13X沸石分子筛对水中Hg2+吸附性能的实验研究

13X沸石分子筛吸附水中Hg2+的实验研究表明,13X沸石在pH值为5~6、时间为20 min、温度为20~30 ℃条件下对Hg2+ 的吸附效果最佳。在13X沸石的用量为4 g/L的条件下对原始浓度为0.2 ~100mg/L的Hg2+进行吸附,吸附量由0.035 6 mg/g增加到21.87 mg/g。13X沸石可使原始浓度为0.01 mg/L的Hg2+降至0.002 mg/L以下。饱和NaCl溶液对吸附Hg2+后的13X沸石解吸效果良好,解吸后的13X沸石循环使用4次,对Hg2+的吸附率仍未降低,表明13X沸石的重复利用效果良好。通过在洗脱Hg2+ 的解吸液中加入Na2S·9H2O,可使Hg2+形成HgS沉淀进行回收,回收率可达90%以上。实验表明,13X沸石适用于对水中低浓度Hg2+的深度净化处理。     

13X沸石分子筛对饮用水中NH_4~+-N吸附性能的实验研究

研究了 13X沸石分子筛对饮用水中低浓度NH+4 N的吸附性能 ,包括影响吸附的主要因素、沸石对NH+4 N的吸附效果、沸石的再生效果及沸石对NH+4 N的吸附机理。实验表明用NaOH处理的沸石比未处理的沸石对NH+4 N的吸附效果要好。在 pH值为 6 5～ 7 5、吸附时间为 2 0min、吸附温度为 2 0～ 30℃的条件下 ,沸石对NH+4 N的吸附率接近 10 0 % ,沸石对NH+4 N的吸附量可达 16 32mg/g。用直接焙烧法进行再生活化处理后的沸石对NH+4 N的吸附率仍接近 10 0 % ,沸石对NH+4 N的吸附机理是以离子交换吸附作用为主。 13X沸石吸附NH+4 N的过程符合Langmuir吸附等温模式。实验证明 ,利用 13X沸石净化含低浓度NH+4 N的饮用水具有良好的工业化应用前景。     

13X沸石对Ni2+吸附性能的实验研究

在静态条件下，实验研究了13X沸石的用量、温度、时间、溶液pH值、初始Ni^2 质量浓度对Ni^2 吸附性能的。结果表明：在室温下，13X沸石对Ni^2 的吸附平衡时间为15min，对Ni^2 的最大吸附量为49.7mg/g沸石；静态等温吸附过程符合Langmiur吸附等温方程式；13X沸石对Ni^2 的吸附机理为离子交换吸附和表面络合吸附。     

13X沸石处理含赖氨酸废水的实验研究

用合成的13X沸石对废水中氨基酸(赖氨酸)进行静态吸附实验,研究了pH、温度、吸附时间、沸石用量等对吸附率的影响,结果表明,室温下沸石对赖氨酸的吸附平衡时间为30min,pH=pKa1=2.2时,赖氨酸在沸石上的吸附效果最好,吸附率大于82%,饱和吸附量达51.73mg.g-1。吸附等温线近似呈直线型,表明离子交换机制是沸石吸附氨基酸的主要方式。对已饱和吸附的沸石用饱和氯化钠溶液进行再生实验,赖氨酸的解吸率大于95%,沸石可重复使用。实验研究表明可用13X分子筛处理含氨基酸废水,为实际处理含氨基酸废水提供了可行性依据。     

大洋多金属结核浸出渣动态吸附Cu2+的实验研究

实验以大洋多金属结核浸出渣(66%,质量分数)为主要原料、高岭土(21%)为粘结剂、蛭石(13%)为膨胀剂,研制出用于动态吸附废水中重金属离子的浸出渣颗粒。以造粒后的颗粒为吸附剂动态处理含Cu2 的模拟废水,研究发现溶液浓度、流速、pH值对动态吸附效果的影响,选定浸出渣颗粒动态处理重金属废水的工艺参数:造粒后浸出渣颗粒的比表面积为18.61 m2/g,当模拟废水中Cu2 溶液的初始浓度为27 mg/L、pH=5.35、出口流速为10 ml/h时,每克浸出渣颗粒可动态处理模拟废水114.3 ml,处理后溶液中阳离子的浓度≤0.5 mg/L,实验效果明显。     

赤泥与13X沸石混合使用去除废水中砷

对福建沙县钾长石粉合成的13X沸石及其与取自山东铝业公司的赤泥混合使用时除砷的效果和适宜条件进行实验。结果表明，以单一的13X沸石为吸附剂时，改变沸石用量和溶液的酸度均不能有效去除砷；赤泥和沸石混合使用时对低浓度砷（〈5mg／L）具有良好的去除效果。适宜的吸附条件为赤泥用量2g／L，沸石用量1．5g／L，pH值约为8，平衡时间1h。实验表明，赤泥在混合吸附剂除砷过程中起着重要的作用，沸石与赤泥的合理混合使用，对于含砷重金属废水处理具有重要意义。对可能的机理进行了探讨。     

羟基磷灰石吸附水溶液中Cd^2＋的影响因素的研究

对羟基磷灰石(Hap)固定水溶性Cd2+的影响因素进行了较为系统的实验研究.实验表明去除率与Cd2+初始浓度呈负相关,在Cd2+初始浓度<10 mg/L时,与作用时间、pH值、Hap用量呈正相关,温度对去除率的影响较小.通过正交实验确定了最佳吸附条件Hap用量为5 g/L,pH值为6,作用时间5 min.     

炉渣处理含磷废水的实验研究

以炉渣作为吸附剂，用静态吸附实验方法研究了炉渣对模拟含磷废水脱磷的一般规律，结果表明，炉渣是一种有效的吸附剂，对废水中的磷有较强的吸附去除性能。影响炉渣除磷的主要因素有吸附时间、炉渣用量、pH值和原水含磷浓度。在含磷浓度2～13mg／L、炉渣用量5g／L、中性、吸附时间为2h的实验条件下，磷的去除率可高达99％以上。     

淡水中丝状绿藻对重金属Pb2+的吸附

通过淡水中绿藻门的一些丝状种类,如毛枝藻(Stigeoclonium)、刚毛藻(Cladophora)、水绵(Spirogyra)对铅的吸附实验,研究淡水藻类与铅的吸附关系及影响因素。结果表明,淡水中丝状绿藻对铅有较强的吸附能力, 当pH值和温度以及包埋藻类的量控制在一定条件下,即pH值约为4,温度为28℃左右,按照2 g藻类处理20 mL 质量浓度为100 mg/L Pb²⁺溶液原则包埋藻类,就可以使单位藻类吸附效率达到40％。     

Fe2O3对13X沸石分子筛合成条件及性能的影响研究

对江苏丰县的富钾页岩进行预处理,得到不同Fe2O3 质量分数的钾长石粉体原料FXY1、FXY2,经中温焙烧得到偏铝硅酸盐前体化合物,水热晶化合成了13X沸石分子筛。采用正交实验法,确定了水热晶化反应的优化工艺条件,原料中Fe2O3 质量分数的不同导致水热晶化反应的工艺参数有所不同。合成的两种沸石的性能与13X沸石分子筛的工业产品相似,吸附量均达到国家化学工业产品标准HG/T 2690 95的要求。对比实验表明,原料中Fe2O3 质量分数的降低可使其在更宽的碱度范围内合成性能更优的13X沸石产品。由低Fe2O3 质量分数的FXY2为原料合成的沸石,其物相纯度、热稳定性、白度、比表面积、吸附性等性质更优。合成沸石均可用于对含重金属离子废水的深度净化处理,由FXY2为原料合成的13X沸石还可用作洗涤助剂。     

混凝沉淀-改性沸石方法联合处理锡铅锌多金属矿选矿废水初步研究

锡铅锌金属选矿过程中,重金属离子的溶出,使得选矿废水中重金属含量较高,需要处理才能达标排放。取原水pH值为8,Zn~(2+)为13.8mg/L,Cd~(2+)为0.07mg/L,采用混凝沉淀-改性沸石处理工艺流程处理,可使废水达到铅锌行业排放标准。在工程应用中,可使选矿废水达标排放,效果稳定,但沸石产泥量较大。     

Removal of heavy metals from paint industry’s wastewater using Leca as an available adsorbent

The ability of light expanded clay aggregate to remove lead and cadmium from paint industry’s effluents was studied at different levels of adsorbent, contact time and pH in April 2008. For this purpose, lead and cadmium removal from paint industry effluents were studied in batch reactors. lead and cadmium measurements have been taken with non-flame atomic absorption techniques and test methods were adapted from 19^th. Ed. of standard methods for the examination of water and wastewater. In this study, different amounts of Leca (1, 2, 3, 4, 5, 6, 7, 8, 9 and 10 g/L) were investigated. The amount of adsorbed lead and cadmium exposure to Leca increased from 1.41 to 3 mg/g and 0.22 to 0.75 mg/g, respectively. The maximum removal efficiency for Pb was 93.75 % at pH = 7 and exposure to 10 g/L of Leca, while for cadmium, it was nearly 89.7 % at the same condition. In this study, adsorption process of lead and cadmium was fitted with Freundlich adsorption isotherm (R² _Pb = 0.97 and R² _Cd = 0.98). The sufficient contact time was deemed 1–2 h for lead and cadmium. According to the results, Leca is recommended as a low cost and available adsorbent to remove lead and cadmium from industrial wastewater.     

活化沸石除铵及其动力学过程研究

对新型水处理材料活化沸石去除水中氨氮的各项性能进行了研究。单因素影响试验表明,沸石用量、粒径、溶液温度、浓度、pH值及吸附时间对去除效果有重要影响。据此确定了最佳静态试验条件,在该条件下,活化沸石对水中的氨氮有较好的去除效果,可将生活污水中的120 mg/L氨氮降到40 mg/L。动态小试确定了小试设备的工艺参数,该处理设备在实际运行过程中,吸附周期为64 h,处理效果良好。动力学研究表明,活化沸石除铵是离子交换与吸附两种行为共同作用的结果,该过程符合Freundlich等温式,动力学方程可用一级反应来描述。     

Hydrothermal synthesis of hydroxy sodalite from fly ash for the removal of lead ions from water

Zeolites are known to possess valuable physiochemical properties such as adsorption, cation exchange, molecular sieving, and catalysis. In addition, zeolites are highly selective scavengers of a variety of heavy metals from liquid effluents through the process of ion exchange. The present study was performed to hydrothermally synthesize Na₈[AlSiO₄]₆(OH)₂·2H₂O (also known as hydroxy sodalite hydrate). Due to its small aperture size, this material can be an ideal candidate for the separation of small molecules and ions from aquatic and gas mixtures. Synthetic zeolites offer many advantages over natural zeolites, such as higher ion affinity and adsorption capacity. Batch adsorption isotherm studies were conducted to evaluate the obtained adsorbent for the lead ion removal from aqueous media. Modeling lead ion adsorption using Langmuir and Freundlich isotherm expressions determined the capacity of the adsorbent. A removal efficiency of 98.1 % in a 3.0 g/l adsorbent/solution mixture with a maximum adsorption capacity of 153.8 mg/g was obtained. One potential application of the synthesized zeolite is for the lead removal in point-of-use treatment devices.     

广西车田沸石及其开发利用研究进展

文章在总结车田沸石的晶形及物理性质、化学成分特征、红外光谱、差热-热重、X射线衍射等矿物学特征，以及耐热稳定性、耐酸碱稳定性、离子吸附与交换性能等资源特性研究进展的基础上，重点介绍了车田沸石的开发利用研究新进展，即利用其在低温煅烧和低浓度酸处理后可使其成为无定形非晶态物质的特性制备A型、X型、Y型和P型分子筛；利用其吸附和离子交换性能制备水处理剂、沸石型化肥、无机抗菌剂、干燥剂；利用其化学成分和晶体结构特性制备沸石砖、橡胶和塑料的增强剂等。并对今后车田沸石及其开发利用的研究方向和研究前景进行了展望。     

一种重金属废水处理剂处理工业含铅废水的研究

用滚动成型的方法将改性天然磷灰石粉末制备成颗粒状水处理剂,并对工业含铅废水进行了静态和动态处理研究.静态实验中该水处理剂去除铅离子的能力可达到661.10 mg/g;动态实验结果表明该水处理剂每1 kg可以处理Pb2 浓度为58.3 mg/L的废水3 m3,出水达到排放标准.对使用过的水处理剂进行高温固化或者添加到粘土中制砖,可避免二次污染.经济分析显示该水处理剂具有很好的应用潜力和开发价值.