript> · 2H<Subscript>2</Subscript>O: Occurrences on the Kola Peninsula and Redefinition and Validation as a Mineral Species

Based on a study of samples found in the Khibiny (Mt. Rasvumchorr: the holotype) and Lovozero (Mts Alluaiv and Vavnbed) alkaline complexes on the Kola Peninsula, Russia, tinnunculite was approved by the IMA Commission on New Minerals, Nomenclature, and Classification as a valid mineral species (IMA no. 2015-02la) and, taking into account a revisory examination of the original material from burnt dumps of coal mines in the southern Urals, it was redefined as crystalline uric acid dihydrate (UAD), C₅H₄N₄O₃ · 2H₂O. Tinnunculite is poultry manure mineralized in biogeochemical systems, which could be defined as “guano microdeposits.” The mineral occurs as prismatic or tabular crystals up to 0.01 × 0.1 × 0.2 mm in size and clusters of them, as well as crystalline or microglobular crusts. Tinnunculite is transparent or translucent, colorless, white, yellowish, reddish or pale lilac. Crystals show vitreous luster. The mineral is soft and brittle, with a distinct (010) cleavage. D_calc = 1.68 g/cm³ (holotype). Tinnunculite is optically biaxial (–), α = 1.503(3), β = 1.712(3), γ = 1.74(1), 2V_obs = 40(10)°. The IR spectrum is given. The chemical composition of the holotype sample (electron microprobe data, content of H is calculated by UAD stoichiometry) is as follows, wt %: 37.5 О, 28.4 С, 27.0 N, 3.8 H_calc, total 96.7. The empirical formula calculated on the basis of (C + N+ O) = 14 apfu is: C_4.99H₈N_4.07O_4.94. Tinnunculite is monoclinic, space group (by analogy with synthetic UAD) P2₁/c. The unit cell parameters of the holotype sample (single crystal XRD data) are a = 7.37(4), b = 6.326(16), c = 17.59(4) Å, β = 90(1)°, V = 820(5) ų, Z = 4. The strongest reflections in the XRD pattern (d, Å–I[hkl]) are 8.82–84[002], 5.97–15[011], 5.63–24[102?, 102], 4.22–22[112], 3.24–27[114?,114], 3.18–100[210], 3.12–44[211?, 211], 2.576–14[024].     

Phase relations of potassium-bearing clinopyroxene in the system CaMgSi<Subscript>2</Subscript>O<Subscript>6</Subscript>-KAlSi<Subscript>2</Subscript>O<Subscript>6</Subscript> at 7 GPa

The pseudo-binary system CaMgSi₂O₆-KAlSi₂O₆, modeling the potassium-bearing clinopyroxene (KCpx) solid solution, has been studied at 7 GPa and 1,100–1,650 °C. The KCpx is a liquidus phase of the system up to 60 mol% of KAlSi₂O₆. At higher content of KAlSi₂O₆ in the system, grossular-rich garnet becomes a liquidus phase. Above 75 mol% of KAlSi₂O₆ in the system, KCpx is unstable at the solidus as well, and garnet coexists with kalsilite, Si-wadeite and kyanite. No coexistence of KCpx with kyanite was observed. Above the solidus, KAlSi₂O₆ content of the KCpx coexisting with melt increases with decreasing temperature. Near the solidus of the system (about 1,250 °C) KCpx contains up to 5.6 wt% of K₂O, i.e. about 22–26 mol% of KAlSi₂O₆. Such high concentration of potassium in KCpx is presumably the maximal content of KAlSi₂O₆ in the Fe-free clinopyroxene at 7 GPa. In addition to the major substitution Mg^M1C²Al¹K², the KCpx solid solution contains Ca-Eskola and only minor Ca-Tschermack components. Our experimental results indicate that the natural assemblage KCpx+grossular-rich garnet might be a product of crystallization of the ultra-potassic SiO₂-rich alumino-silicate mantle melts (>200 km).Editorial responsibility: J. Hoefs     

The high-pressure stability of chlorite and other hydrates in subduction mélanges: experiments in the system Cr<Subscript>2</Subscript>O<Subscript>3</Subscript>–MgO–Al<Subscript>2</Subscript>O<Subscript>3</Subscript>–SiO<Subscript>2</Subscript>–H<Subscript>2</Subscript>O

The solubility of chromium in chlorite as a function of pressure, temperature, and bulk composition was investigated in the system Cr₂O₃–MgO–Al₂O₃–SiO₂–H₂O, and its effect on phase relations evaluated. Three different compositions with X _Cr = Cr/(Cr + Al) = 0.075, 0.25, and 0.5 respectively, were investigated at 1.5–6.5 GPa, 650–900 °C. Cr-chlorite only occurs in the bulk composition with X _Cr = 0.075; otherwise, spinel and garnet are the major aluminous phases. In the experiments, Cr-chlorite coexists with enstatite up to 3.5 GPa, 800–850 °C, and with forsterite, pyrope, and spinel at higher pressure. At P > 5 GPa other hydrates occur: a Cr-bearing phase-HAPY (Mg_2.2Al_1.5Cr_0.1Si_1.1O₆(OH)₂) is stable in assemblage with pyrope, forsterite, and spinel; Mg-sursassite coexists at 6.0 GPa, 650 °C with forsterite and spinel and a new Cr-bearing phase, named 11.5 Å phase (Mg:Al:Si = 6.3:1.2:2.4) after the first diffraction peak observed in high-resolution X-ray diffraction pattern. Cr affects the stability of chlorite by shifting its breakdown reactions toward higher temperature, but Cr solubility at high pressure is reduced compared with the solubility observed in low-pressure occurrences in hydrothermal environments. Chromium partitions generally according to \(X_{\text{Cr}}^{\text{spinel}}\) ? \(X_{\text{Cr}}^{\text{opx}}\) > \(X_{\text{Cr}}^{\text{chlorite}}\) ≥ \(X_{\text{Cr}}^{\text{HAPY}}\) > \(X_{\text{Cr}}^{\text{garnet}}\). At 5 GPa, 750 °C (bulk with X _Cr = 0.075) equilibrium values are \(X_{\text{Cr}}^{\text{spinel}}\) = 0.27, \(X_{\text{Cr}}^{\text{chlorite}}\) = 0.08, \(X_{\text{Cr}}^{\text{garnet}}\) = 0.05; at 5.4 GPa, 720 °C \(X_{\text{Cr}}^{\text{spinel}}\) = 0.33, \(X_{\text{Cr}}^{\text{HAPY}}\) = 0.06, and \(X_{\text{Cr}}^{\text{garnet}}\) = 0.04; and at 3.5 GPa, 850 °C \(X_{\text{Cr}}^{\text{opx}}\) = 0.12 and \(X_{\text{Cr}}^{\text{chlorite}}\) = 0.07. Results on Cr–Al partitioning between spinel and garnet suggest that at low temperature the spinel- to garnet-peridotite transition has a negative slope of 0.5 GPa/100 °C. The formation of phase-HAPY, in assemblage with garnet and spinel, at pressures above chlorite breakdown, provides a viable mechanism to promote H₂O transport in metasomatized ultramafic mélanges of subduction channels.     

Optical spectroscopic study of synthetic NaScSi<Subscript>2</Subscript>O<Subscript>6</Subscript>–CaNiSi<Subscript>2</Subscript>O<Subscript>6</Subscript> pyroxenes at normal and high pressures

Six synthetic NaScSi₂O₆–CaNiSi₂O₆ pyroxenes were studied by optical absorption spectroscopy. Five of them of intermediate (Na_1−x , Ca _x )(Sc_1−x , Ni _x )Si₂O₆ compositions show spectra typical of Ni²⁺ in octahedral coordination, more precise Ni²⁺ at the M1 site of the pyroxene structure. The common feature of all spectra is three broad absorption bands with maxima around 8,000, 13,000 and 24,000 cm⁻¹ assigned to ³ A _2g → ³ T _2g, ³ A _2g → ³ T _1g and →³ T _1g (³ P) electronic spin-allowed transitions of ^VINi²⁺. A weak narrow peak at ∼14,400 cm⁻¹ is assigned to the spin-forbidden ³ A _2g → ¹ T _2g (¹ D) transition of Ni²⁺. Under pressure the spin-allowed bands shift to higher energies and change in intensity. The octahedral compression modulus, calculated from the shift of the ³ A _2g → ³ T _2g band in the (Na_0.7Ca_0.3)(Sc_0.7Ni_0.3)Si₂O₆ pyroxene is evaluated as 85±20 GPa. The Racah parameter B of Ni²⁺(M1) is found gradually changing from ∼919 cm⁻¹ at ambient pressure to ∼890 cm⁻¹ at 6.18 GPa. The Ni end-member pyroxene [(Ca_0.93 Ni_0.07)NiSi₂O₆] has a spectrum different from all others. In addition to the above mentioned bands of Ni²⁺(M1) it displays several new relatively intense and broad extra bands, which were attributed to electronic transitions of Ni²⁺ at the M2 site. In difference to CaO₈ polyhedron geometry of an eightfold coordination, Ni²⁺(M2)O₈ polyhedra are assumed to be relatively large distorted octahedra. Due to different distortions and different compressibilities of the M1 and M2 sites the Ni²⁺(M1)- and Ni²⁺(M2)-bands display rather different pressure-induced behaviors, becoming more resolved in the high-pressure spectra than in that measured at atmospheric pressure. The octahedral compression modulus of Ni²⁺(M1) in this end-member pyroxene is evaluated as 150 ± 25 GPa, which is noticeably larger than in Ni_0.3 pyroxene. This is due to a smaller size and, thus, a stiffer character of Ni²⁺(M1)O₆ octahedron in the (Ca_0.93Ni_0.07)NiSi₂O₆ pyroxene compared to (Na_0.7Ca_0.3)(Sc_0.7Ni_0.3)Si₂O₆.

Measurements and calculations of solid-liquid equilibria in the ternary systems NaBr–Na<Subscript>2</Subscript>SO<Subscript>4</Subscript>–H<Subscript>2</Subscript>O and KBr–K<Subscript>2</Subscript>SO<Subscript>4</Subscript>–H<Subscript>2</Subscript>O at 348 K

According to the compositions of the underground brine resources in the west of Sichuan Basin, solubilities of the ternary systems NaBr–Na₂SO₄–H₂O and KBr–K₂SO₄–H₂O were investigated by isothermal method at 348 K. The equilibrium solid phases, solubilities of salts, and densities of the solutions were determined. On the basis of the experimental data, the phase diagrams and the density-composition diagrams were plotted. In the two ternary systems, the phase diagrams consist of two univariant curves, one invariant point and two crystallization fields. Neither solid solution nor double salts were found. The equilibrium solid phases in the ternary system NaBr–Na₂SO₄–H₂O are NaBr and Na₂SO₄, and those in the ternary system KBr–K₂SO₄–H₂O are KBr and K₂SO₄. Using the solubilities data of the two ternary subsystems at 348 K, mixing ion-interaction parameters of Pitzer’s equation θxxx, Ψxxx and Ψxxx were fitted by multiple linear regression method. Based on the chemical model of Pitzer’s electrolyte solution theory, the solubilities of phase equilibria in the two ternary systems NaBr–Na₂SO₄–H₂O and KBr–K₂SO₄–H₂O were calculated with corresponding parameters. The calculation diagrams were plotted. The results showed that the calculated values have a good agreement with experimental data.