An experimental study of magnesite dissolution rates at neutral to alkaline conditions and 150 and 200 °C as a function of pH, total dissolved carbonate concentration, and chemical affinity

Steady-state magnesite dissolution rates were measured in mixed-flow reactors at 150 and 200 °C and 4.6 < pH < 8.4, as a function of ionic strength (0.001 M ? I ? 1 M), total dissolved carbonate concentration (10⁻⁴ M < ΣCO₂ < 0.1 M), and distance from equilibrium. Rates were found to increase with increasing ionic strength, but decrease with increasing temperature from 150 to 200 °C, pH, and aqueous CO₃²⁻ activity. Measured rates were interpreted using the surface complexation model developed by Pokrovsky et al. (1999a) in conjunction with transition state theory (Eyring, 1935). Within this formalism, magnesite dissolution rates are found to be consistent with

     

Kinetics and mechanism of natural fluorapatite dissolution at 25 °C and pH from 3 to 12

The dissolution rates of natural fluorapatite (FAP), Ca₁₀(PO₄)₆F₂, were measured at 25 °C in mixed-flow reactors as a function of pH from 3.0 to 11.7, and aqueous calcium, phosphorus, and fluoride concentration. After an initial preferential Ca and/or F release, stoichiometric Ca, P, and F release was observed. Measured FAP dissolution rates decrease with increasing pH at 3 ? pH ? 7, FAP dissolution rates are pH independent at 7 ? pH ? 10, and FAP dissolution rates again decrease with increasing pH at pH ? 10. Measured FAP dissolution rates are independent of aqueous Ca, P, and F concentration at pH ≈ 3 and pH ≈ 10.Apatite dissolution appears to be initiated by the relatively rapid removal from the near surface of F and the Ca located in the M1 sites, via proton for Ca exchange reactions. Dissolution rates are controlled by the destruction of this F and Ca depleted surface layer. The destruction of this layer is facilitated by the adsorption/penetration of protons into the surface at acidic conditions, and by surface hydration at neutral and basic conditions. Taking into account these two parallel mechanisms, measured fluorapatite forward dissolution rates can be accurately described using

     

A potentiometric study of the stability of aqueous yttrium-acetate complexes from 25 to 175 °C and 1-1000 bar

The stability of yttrium-acetate (Y-Ac) complexes in aqueous solution was determined potentiometrically at temperatures 25-175 °C (at P_s) and pressures 1-1000 bar (at 25 and 75 °C). Measurements were performed using glass H⁺-selective electrodes in potentiometric cells with a liquid junction. The species YAc²⁺ and were found to dominate yttrium aqueous speciation in experimental solutions at 25-100 °C (log [Ac⁻] < −1.5, pH < 5.2), whereas at 125, 150 and 175 °C introduction of into the Y-Ac speciation model was necessary. The overall stability constants β_n were determined for the reaction

     

Dissolution kinetics of fosteritic olivine at 90-150 °C including effects of the presence of CO2

The steady state dissolution rate of San Carlos olivine [Mg_1.82Fe_0.18 SiO₄] in dilute aqueous solutions was measured at 90, 120, and 150 °C and pH ranging from 2 to 12.5. Dissolution experiments were performed in a stirred flow-through reactor, under either a nitrogen or carbon dioxide atmosphere at pressures between 15 and 180 bar. Low pH values were achieved either by adding HCl to the solution or by pressurising the reactor with CO₂, whereas high pH values were achieved by adding LiOH. Dissolution was stoichiometric for almost all experiments except for a brief start-up period. At all three temperatures, the dissolution rate decreases with increasing pH at acidic to neutral conditions with a slope of close to 0.5; by regressing all data for 2 ? pH ? 8.5 and 90 °C ? T ? 150 °C together, the following correlation for the dissolution rate in CO₂-free solutions is obtained:

     

An experimental study of the dissolution mechanism and rates of muscovite

Steady-state muscovite dissolution rates have been measured at temperatures from 60 to 201 °C and 1 ? pH ? 10.3 as a function of reactive solution K, Si, and Al concentration. The pegmatitic muscovite used in these experiments has a composition consistent with (Na_0.09, K_0.86)Fe_0.05Al_2.92Si_3.05O₁₀(OH_1.95, F_0.06). All experiments were performed in titanium mixed-flow reactors. All experiments were performed at far-from-equilibrium conditions with respect to muscovite. All reactive solutions were undersaturated with respect to secondary product phases other than for some experiments which were supersaturated with respect to bohemite and diaspore; steady-state dissolution was stoichiometric for all experiments that were undersaturated with respect to these phases.The variation of rates with reactive solution composition depends on the solution pH. At pH ? 7 rates were found to decrease significantly with increasing reactive fluid Al activity but be independent of aqueous SiO₂ activity. pH < 7 rates measured in the present study from 60 to 175 °C are consistent with

     

The origin of Zn isotope fractionation in sulfides

Isotope fractionation of Zn between aqueous sulfide, chloride, and carbonate species (Zn²⁺, Zn(HS)₂, , , ZnS(HS)⁻, ZnCl⁺, ZnCl₂, , and ZnCO₃) was investigated using ab initio methods. Only little fractionation is found between the sulfide species, whereas carbonates are up to 1‰ heavier than the parent solution. At pH > 3 and under atmospheric-like CO₂ pressures, isotope fractionation of Zn sulfides precipitated from sulfidic solutions is affected by aqueous sulfide species and the δ⁶⁶Zn of sulfides reflect these in the parent solutions. Under high P_CO2 conditions, carbonate species become abundant. In high P_CO2 conditions of hydrothermal solutions, Zn precipitated as sulfides is isotopically nearly unfractionated with respect to a low-pH parent fluid. In contrast, negative δ⁶⁶Zn down to at least −0.6‰ can be expected in sulfides precipitated from solutions with pH > 9. Zinc isotopes in sulfides and rocks therefore represent a potential indicator of mid to high pH in ancient hydrothermal fluids.     

Dissolution kinetics of synthetic Na-smectite. An integrated experimental approach

The effect of pH and Gibbs energy on the dissolution rate of a synthetic Na-montmorillonite was investigated by means of flow-through experiments at 25 and 80 °C at pH of 7 and 9. The dissolution reaction took place stoichiometrically at 80 °C, whereas at 25 °C preferential release of Mg over Si and Al was observed. The TEM-EDX analyses (transmission electronic microscopy with quantitative chemical analysis) of the dissolved synthetic phase at 25 °C showed the presence of newly formed Si-rich phases, which accounts for the Si deficit. At low temperature, depletion of Si concentration was attributed to incongruent clay dissolution with the formation of detached Si tetrahedral sheets (i.e., alteration product) whereas the Al behaviour remains uncertain (e.g., possible incorporation into Al-rich phases). Hence, steady-state rates were based on the release of Mg. Ex situ AFM measurements were used to investigate the variations in reactive surface area. Accordingly, steady-state rates were normalized to the initial edge surface area (11.2 m² g⁻¹) and used to propose the dissolution rate law for the dissolution reactions as a function of ΔG_r at 25 °C and pH∼9:

     

Reaction pathways for quartz dissolution determined by statistical and graphical analysis of macroscopic experimental data

In light of recent work on the reactivity of specific sites on large (hydr)oxo-molecules and the evolution of surface topography during dissolution, we examined the ability to extract molecular-scale reaction pathways from macroscopic dissolution and surface charge measurements of powdered minerals using an approach that involved regression of multiple datasets and statistical graphical analysis of model fits. The test case (far-from-equilibrium quartz dissolution from 25 to 300 °C, pH 1-12, in solutions with [Na⁺] ? 0.5 M) avoids the objections to this goal raised in these recent studies. The strategy was used to assess several mechanistic rate laws, and was more powerful in distinguishing between models than the statistical approaches employed previously. The best-fit model included three mechanisms—two involving hydrolysis of Si centers by H₂O next to neutral (>Si-OH⁰) and deprotonated (>Si-O⁻) silanol groups, and one involving hydrolysis of Si centers by OH⁻. The model rate law is

     

The kinetics of iodide oxidation by the manganese oxide mineral birnessite

The kinetics of iodide (I⁻) and molecular iodine (I₂) oxidation by the manganese oxide mineral birnessite (δ-MnO₂) was investigated over the pH range 4.5-6.25. I⁻ oxidation to iodate proceeded as a two-step reaction through an I₂ intermediate. The rate of the reaction varied with both pH and birnessite concentration, with faster oxidation occurring at lower pH and higher birnessite concentration. The disappearance of I⁻ from solution was first order with respect to I⁻ concentration, pH, and birnessite concentration, such that −d[I⁻]/dt = k[I⁻][H⁺][MnO₂], where k, the third order rate constant, is equal to 1.08 ± 0.06 × 10⁷ M⁻² h⁻¹. The data are consistent with the formation of an inner sphere I⁻ surface complex as the first step of the reaction, and the adsorption of I⁻ exhibited significant pH dependence. Both I₂, and to a lesser extent, sorbed to birnessite. The results indicate that iodine transport in mildly acidic groundwater systems may not be conservative. Because of the higher adsorption of the oxidized I species I₂ and , as well as the biophilic nature of I₂, redox transformations of iodine must be taken into account when predicting I transport in aquifers and watersheds.     

Kinetic analysis of cation exchange in birnessite using time-resolved synchrotron X-ray diffraction

In this study, we applied time-resolved synchrotron X-ray diffraction (TRXRD) to develop kinetic models that test a proposed two-stage reaction pathway for cation exchange in birnessite. These represent the first rate equations calculated for cation exchange in layered manganates. Our previous work has shown that the substitution of K, Cs, and Ba for interlayer Na in synthetic triclinic birnessite induces measurable changes in unit-cell parameters. New kinetic modeling of this crystallographic data supports our previously postulated two-stage reaction pathway for cation exchange, and we can correlate the kinetic steps with changes in crystal structure. In addition, the initial rates of cation exchange, R (ų min⁻¹), were determined from changes in unit-cell volume to follow these rate laws: R = 1.75[]^0.56, R = 41.1[]^1.10, R = 1.15[]^0.50. Thus, the exchange rates for Na in triclinic birnessite decreased in the order: Cs ? K > Ba. These results are likely a function of hydration energy differences of the cations and the preference of the solution phase for the more readily hydrated cation.     

Dissolution rates of talc as a function of solution composition, pH and temperature

Steady-state talc dissolution rates, at far-from-equilibrium conditions, were measured as a function of aqueous silica and magnesium activity, pH from 1 to 10.6, and temperature from 25 to 150 °C. All rates were measured in mixed flow reactors and exhibited stoichiometric or close to stoichiometric dissolution. All measured rates at pH > 2 obtained at a fixed ionic strength of 0.02 M can be described to within experimental uncertainty using

     

Synthesis and properties of ammoniojarosites prepared with iron-oxidizing acidophilic microorganisms at 22-65 °C

Ammoniojarosite [(NH₄,H₃O)Fe₃(OH)₆(SO₄)₂], a poorly soluble basic ferric sulfate, was produced by microbiological oxidation of ferrous sulfate at pH 2.0-3.0 over a range of concentrations (5.4-805 mM) and temperatures (22-65 °C). Ammoniojarosites were also produced by chemical (abiotic) procedures in parallel thermal (36-95 °C) experiments. At 36 °C, schwertmannite [ideally Fe₈O₈(OH)₆(SO₄)] was the only solid product formed at <10 mM concentrations. Between 11.5 and 85.4 mM , a mixed product of ammoniojarosite and schwertmannite precipitated, as identified by X-ray diffraction. In excess of 165 mM , ammoniojarosite was the only solid phase produced. An increase in the incubation temperature using thermoacidophiles at 45 and 65 °C accelerated the formation of ammoniojarosite in culture solutions containing 165 mM . Both the biogenic and chemical ammoniojarosites were yellow (2Y-4Y in Munsell hue), low surface area (<1 m²/g), well crystalline materials with average c_o and a_o unit cell parameters of 17.467 ± 0.048 Å and 7.330 ± 0.006 Å, respectively. Strong positive correlations were observed between unit cell axial ratios (c_o/a_o) and increasing synthesis temperature in both biotic and abiotic systems. All samples were N deficient compared to stoichiometric ammoniojarosite, and both chemical and X-ray data indicated partial replacement of by H₃O⁺ to form solid solutions with 0.14-0.24 mole H₃O⁺ per formula unit. The morphology of the biogenic jarosites included aggregated discs, pseudo-cubic crystals and botryoidal particles, whereas the chemical specimens prepared at 36-95 °C were composed of irregular crystals with angular edges. Morphological information may thus be useful to evaluate environmental parameters and mode of formation. The data may also have application in predicting phase boundary conditions for Fe(III) precipitation in biogeochemical processes and treatment systems involving acid sulfate waters.     

Thermodynamic properties of anhydrous smectite MX-80, illite IMt-2 and mixed-layer illite-smectite ISCz-1 as determined by calorimetric methods. Part I: Heat capacities, heat contents and entropies

The heat capacities of the anhydrous international reference clay minerals, smectite MX-80, illite IMt-2 and mixed-layer illite-smectite ISCz-1, were measured by low temperature adiabatic calorimetry and differential scanning calorimetry, from 6 to 520 K (at 1 bar). The samples were chemically purified and Na-saturated. Dehydrated clay fractions <2 μm were studied. The structural formulae of the corresponding clay minerals, obtained after subtracting the remaining impurities, are K_0.026Na_0.435Ca_0.010(Si_3.612Al_0.388) (Al_1.593Mg_0.228Ti_0.011)O₁₀(OH)₂ for smectite MX-80, K_0.762Na_0.044(Si_3.387Al_0.613) (Al_1.427Mg_0.241O₁₀(OH)₂ for illite IMt-2 and K_0.530Na_0.135(Si_3.565Al_0.435)(Al_1.709Mg_0.218Ti_0.005)O₁₀(OH)₂for mixed-layer ISCz-1. From the heat capacity values, we determined the molar entropies, standard entropies of formation and heat contents of these minerals. The following values were obtained at 298.15 K and 1 bar:

	(J mol−1 K−1)	S0 (J mol−1 K−1)
Smectite MX-80	326.13 ± 0.10	280.56 ± 0.16
Illite IMt-2	328.21 ± 0.10	295.05 ± 0.17
Mixed-layer ISCz-1	320.79 ± 0.10	281.62 ± 0.15

Full-size table

     

Dissociation constants and speciation in aqueous Li2SO4 and K2SO4 from measurements of electrical conductance to 673 K and 29 MPa

The electrical conductivities of aqueous solutions of Li₂SO₄ and K₂SO₄ have been measured at 523-673 K at 20-29 MPa in dilute solutions for molalities up to 2 × 10⁻² mol kg⁻¹. These conductivities have been fitted to the conductance equation of Turq, Blum, Bernard, and Kunz with a consensus mixing rule and mean spherical approximation activity coefficients. In the temperature interval 523-653 K, where the dielectric constant, ε, is greater than 14, the electrical conductance data can be fitted by a solution model which includes ion association to form , , and , where M is Li or K. The adjustable parameters of this model are the first and second dissociation constants of the M₂SO₄. For the 673 K and 300 kg m⁻³ state point where the Coulomb interactions are the strongest (dielectric constant, ε = 5), models with more extensive association give good fits to the data. In the case of the Li₂SO₄ model, including the multi-ion associate, , gave an extremely good fit to the conductance data.     

Oxidation of Sb(III) to Sb(V) by O2 and H2O2 in aqueous solutions

The rates of Sb(III) oxidation by O₂ and H₂O₂ were determined in homogeneous aqueous solutions. Above pH 10, the oxidation reaction of Sb(III) with O₂ was first order with respect to the Sb(III) concentration and inversely proportional to the H⁺ concentrations at a constant O₂ content of 0.22 × 10⁻³ M. Pseudo-first-order rate coefficients, k_obs, ranged from 3.5 × 10⁻⁸ s⁻¹ to 2.5 × 10⁻⁶ s⁻¹ at pH values between 10.9 and 12.9. The relationship between k_obs and pH was:

     

Experimental constraints on the mobility of Rhenium in silicate liquids

The volatization of Rhenium (Re) from melts of natural basalt, dacite and a synthetic composition in the CaO-MgO-Al₂O₃-SiO₂ system has been investigated at 0.1 MPa and 1250-1350 °C over a range of fO₂ conditions from log fO₂ = −10 to −0.68. Experiments were conducted using open top Pt crucibles doped with Re and Yb. Analysis of quenched glasses by laser ablation-inductively coupled plasma mass spectrometry (LA-ICP-MS) normal to the melt/gas interface showed concentration profiles for Re, to which a semi-infinite one-dimensional diffusion model could be applied to extract diffusion coefficients (D). The results show Re diffusivity in basalt at 1300 °C in air is log D_Re = −7.2 ± 0.3 cm²/s and increases to log D_Re = −6.6 ± 0.3 cm²/s when trace amounts of Cl were added to the starting material. At fO₂ conditions below the nickel-nickel oxide (NNO) buffer Re diffusivity decreases to and to in dacitic melt. In the CMAS composition, . The diffusivity of Re is comparable to Ar and CO₂ in basalt at 500 MPa favoring its release as a volatile. Our results support the contention that subaerial degassing is the cause of lower Re concentrations in arc-type and ocean island basalts compared to mid-ocean ridge basalts.     

Gold and copper partitioning in magmatic-hydrothermal systems at 800 °C and 100 MPa

Porphyry-type ore deposits sometimes contain fluid inclusion compositions consistent with the partitioning of copper and gold into vapor relative to coexisting brine at the depositional stage. However, this has not been reproduced experimentally at magmatic conditions. In an attempt to determine the conditions under which copper and gold may partition preferentially into vapor relative to brine at temperatures above the solidus of granitic magmas, we performed experiments at 800 °C, 100 MPa, oxygen fugacity () buffered by Ni-NiO, and fixed at either 3.5 × 10⁻² by using intermediate solid solution-pyrrhotite, or 1.2 × 10⁻⁴ by using intermediate solid solution-pyrrhotite-bornite. The coexisting vapor (∼3 wt.% NaCl eq.) and brine (∼68 wt.% NaCl eq.) were composed initially of NaCl + KCl + HCl + H₂O, with starting HCl set to <1000 μg/g in the aqueous mixture. Synthetic vapor and brine fluid inclusions were trapped at run conditions and subsequently analyzed by laser ablation inductively coupled plasma mass spectrometry (LA-ICP-MS). Our experiments demonstrate that copper and gold partitioned strongly into the magmatic volatile phase(s) (MVP) (i.e., vapor or brine) relative to a silicate melt over the entire imposed range of . Nernst style partition coefficients between coexisting brine (b) and melt (m), D^b/m (±1σ), range from 3.6(±2.2) × 10¹ to 4(±2) × 10² for copper and from 1.2(±0.6) × 10² to 2.4(±2.4) × 10³ for gold. Partition coefficients between coexisting vapor (v) and melt, D^v/m range from 2.1 ± 0.7 to 18 ± 5 and 7(±3) × 10¹ to 1.6(±1.6) × 10² for copper and gold, respectively. Partition coefficients for all experiments between coexisting brine and vapor, D^b/v (±1σ), range from 7(±2) to 1.0(±0.4) × 10² and 1.7(±0.2) to 15(±2) for copper and gold, respectively. Observed average D^b/v at an of 1.2 × 10⁻⁴ were elevated, 95(±5) and 15 ± 1 for copper and gold, respectively, relative to those at the higher of 3.5 × 10⁻² where D^b/v were 10(±5) for copper and 7(±6) for gold. Thus, there is an inverse relationship between the and the D^b/v for both copper and gold with increasing resulting in a decrease in the D^b/v signifying increased importance of the vapor phase for copper and gold transport. This suggests that copper and gold may complex with volatile S-species as well as Cl-species at magmatic conditions, however, none of the experiments of our study at 800 °C and 100 MPa had a D^b/v ? 1. We did not directly determine speciation, but infer the existence of some metal-sulfur complexes based on the reported data. We suggest that copper and gold partition preferentially into the brine in most instances at or above the wet solidus. However, in most systems, the mass of vapor is greater than the mass of brine, and vapor transport of copper and gold may become more important in the magmatic environment at higher , lower , or near the critical point in a salt-water system. A D^b/v ? 1 at subsolidus hydrothermal conditions may also occur in response to changes in temperature, , , and/or acidity.Additionally, both copper and gold were observed to partition into intermediate solid solution and bornite much more strongly than into vapor, brine or silicate melt. This suggests that, although vapor and brine are both efficient at removing copper and gold from a silicate melt, the presence of Cu-Fe sulfides can sequester a substantial portion of the copper and gold contained within a silicate melt if the Cu-Fe sulfides are abundant.     

Solubilities of corundum, wollastonite and quartz in H2O-NaCl solutions at 800 °C and 10 kbar: Interaction of simple minerals with brines at high pressure and temperature

Solubilities of corundum (Al₂O₃) and wollastonite (CaSiO₃) were measured in H₂O-NaCl solutions at 800 °C and 10 kbar and NaCl concentrations up to halite saturation by weight-loss methods. Additional data on quartz solubility at a single NaCl concentration were obtained as a supplement to previous work. Single crystals of synthetic corundum, natural wollastonite or natural quartz were equilibrated with H₂O and NaCl at pressure (P) and temperature (T) in a piston-cylinder apparatus with NaCl pressure medium and graphite heater sleeves. The three minerals show fundamentally different dissolution behavior. Corundum solubility undergoes large enhancement with NaCl concentration, rising rapidly from Al₂O₃ molality (m_Al2O3) of 0.0013(1) (1σ error) in pure H₂O and then leveling off to a maximum of ∼0.015 at halite saturation (X_NaCl ≈ 0.58, where X is mole fraction). Solubility enhancement relative to that in pure H₂O, , passes through a maximum at X_NaCl ≈ 0.15 and then declines towards halite saturation. Quenched fluids have neutral pH at 25 °C. Wollastonite has low solubility in pure H₂O at this P and T(m_CaSiO3=0.0167(6)). It undergoes great enhancement, with a maximum solubility relative to that in H₂O at X_NaCl ≈ 0.33, and solubility >0.5 molal at halite saturation. Solute silica is 2.5 times higher than at quartz saturation in the system H₂O-NaCl-SiO₂, and quenched fluids are very basic (pH 11). Quartz shows monotonically decreasing solubility from m_SiO2=1.248 in pure H₂O to 0.202 at halite saturation. Quenched fluids are pH neutral. A simple ideal-mixing model for quartz-saturated solutions that requires as input only the solubility and speciation of silica in pure H₂O reproduces the data and indicates that hydrogen bonding of molecular H₂O to dissolved silica species is thermodynamically negligible. The maxima in for corundum and wollastonite indicate that the solute products include hydrates and Na⁺ and/or Cl⁻ species produced by molar ratios of reactant H₂O to NaCl of 6:1 and 2:1, respectively. Our results imply that quite simple mechanisms may exist in the dissolution of common rock-forming minerals in saline fluids at high P and T and allow assessment of the interaction of simple, congruently soluble rock-forming minerals with brines associated with deep-crustal metamorphism.